Surfaces of cam shafts made of AISI 8620 steels were hardened by boriding processes in both solid and liquid mediums. Various chemical agents were used to achieve boride layers on the surfaces of the cam shafts in these processes. It was aimed to examine effects of the chemical agents on microhardness and thickness of the boride layers obtained. It was concluded that a bath composition of 5% B4C-90% SiC-5% KBF4 was appropriate for the hardest and thickest boride layer achieved in the solid medium, and a composition of 70% Na2B4O7-30% B4C in the liquid medium.
2
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Alloys of FeNiSiB soft magnetic materials containing variable Fe and Ni contents (wt.%) have been produced by melt spinning method, a kind of rapid solidification technique. The magnetic and structural properties of FeNiSiB alloys with soft magnetic properties were investigated by increasing the Fe ratio. X-ray diffraction analysis and SEM images shows that the produced alloy ribbons generally have an amorphous structure, together with also partially nanocrystalline regions. It was observed that the structure became much more amorphous together with increasing Fe content in the composition. Among the alloy ribbons, the highest saturation magnetization was obtained as 0.6 emu/g in the specimen with 50 wt.% Fe. In addition, the highest Curie temperature was observed in the sample containing 46 wt.% Fe.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.