Polyurethanes used in the endoprosthesis of joints

Domańska A., Boczkowska A., Izydorzak M., Jaegermann Z., Kurzydłowski K. J.

Polish Journal of Chemical Technology

2010

Vol. 12, nr 3

10-14

The aim of the studies presented in this paper was the selection of the polyurethanes synthesized from different substrates in order to obtain i) ceramic - biodegradable polymer composite and ii) polyurethane resistant to abrasive wear. The polyurethanes were obtained from the crystalline prepolymers extended by water, because it may have a beneficial effect on the toxicity of the material. The properties of PUs were investigated using infrared spectroscopy, thermogravimetry, differential scanning calorimetry and scanning electron microscopy. In all the tested polyurethanes the peak from the reactive -NCO groups was not observed, which indicates that all the substrates are fully reacted. Such polyurethanes are characterized by interesting properties with the perspective use as components of ceramic-polymer joints endoprosthesis. The designed endoprosthesis should fulfill at least three functions: load bearing function (ceramic core), fastening and stabilizing endoprosthesis to the bone (composite ceramics – biodegradable polymer) and tribologic function allowing mating with parts of the prosthesis (polyurethane layer resistant to abrasive wear).

Synthesis of magnetic nanocrystallites in carbon matrix

Szmidt E., Leonowicz M., Izydorzak M., Jezierska E.

Inżynieria Materiałowa

2010

Vol. 31, nr 3

299-302

Synthesis of a metal containing monomer, followed by its polymerization and further pyrolysis was applied for the processing of magnetic nanocrystallites in carbon beads. The magnetic ordering, size and properties of the nanocrystallites depended on the processing variables. Changing the polymeric precursor type and varying the pyrolysis temperature we obtained cobalt, iron, iron carbide and nickel nanocrystallites. The latter elementary metal crystallites were either ferromagnetic or superparamagnetic, depending on their size determined by the pyrolysis temperature.

Do otrzymywania magnetycznych nanokrystalitów w osnowie węglowej zastosowano metodę opartą na wytworzeniu monomeru zawierającego metal, z jego późniejszą polimeryzacją i pirolizą. Typ magnetycznego uporządkowania, wielkość krystalitów i ich właściwości zależały od parametrów procesu. Zmieniając prekursor polimerowy i temperaturę pirolizy, otrzymano nanokrystality kobaltu, żelaza, węglika żelaza i niklu. Nanokrystality niklu wykazywały uporządkowanie ferromagnetyczne lub superparamagnetyczne, zależnie od wielkości krystalitów, determinowanej przez temperaturę pirolizy.