Chitosan Fibres Modified by Fibroin

Strobin G., Ciechańska D., Wawro D., Stęplewski W., Jóźwicka J., Sobczak S., Haga A.

Fibres & Textiles in Eastern Europe

2007

Vol. 15, no. 5-6 (64)

146--148

This article presents research results concerning the formation of chitosan fibres modified by silk-fibroin. Silk-fibroin isolated from the Bombyx mori silkworm cocoons and chitosan were used for our investigations. In order to find advantageous fibre-formation conditions, the influence of bath composition and spinning solution composition on the silk-fibroin content in the bath were tested. The best coagulation bath for spinning solution with 5% silk-fibroin content was the aqueous solution of NaOH at concentration of 10%. In the case of spinning solution with 10 and 15% of silk-fibroin the best coagulation bath was aqueous solution of NaOH at concentration of 10% with an ethyl alcohol in the ratio of 70:30. The chitosan/silk-fibroin fibres obtained under these conditions were characterised by a silk-fibroin content from 4,5 to 11% and by mechanical properties sufficient for their further processing into dressing materials

W artykule opisano warunki formowania oraz wybrane właściwości mechaniczne włókien chitozanowych modyfikowanych fibroiną. Do badań zastosowano chitozan oraz fibroiną otrzymaną z jedwabiu natoralnego pochodzącą z kokonów jedwabnika Bombyx mori. Włókna chitozanowe modyfikowane fibroiną formowano z roztworów o zróżnicowanej zawartośco fibroiny. Badasno również wpływ kąpieli koagulacyjnej na właściwości otrzyanych włókien. Stwierdzono, że dla roztworów przędzalniczych o stosunku wagowym chitozanu do fibrainy 90 : 10 oraz 85 : 15 odpowiednią kąpielą koagulacyjną jest wodny roztwór wodorotlenku sodowego o stężeniu 10% wag. zawierający alkohol etylowy w stosunku 70 : 30. Otrzymane włókna chitozanowe modyfikowane fibroiną charakteryzowały się zawartością fibroiny w zakresie od 4,5 do 11% i właściwościami mechanicznymi odpowiednimi do dalszego przerobu włókienniczego.

Formation of Cellulose/Silk - Fibroin Blended Fibres

Strobin G., Wawro D., Stęplewski W., Ciechańska D., Jóźwicka J., Sobczak S., Haga A.

Fibres & Textiles in Eastern Europe

2006

Vol. 14, no. 4 (58)

32--35

This article presents research results concerning the formation of cellulose/silk-fibroin blended fibres. Bio-modified cellulose and silk-fibroin isolated from cocoons of the Bombyx mori silkworm were used for our investigations. In order to find advantageous fibre-formation conditions, the influence of bath composition and formation (spinning) speed on the silk-fibroin content in the fibres was tested. An aqueous solution of sulphuric acid with the addition of ammonium sulphate (VI) and sodium sulphate (VI) was used as the coagulation bath, and the fibre spinning was carried out at speed of 15 m/min. The fibres obtained, with a content of silk-fibroin within the range of 2% to 13.5%, were tested in order to assess their mechanical properties, and their surface and cross-sections state was evaluated by the SEM method.

Pomimo rozwoju inżynierii materiałowej ciągle brak jest nowoczesnego, wielofunkcyjnego materiału opatrunkowego. Jednym z obiecujących kierunków badań w tym obszarze jest opracowanie kompozycji polimerowych, których jednym ze składników jest fibroina – białko fibrylarne charakteryzujące się właściwościami stymulacji procesu gojenia się ran. W pracy zastosowano bio-modyfikowaną celulozę oraz fibroinę wyizolowaną z kokonów jedwabnika Bombyx mori. Zbadano proces mokrego formowania mieszanych włókien celulozowo-fibroinowych. W celu znalezienia optymalnych warunków formowania włókien przeprowadzono badania wpływu składu kąpieli i prędkości formowania na zawartość fibroiny we włóknach. Jako kąpiel koagulującą zastosowano siarczan amonu o stężeniu 450 g/dm3 a formowanie prowadzono przy prędkości 15 m/min. Uzyskane włókna, zawierające od 2 do 13,5% fibroiny, poddano badaniu właściwości mechanicznych oraz ocenie powierzchni i przekroju poprzecznego metodą SEM.