Content available Research of surfaсe hardening influence on the microstructure, microhardness and wear resistence 18CrNi3MoA-Sh steel
Skakov M., Bayatanova L., Sheffler M.
Tribologia
|
2012
|
nr 5
147--153
EN
The research shows the results of electrolyte-plasma treatment influence on structure-phase state, mechanical properties and wear-resistance of drilling tool steel samples. The comparative analysis of the microstructure, microhardness, and wear-resistance of the samples in initial state and after electrolyte-plasma treatment is represented. It was found that 18CrNi3MoA-Sh steel has a fine-grained martensite-bainite microstructure after the treatment. It was determined that 18CrNi3MoA-Sh steel possesses high wear-resistance after electrolyteplasma treatment and that this technology is characterised by low power consumption and cost. The average initial state microhardness is 2800 MPa. The average microhardness on the bearing lane surface after electrolyte-plasma processing is 7500 MPa. Microhardness increases bay a factor of 2 to 2.5, indicating technology efficiency.
PL
Wyniki badań przedstawiają wpływ obróbki elektrolotyczno-plazmowej na stan strukturalno-fazowy, własności mechaniczne i odporność na zużywanie próbek stali na narzędzia wiertnicze. W pracy przedstawiono analizy porównawcze mikrostruktury, mikrotwardości i odporności na zużywanie próbek w stanie wyjściowym i po obróbce. Stwierdzono, że martenzytyczno-bajnityczna mikrostruktura stali 18CrNi3MoA-Sh po obróbce jest drobnoziarnista. Zauważono, że obróbka podwyższa odporność stali na zużywanie, co jest korzystne przy jej niskim zapotrzebowaniu na moc i niskim koszcie. Wartość średnia mikrotwardości próbek w stanie wyjściowym wynosi 2800 MPa, natomiast po obróbce wartość średnia mikrotwardości wzrasta do 7500 MPa. Mikrotwardość stali po obróbce elektolityczno-plazmowej wzrosła więc 2–2,5-krotnie w odniesieniu do stanu początkowego, co świadczy o skuteczności zastosowanej obróbki.
2
Content available Influence of regimes electrolyte-plasma processing on phase structure, mechanical properties and wear resistance of steel 30CrMnSi
Skakov M., Zhurerova L., Scheffler M.
Tribologia
|
2012
|
nr 5
175--182
EN
The present work is research on the influence of various modes of electrolytic plasma cementation on changes in structurally-phase conditions and hardening of constructional steel 30CrMnSi. This process has been chosen for investigation because of its economical use of power, the formation of stable ferrite-perlite structures, and higher mechanical properties. The cementation process was carried by selecting different modes of electrolytic-plasma processing in the electrolyte containing a water solution of 10% sodium carbonate and 10 % glycerine.
PL
Prezentowana praca poświęcona jest badaniom wpływu różnych sposobów obróbki elektrolityczno-plazmowej na zmianę właściwości strukturalno-fazowych i twardości stali 30CrMnSi. Dokonano wyboru procesów obróbki odznaczających się zapotrzebowaniem na małe moce i zasoby materiałowe, co zostało potwierdzone badaniami naukowymi. Wybrane procesy prowadzą do formowania stabilnej struktury ferrytyczno-perlitycznej oraz podwyższają własności mechaniczne stali. Procesy obróbki przeprowadzono przy wyborze różnych parametrów elektrolityczno-plazmowych w elektrolicie zawierającym wodny roztwór 10-procentowy węglanu sodu i 10% gliceryny.
3
Content available Influence of electrolytic plasma cementation on the microhardness and wear resistance of steel 12Cr18Ni10Ti
Skakov M., Kurbanbekov S., Scheffler M.
Tribologia
|
2012
|
nr 5
155--163
EN
The present work presents the results of electrolytic-plasma treatment influence on the mechanical properties and structural-phase condition of the surface layers of 12Cr18Ni10Ti steel. In the work, the mechanical characteristics of the surface layers that have been pack cemented by electrolytic plasma with the composition of 10% Nа₂CO₃ and 10% С3Н8О3 are investigated. The operational parameters for the processing are determined. The optimal content of components in saturating mixtures of plasma by cementation is defined. Structural research of the samples was carried out by x-ray diffraction analysis, and optical and electron microscopy. The comparative study of the structure, phase and chemical composition of the modified surface layers of steel 12Cr18Ni10Ti is executed after electrolytic plasma processing. According to the study, after electrolyte plasma processing, high wear resistance and hardness increased by a factor of 2 to 2.5 more than in the original condition. A hardened layer with a thickness 200–250 µm is formed. It is shown that, after the electrolyte-plasma processing of steel 12Cr18Ni10Ti, the microstructure contains particles of carbides and has a fine-grained martensitic structure.
PL
W pracy przedstawiono wyniki wpływu obróbki elektrolityczno-plazmowej na własności mechaniczne i stan strukturalno-fazowy warstwy wierzchniej stali 12Cr18Ni10Ti. W pracy badano charakterystyki mechaniczne warstwy wierzchniej stali cementowanej w elektrolitycznej plazmie o składzie 10% Nа2CO3 i 10% С3Н8О3. Określono warunki prowadzenia procesu oraz optymalny skład mieszaniny plazmy. Badania strukturalne próbek prowadzono z wykorzystaniem analizy rentgenowskiej dyfrakcyjnej, mikroskopii optycznej i elektronowej. Badania porównawcze struktury, faz i składu chemicznego modyfikowanej warstwy wierzchniej stali 12Cr18Ni10Ti wykonano po obróbce elektrolityczno-plazmowej. Na podstawie badań stwierdzono, że w wyniku obróbki wzrosła odporność na zużywanie i twardość (2–2,5-krotnie w odniesieniu do stanu przed obróbką). Utwardzona warstwa ma grubość 200–250 µm. Świadczy to o tym, że w wyniku obróbki elektrolityczno-plazmowej stali 12Cr18Ni10Ti jej mikrostruktura zawiera cząstki węglików i ma drobnoziarnistą strukturę martenzytyczną.
4
Content available Change of structure and wear resistance of P6M5 steel from processing in electrolyte plasma
Skakov M., Rakhadilov B., Sheffler M.
Tribologia
|
2012
|
nr 5
165--173
EN
Mechanical characteristics of nitrated and carbonitriding in electrolyte plasma Р6М5 steel surface layers are investigated in the research. Perspective technology of cutting tool electrolyte-plasma treatment is displayed. Comparative research of structure, phase composition of fast-cutting P6M5 steel modified surface layers after electrolyte plasma treatment was carried out by scanning-electron and light microscopy, and X-ray structure analysis methods.
PL
W przeprowadzonych badaniach określano charakterystykę mechaniczną stali P6M5 azotowanej i cyjanowanej poprzez obróbkę elektrolityczno-plazmową. Przedstawiono obróbkę elektrolityczno-plazmową, która jest przyszłościowa dla obróbki narzędzi obróbkowych. Badania porównawcze struktury, budowy fazowej stali szybkotnącej P6M5 z modyfikowaną warstwą wierzchnią w trakcie obróbki elektrolityczno-plazmowej prowadzono z wykorzystaniem mikroskopii skaningowej i optycznej oraz analizy rentgenowskiej.