Production of Shape Memory Alloy Core-Sheath Friction Yarns

Ahmad M. R., Yahya M. H. M., Hassan M. R., Salleh J., Ahmad W. Y. W., Hassim N.

Fibres & Textiles in Eastern Europe

2013

Vol. 21, no. 3 (99)

68--72

This paper describes some studies on the development of shape memory alloy (SMA) coresheath friction yarns. SMA wires for actuating purposes were utilised as a conductive element in the core-sheath friction yarn. A DREF 3000 friction spinning machine was used to produce the yarns. The conductive yarn was spun with the SMA actuator wire at the core and 100% cotton fibers in the second layer as the sheath producing a yarn called SMA core-sheath friction yarn (SMA CSFY). During spinning, the core-sheath ratio and spinning drum speeds were varied. The main purposes of the study were to evaluate the SMA CSFY single yarn tensile strength and its actuating performance against changes in the spinningprocess parameters. The results showed that SMA CSFY with the highest spinning drumspeed and 60% core gave the highest tensile strength and fastest actuation performance.

Badania dotyczyły opracowania przędz rdzeniowych z udziałem składnika posiadającego pamięć kształtu. Druty z pamięcią kształtu zostały zastosowane jako elementy elektrycznie przewodzące. Do produkcji tych przędz zastosowano przędzarkę DREF 3000. Przędze przewodzące były produkowane z rdzeniem z drutów o pamięci kształtu oraz otoczką z włókien bawełnianych (100%). Przędzenie przeprowadzano przy zmianie prędkości bębna przędącego. Głównym celem badań była ocena właściwości wytrzymałościowych otrzymanej przędzy oraz wpływ parametrów przędzenia na pamięć kształtu przędzy. Wyniki badań wskazują, że przędze otrzymane przy najwyższych prędkościach bębna przędącego i udziale rdzenia 60% posiadają najlepsze właściwości wytrzymałościowe i korzystne reakcje na zmianę kształtu.

Preliminary Investigation on the Ballistic Limit of Ultra High Molecular Weight Polyethylene Unidirectional Coated Fabric System

Ahmad M. R., Hassim N., Ahmad W. Y. W., Samsuri A., Yahya M. H. M.

Fibres & Textiles in Eastern Europe

2013

Vol. 21, no. 3 (99)

89--94

This paper reports an investigation on the ballistic impact performance of high strength unidirectional (UD) fabrics UHMWPE coated with natural rubber latex (NRL). The effects of adding calcium carbonate in the NRL on the ballistic impact were also studied. Several NRL coated UD fabrics were assembled together with neat UD fabrics in a 12-ply fabric system. The ballistic limit and energy absorption of the fabric systems were determined. Results of the ballistic limit test showed that the NRL coated UD fabrics gave some positive effects in enhancing the ballistic impact performance of the fabric systems in comparison with all-neat fabric systems. Several mechanisms of energy absorption were observed on the fabric systems which include burn marks, fibre stretching, fibre pull-out, shearing, delamination of fabric plies for completely penetrated fabric systems and a punched-out effect on the back ply of partially penetrated fabric systems.

Badania dotyczyły efektu uderzenia pocisku w balistyczny pakiet wykonany z pokrywanych naturalną gumą tkanin typu UD wykonanych z polietylenu o ultra wysokiej masie cząsteczkowej. Dodatkowo badano wpływ dodania węglanu wapnia do kauczuku naturalnego. W pakietach składano tkaniny powlekane i niepowlekane w systemy zawierające do 12 warstw. Określano limit balistyczny i energię absorpcji uzyskanych pakietów. Wyniki badań wskazują, że powlekanie warstw gumą naturalną daje pozytywne efekty poprawiając zachowanie pakietu na uderzenie pocisku. Obserwowano pojawianie się przypalenia pakietów, rozciąganie włókien, wyciąganie włókien, ścinanie, delaminację pakietów aż do całkowitej penetracji wszystkich warstw systemu.