Effect of Wetting Agent and Carbide Volume Fraction on the Wear Response of Aluminum Matrix Composites Reinforced by WC Nanoparticles and Aluminide Particles

Lekatou A., Gkikas N., Karantzalis A. E., Kaptay G., Gacsi Z., Baumli P., Simon A.

Archives of Metallurgy and Materials

2017

Vol. 62, iss. 2B

1235--1242

Aluminum matrix composites were prepared by adding submicron sized WC particles into a melt of Al 1050 under mechanical stirring, with the scope to determine: (a) the most appropriate salt flux amongst KBF4 , K2 TiF6 , K3 AlF6 and Na3 AlF6 for optimum particle wetting and distribution and (b) the maximum carbide volume fraction (CVF) for optimum response to sliding wear. The nature of the wetting agent notably affected particle incorporation, with K2 TiF6 providing the greatest particle insertion. A uniform aluminide (in-situ) and WC (ex-situ) particle distribution was attained. Two different sliding wear mechanisms were identified for low CVFs (≤1.5%), and high CVFs (2.0%), depending on the extent of particle agglomeration.

Microstructure And Mechanical Properties Of Al-WC Composites

Simon A., Lipusz D., Baumli P., Balint P., Kaptay G., Gergely G., Sfikas S., Lekatou A., Karantzalis A., Gacsi Z.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 2B

1517--1521

The scope of the research work is the production and characterization of Al matrix composites reinforced with WC ceramic nanoparticles. The synthesis process was powder metallurgy. The produced composites were examined as far as their microstructure and mechanical properties (resistance to wear, micro/macrohardness). Intermetallic phases (Al12W and Al2Cu) were identified in the microstrucutre. Al4C3 was not detected in the composites. Adding more than 5 wt% WC to the aluminum, microhardness and wear resistance exceed the values of Al alloy. Composites having weak interface bond performed the highest wear rate.