The Impact of Composition and the Densification Level of Furan Molding Compounds on the Strength of Large-Size Casting Molds

Petrus Ł., Bulanowski A., Kołakowski J., Urbanowicz M., Sobieraj J., Jelonek M., Brzeżański M., Zych J. S., Janerka K.

Archives of Metallurgy and Materials

2020

Vol. 65, iss. 4

1431--1436

The paper presents the test results of molding compounds, sand casting molds and their analysis. The subject of testing was compound containing furan resins prepared according to the following recipe: matrix – regenerate 90% + fresh sand – 10%, furanresin – 1.10% by weight, hardener – 0.40% by weight. The impact of adhesive type and its quantity (Quan = 0.90, 1.1 and 1.5%) on the strength indexes of molding compound subject to densification was analyzed. The publication presents the test results: tensile strength Rm, compressive strength Rc and flexural strength Rg, as well as compound permeability as function of its density. The analysis also covers the impact of density level on mold strength and the distribution of density level along the mold height. Based on the test results, it was found that the best method to obtain high strength molds made from compounds with chemical adhesives was to densify it by vibrating the system: match plate – molding flask – compound filling the mold. The effectiveness of this densification method depends on the amplitude and frequency of vibrations.

The Influence of Selected Melting Parameters on the Physical and Chemical Properties of Cast Iron

Petrus Ł., Bulanowski A., Kołakowski J., Brzeżański M., Urbanowicz M., Sobieraj J., Matuszkiewicz G., Szwalbe L., Janerka K.

Archives of Foundry Engineering

2020

Vol. 20, iss. 1

105--110

This paper presents the problems related to smelting gray and ductile cast iron. Special attention is paid to the metallurgical quality of cast iron. It depends on the type of furnace, charge materials and the special combination of charge, overheating and holding temperature, melting time, modification and spheroidization method. The evaluation of metallurgical quality has been performed by using derivative-thermal analysis (DTA). During the smelting process and secondary metallurgy, the ITACA system was used allowing to obtain information on alloy characteristic temperatures (Tliquidus, TeMin, TeMax, Tsolidus), VPS value, recalescence value, IGQ coefficient, nucleation gauge, porosity etc. The results of investigations and calculations are displayed in the form of graphs and dependencies. It has been shown that the derivative-thermal analysis (DTA) is an effective complement of chemical analysis and it has been found that both the increase in temperature and metal holding time have a negative impact on the metallurgical quality of liquid metal. The metallurgical quality can be improved by using proper composition of charge materials and modifiers.