Viscosity and creep compliance of polyoxymethylene copolymers of various average molecular weights

Gonzalez-Gutierrez J., Oblak P., Megen Z. M., Emri I.

Polimery

2015

T. 60, nr 10

620--627

The effect of average molecular weight (Mw ) of polyoxymethylene (POM) on melt viscosity and solid state creep compliance were investigated. Viscosity follows the power function of Mw. Creep compliance results indicate that time-temperature superposition applies to POM copolymers. Creep compliance in ashort time (0.25 s) is independent of Mw, but in a longer time (10 years) it follows an inverse power law relation with Mw, up to a critical value of Mw = 81 100, where creep compliance becomes independent of Mw. At intermediate time (17 min), similar to short one, no effect on susceptibility to creep compliance was observed. It was also stated that the activation energy is independent of Mw.

Zbadano wpływ średniego ciężaru cząsteczkowego (Mw) wybranych kopolimerów polioksymetylenowych (POM) na lepkość stopu i podatność na pełzanie próbki w stanie stałym. Stwierdzono, że w przypadku wszystkich badanych kopolimerów POM zależność lepkości od Mw opisuje funkcja potęgowa. Wyniki badań podatności na pełzanie wykazały zgodność z zasadą równoważności temperaturowo-czasowej. Podatność na pełzanie w krótkim czasie (0,25 s) była niezależna od Mw, natomiast w czasie dłuższym (10 lat) wielkość ta zmniejszała się ze zwiększaniem Mw, aż do wartości krytycznej Mc = 81 100, po której nie zależała już od Mw. W średnim czasie (17 min), podobnie jak w czasie krótkim, Mw nie wpływał na podatność na pełzanie. Zaobserwowano również, że energia aktywacji nie jest funkcją Mw.