Wetting behavior of Si-13.5B alloy on polycrystalline h-BN-based substrates

Polkowski W., Sobczak N., Nowak R., Kudyba A., Bruzda G., Polkowska A., Homa M., Turalska P., Shuleshova O., Kaban I.

Prace Instytutu Odlewnictwa

2017

Vol. 57, no. 4

321--326

In this work, for the first time the results of an experimental evaluation of the high temperature behavior of molten Si-B alloy in contact with refractory materials at temperatures up to 1750°C, under static argon atmosphere (p = 850– 900 mbar), is shown. The material investigated, having a nominal chemical composition of Si-13.5B (at. %), was fabricated by using the crucible-less electric arc-melting process assisted by the levitation drop method. The wettability of the molten alloy in contact with commercial hexagonal boron nitride (h-BN) substrates was evaluated by means of especially developed sessile drop technique combined with a contact heating procedure. It was found that both couples show a lack of wettability in the whole tested temperature range (the measured contact angle was θ > 130°). The more stable behavior in contact with molten Si-13.B alloy, evidenced by higher θ values and a lack of drop vibration during the high temperature exposition, was observed for the h-BN based composite substrate.