Wyniki wyszukiwania - BazTech

1

Study on Electromagnetic Properties of Graphite/Graphene/Silver-Coated Copper Powder Monolayer Coated Composites

Liu Yuanjun, Han Xiaohui, Bao Wenli, Ding Xiongwei, Zhao Xiaoming

Fibres & Textiles in Eastern Europe

|

2023

|

Vol. 31, no. 1

83--90

EN

With the rapid development of electronic technology and military techniques, electromagnetic protection materials are becoming more and more significant to people. Harmful electromagnetic radiation not only affects the normal operation of electronic equipments and military security, but also has a serious impact on human health. At present, using absorbing and shielding materials are effective means to reduce the harm of electromagnetic waves. In this project, graphite, graphene and silver-coated copper powder coated composites were prepared using PU-2540 polyurethane and adopting a coating process for the substrate on plain polyester/cotton fabric. The controlled variable method was used to prepare and study the electromagnetic properties of single-layer coating composites with different functional particle contents. The result showed that within the frequency range of 0.01GHz~1.0GHz, when the total mass of functional particles was 48% relative to that of the polyurethane, the value of the real part of the dielectric constant of the sample remained the largest and its polarization ability was the strongest. Within the frequency range of 0.08GHz~1.0GHz, when the content of functional particles was 24% relative to that of the polyurethane, the value of the imaginary part of the dielectric constant and the loss of the tangent value of the sample kept the maximum, and the loss and attenuation ability with respect to electromagnetic waves were both the strongest. Within the frequency range of 1.3GHz~2.0GHz, when the content of functional particles was 36% relative to that of the polyurethane, the value of the reflection loss of the sample was -26.93dB, and the minimum value of the reflection loss was obtained at a frequency of 1.6GHz, at the moment of which, the absorbing property of the sample was the best.

2

Research on the Performance of Polypyrrole Coated Conductive Fabrics Prepared from Different Base Materials

Liu Yuanjun, Xue Huangyu, Liu Yanyan, Zhao Jiaqi, Wu Haiying, Zhao Xiaoming

Fibres & Textiles in Eastern Europe

|

2023

|

Vol. 31, no. 2

75--81

EN

In this paper, polypyrrole coated conductive fabrics were prepared using pyrrole as the monomer, p-toluene sulfonic acid as the doping agent and ammonium persulfate as the oxidant, adopting the simple method of situ polymerization of the liquid phase. Six types of conductive polypyrrole coated fabrics were prepared adopting polyester-cotton blended fabrics, nylon fabrics, wool fabrics, silk fabrics, basalt fabrics and aramid fabric respectively as base materials and using the same process conditions; its electrical conductivity was compared, and the distribution and resistance of the washing fastness of polypyrrole on the surface of those fabrics were studied. Results showed that under the same process conditions, the conductivity of polypyrrole coated terylene fabrics was the best, followed by the polypyrrole coated nylon fabrics and polypyrrole coated wool fabrics. Observed by electron microscope, the distribution of polypyrrole was more homogeneous on different base cloths. After washing, it was concluded that the combination fastness of polypyrrole with polyester-cotton, nylon and wool was better, while the combination fastness of polypyrrole with basalt and aramid was poor.

3

Influence of the Content of Nickel Powders on the Electromagnetic Properties of SingleLayer Coated Polyester-Cotton Plain Weave Fabric

Liu Yuanjun, Xue Huangyu, Wang Ciyi, Han Xiaohui, Zhao Xiaoming

Fibres & Textiles in Eastern Europe

|

2022

|

Vol. 30, no. 5

47--52

EN

A coated composite was prepared on polyester-cotton plain weave fabric, using PU2540 polyurethane as the matrix. The influences of the content of nickel powders on the dielectric constant (the real and imaginary parts and loss tangent value), reflection loss and shielding effectiveness of single-layer coated composites were mainly investigated. The results showed that within the frequency range of 1-1000 MHz, the value of the real part of the dielectric constant of the coated composites was the largest, and the polarisation ability with regard to electromagnetic waves was the strongest when the content of nickel powders was 40%. Within the frequency range of 15-225 MHz, the value of the imaginary part of the dielectric constant of the coated composites was the largest and the loss ability with regard to electromagnetic waves was the strongest when the content of nickel powders was 40%. Within the frequency range of 250-800 MHz, the loss tangent value of the dielectric constant of coated composites was the largest, and the attenuation ability with regard to electromagnetic waves was the strongest when the content of nickel powders was 40%. Within the frequency range of 1220-3000 MHz, the reflection loss value was the smallest when the content of nickel powders was 40%, and its absorption ability with regard to electromagnetic waves was the strongest. Within the frequency range of 760-3000 MHz, the shielding effectiveness of the coated composite was the largest when the content of nickel powders was 40%.

4

Study of the Dielectric Properties and Conductivity of Double Coated Glass Fibre Felt Composites

Liu Yuanjun, Wang Caixia, Ma Yiping, Liu Yanyan, Wu Haiying, Zhao Xiaoming

Fibres & Textiles in Eastern Europe

|

2021

|

Vol. 29, no. 4 (148)

75--80

EN

Graphite/talcum powder double-coated glass fibre felt composites were prepared using glass fibre felt as the base material, graphite as the surface absorbing agent, talcum powder as the underlying absorbing agent, epoxy resin E44 as the adhesive and low molecular 650 polyamide as the curing agent. The influences of the surface graphite content and underlying talcum powder content on the dielectric properties and conductivity of glass fibre felt composites were the main focus of the investigation. Results showed that when the frequency is less than 103 Hz, the values of the real and imaginary parts of the dielectric constant for double-coated glass fibre felt composites are largest when the surface graphite content is 50%. When the frequency is larger than 106 Hz, the value of the real part of the conductivity is largest when the graphite contents are 40% and 50%. When the frequency is less than 104Hz, the real part of the dielectric constant of the glass fiber mat composites is the largest when the talc content is 40%, and when talc content is 60%, the imaginary part of dielectric constant of glass fiber mat composites is the largest. The maximum loss tangent value for the composites occurs when the talcum powder content is 40%. When the frequency is larger, the value of the real part of the conductivity increases gradually.

PL

W pracy przygotowano podwójnie powlekane kompozyty filcu z włókna szklanego w postaci grafit/talk. Użyto filcu z włókna szklanego jako materiału bazowego, grafitu jako powierzchniowego środka pochłaniającego, talku jako podstawowego środka pochłaniającego, żywicy epoksydowej E44 jako kleju i poliamidu 650 o niskiej masie cząsteczkowej jako środek utwardzającego. Głównym przedmiotem badań było określenie wpływu zawartości grafitu powierzchniowego oraz zawartości proszku talku na właściwości dielektryczne i przewodność kompozytów z filcu z włókna szklanego. Wyniki wykazały, że gdy częstotliwość jest mniejsza niż 103 Hz, wartości części rzeczywistej i urojonej stałej dielektrycznej dla podwójnie powlekanych kompozytów z filcu z włókna szklanego są największe, gdy zawartość grafitu powierzchniowego wynosi 50%. Gdy częstotliwość jest większa niż 106 Hz, wartość rzeczywistej części przewodnictwa jest największa, gdy zawartość grafitu wynosi 40% i 50%. Maksymalna wartość tangensa strat dla kompozytów występuje, gdy zawartość talku wynosi 40%. Gdy częstotliwość jest większa, wartość rzeczywistej części przewodnictwa stopniowo wzrasta.

5

Synthesis of a Decolourising Agent and its Application

Liu Yuanjun, Yu Yongtao, Du Huanfu, Niu Jiarong, Zhao Xiaoming

Fibres & Textiles in Eastern Europe

|

2020

|

Vol. 28, no. 1 (139)

100--105

EN

A type of cationic decolourising agent was prepared and applied to printing and dyeing wastewater treatment. The effects of the concentration of the decolourising agent, the pH value and stirring speed on decolourisation efficiency were studied. The results show that the optimum decolourisation process of the decolourising agent is determined as follows: at room temperature, a dosage of the decolourising agent of 7 mg/l, pH =7.0, and a stirring speed of 150 rpm. The decolourising agent applied to decolourise a direct dye, strong acid dye, weak acid dye and reactive dye in simulated wastewater showed high decolourisation efficiency in all cases. The range of decolourisation efficiency from the highest to lowest is as follows: direct dye, weak acid dye, strong acid dye, and reactive dye.

PL

Przygotowano kationowy środek odbarwiający, który zastosowano do drukowania i oczyszczania ścieków barwiarskich. Zbadano wpływ stężenia środka odbarwiającego, wartości pH i prędkości mieszania na skuteczność odbarwiania. Wyniki pokazują, że optymalny proces odbarwiania środkiem odbarwiającym następuje w określonych warunkach: w temperaturze pokojowej, dawka środka odbarwiającego 7 mg/l, pH = 7,0 i szybkość mieszania 150 obrotów na minutę. Środek odbarwiający zastosowany do odbarwiania barwników: bezpośredniego, kwasowego mocnego, słabo kwasowego i reaktywnego w symulowanych ściekach wykazywał we wszystkich przypadkach wysoką skuteczność odbarwiania. Zakres wydajności dekoloryzacji od najwyższej do najniższej jest następujący: barwniki: bezpośredni, słabo kwasowy, kwasowy mocny i reaktywny.

6

Study on the Thermal Insulation Performance of PAN Pre-Oxidised Fibre Felts

Zhao Xiaoming, Liu Yuanjun, Liang Tenglong

Fibres & Textiles in Eastern Europe

|

2020

|

Vol. 28, no. 3 (141)

27--37

EN

In this paper, an orthogonal experiment of 3 factors and 3 levels was firstly designed to prepare PAN pre-oxidised fibre felts with good thermal insulation properties; the range method was used to analyse the result of the orthogonal experiment, and finally the tensile properties and thermal stability were tested. Finally, pre-oxidised fibre felt composites for the coating of silica aerogel were prepared using the coating process to compound silica aerogel on re-oxidised fibre felts. Firstly, the influence of the content of silica aerogel on the heat insulation performance of the coated composite materials was analysed, and then a test of the coefficient of thermal conductivity, an experiment on the back temperature, and characterisations of the tensile properties and thermal stability of the composite coating of pre-oxidised fibre felt composites of the coating of silica aerogel were carried out. Results showed that through analysis of the orthogonal experiment, we can state that the best preparation process of pre-oxidised fibre needled felts was as follows: needle number – 2, needle depth – 8 mm, and needle frequency – 140 times/min. The transverse tensile strength of PAN pre-oxidised fibre needled felts prepared by crossly webbing of PAN pre-oxidised fibres was superior to the longitudinal tensile strength; thermogravimetric analysis showed that the pre-oxidised fibre needled felts had excellent thermal stability. The coefficient of thermal conductivity of the aerogel coating of the composites firstly decreased and then increased with an increase in the content of aerogel. Coated composites had the lowest coefficient of thermal conductivity when the aerogel content was 4% wt. At temperatures of 100 °C, 150 °C and 200 °C, the heating rate of the transient-state back temperature and the steady-state average temperature were both the lowest when the aerogel content was 6% wt.

PL

W artykule zaprojektowano ortogonalny eksperyment z 3 czynnikami i 3 poziomami w celu przygotowania wstępnie utlenionych filców PAN o dobrych właściwościach termoizolacyjnych; do analizy wyników eksperymentu ortogonalnego zastosowano metodę zakresu, a na koniec przetestowano właściwości rozciągania i stabilność termiczną. Najpierw przeanalizowano wpływ zawartości aerożelu krzemionkowego na właściwości izolacji cieplnej powleczonych materiałów kompozytowych, a następnie wykonano test współczynnika przewodności cieplnej, przeanalizowano też charakterystykę właściwości rozciągania i stabilności termicznej powłoki kompozytowej wstępnie utlenionych kompozytów filcowych. Wyniki pokazały, że poprzez analizę eksperymentu ortogonalnego można stwierdzić, że najlepszy proces przygotowania filców igłowanych charakteryzuje się następującymi parametrami: liczba igły – 2, głębokość igły – 8 mm i częstotliwość igły – 140 razy/min. Wytrzymałość poprzeczna na rozciąganie igłowanych filców z włókien PAN była lepsza niż wytrzymałość na rozciąganie wzdłużne; analiza termograwimetryczna wykazała, że igłowane filce z wstępnie utlenionego włókna miały doskonałą stabilność termiczną. Współczynnik przewodności cieplnej powłoki aerożelowej kompozytów najpierw zmniejszył się, a następnie wzrósł wraz ze wzrostem zawartości aerożelu. Powlekane kompozyty miały najniższy współczynnik przewodności cieplnej, gdy zawartość aerożelu wynosiła 4% wag. W temperaturach 100, 150 i 200 °C szybkość ogrzewania i średnia temperatura w stanie ustalonym były najniższe, gdy zawartość aerożelu wynosiła 6% wag.

7

Study on the Electromagnetic and Mechanical Properties of Coated Composites

Liu Yuanjun, Wang Huanhuan, Zhang Yiqu, Wang Xichen, Yin Guang, Han Xiaohui, Niu Jiarong

Fibres & Textiles in Eastern Europe

|

2020

|

Vol. 28, no. 6 (144)

89--97

EN

In this paper, a single-layer coated composite was prepared using PU2540 polyurethane as the matrix, nickel powder as the wave-absorbing functional particle, and coating technology on plain cotton fabric. The influence of the content of nickel powder on the dielectric properties (the real and imaginary parts and the loss tangent value), the shielding effectiveness and the mechanical properties was studied adopting the method of controlling variables. The result showed that when the content of nickel powder was 0~20% and that of nickel powder relative to that of polyurethane was 20%, the real and imaginary parts of the dielectric constant of the coating were the largest, and its polarising and loss ability with respect to electromagnetic waves were the strongest; when the content of nickel powder relative to that of polyurethane was 15%, the loss tangent value of the coating was the largest, and its absorption and attenuation ability with respect to electromagnetic waves was the strongest. When the values of the coating thickness were at 0.5~2 mm, the real and imaginary parts of the dielectric constant of the coating with a thickness of 1 mm were the largest, and the polarising and loss ability with respect to electromagnetic waves were the strongest. When the loss tangent value and the shielding-attenuation value of the coating with a thickness of 2 mm were the largest, the absorbing-attenuation and shielding-attenuation ability with respect to electromagnetic waves were the strongest.

PL

W pracy wykonano jednowarstwowy kompozyt powlekany z poliuretanu PU2540 jako matrycy i proszku niklowego jako cząstki funkcjonalnej pochłaniającej fale. Przyjmując metodę regulacji zmiennych zbadano wpływ zawartości proszku niklowego na właściwości dielektryczne (części rzeczywiste i urojone oraz wartość stycznej strat) i skuteczność ekranowania oraz właściwości mechaniczne. Wyniki pokazały, że w przypadku zawartości proszku niklu w stosunku do zawartości poliuretanu wynoszącej 20%, rzeczywiste i urojone części stałej dielektrycznej powłoki były największe, a jej polaryzacja w odniesieniu do fal elektromagnetycznych była najsilniejsza. Gdy zawartość proszku niklu w stosunku do poliuretanu wynosiła 15%, wartość stycznej straty powłoki była największa, a jej zdolność pochłaniania i tłumienia fal elektromagnetycznych była największa. Gdy wartości grubości powłoki wynosiły 0,5~2 mm, rzeczywiste i urojone części stałej dielektrycznej powłoki o grubości 1 mm były największe, a polaryzacja w odniesieniu do fal elektromagnetycznych była najsilniejsza. Gdy wartość styczna strat i wartość tłumienia ekranowania powłoki o grubości 2 mm były największe, to zdolność tłumienia absorpcji i tłumienia ekranowania fal elektromagnetycznych była najsilniejsza.

8

Preparation of Polypyrrole/Polyurethane Foam Composite Material

Liu Yuanjun, Li Wenyue, Kick Christopher, Zhao Xiaoming, Wu Haiying

Fibres & Textiles in Eastern Europe

|

2020

|

Vol. 28, no. 3 (141)

69--73

EN

Firstly, the paper focused on the polyurethane foam soaking process with pyrrole solution, and discuss the estimated electro-mechanical properties of the modified PU foam. Secondly, scanning electron microscopy (SEM) micrographs were collected to understand the polypyrrole distribution inside the foam. The results show that the chemical polymerisation parameters needed to realise this amount of polypyrrole in the foam were 0.1 mol/L of pyrrole, a mole ratio of 1:2.25, an oxidation temperature of 12 ± 3 °C, and an oxidation time of 2 hours. SEM images of the samples prepared with the modified approach showed a continuous layer of about 10-15 μm thickness of the polypyrrole attached to the surface of the PU foam.

PL

W artykule skoncentrowano się na procesie namaczania pianki poliuretanowej roztworem pirolu i omówiono oszacowane właściwości elektromechaniczne zmodyfikowanej pianki PU. Następnie zbadano rozkład polipirolu wewnątrz pianki przy zastosowaniu skaningowego mikroskopu elektronowego (SEM). Wyniki pokazały, że parametry polimeryzacji chemicznej potrzebne do uzyskania odpowiedniej ilości polipirolu w piance wynosiły 0,1 mol/l pirolu, stosunek molowy wynosił 1:2,25, temperatura utleniania wynosiła 12 ± 3 ° C i czas utleniania 2 godziny. Obrazy SEM próbek przygotowanych zgodnie ze zmodyfikowanym podejściem pokazały ciągłą warstwę o grubości około 10-15 μm polipirolu na powierzchni pianki PU.

9

Influence of Wave-Absorbing Functional Particles on the Electromagnetic Properties and Mechanical Properties of Coated Composites for Nickel Powders

Liu Yuanjun, Wang Yi, Wu Xiang, Zhang Lulu, Niu Jiarong

Fibres & Textiles in Eastern Europe

|

2020

|

Vol. 28, no. 5 (143)

75--81

EN

In this subject, a single-layer coated composite for nickel powders was prepared using PU2540 polyurethane as the matrix, nickel powder as the wave-absorbing functional particle, and coating technology on plain cotton fabric. The influence of wave-absorbing functional particles on the dielectric, shielding effectiveness and mechanical properties of the single-layer coated composite for nickel powders was mainly analysed and compared. Results showed that the real and imaginary parts and loss tangent of the dielectric constant were all the largest when the iron powder was mixed with the nickel powder, and its polarizing ability, loss ability and attenuation ability with respect to electromagnetic waves were all the maximum. When the graphene was mixed with the nickel powder, the shielding attenuation ability with respect to electromagnetic waves was the best.

PL

W ramach pracy przygotowano jednowarstwowy kompozyt powlekany żywicą poliuretanową zawierającą proszek niklu. Do przygotowania kompozytów użyto poliuretanu PU2540 jako matrycy i proszku niklu jako absorbującej fale cząstki funkcjonalnej oraz zastosowano technologię powlekania na gładkiej tkaninie bawełnianej. Przeanalizowano i porównano głównie wpływ absorbujących fale funkcjonalnych cząstek na dielektryk, skuteczność ekranowania i właściwości mechaniczne jednowarstwowego powlekanego kompozytu. Wyniki pokazały, że rzeczywiste i urojone części oraz styczna strat stałej dielektrycznej były największe, gdy proszek żelaza został zmieszany z proszkiem niklu, a jego zdolność polaryzacyjna, zdolność do strat i zdolność tłumienia fal elektromagnetycznych były maksymalne. Gdy grafen został zmieszany z proszkiem niklu, zdolność tłumienia ekranowania fal elektromagnetycznych była najlepsza.

10

Influence of the Thickness of Graphene Coating on the Electromagnetical and Mechanical Properties of Double-Layer Coated Basalt Fibre Fabrics

Liu Yuanjun, Yang Yanfeng, Yang Zhanhua, Liu Yanyan, Su Ying, Niu Jiarong

Fibres & Textiles in Eastern Europe

|

2020

|

Vol. 28, no. 5 (143)

69--74

EN

A double-layer coated basalt fibre fabric was prepared using polyurethane as the matrix and applying coating technology to the basalt fibre fabric. The influence of the thickness of the graphene coating on the electromagnetic properties and mechanical properties of the double-layer coated basalt fibre fabric was studied. Results showed that when the thickness of the graphene coating was 2.0 mm, the polarising ability, loss ability and attenuating ability of the fabric with respect to electromagnetic waves were all the largest. Along with the increasing thicknesses of the graphene coating, the electromagnetic shielding effectiveness of the double-layer coated basalt fibre fabric also increased, then the shielding ability against electromagnetic waves became stronger.

PL

W pracy przygotowano dwuwarstwowo powlekaną tkaninę z włókna bazaltowego, stosując poliuretan jako matrycę i stosując technologię powlekania na tkaninę z włókien bazaltowych. Badano wpływ grubości powłoki grafenowej na właściwości elektromagnetyczne i mechaniczne dwuwarstwowo powlekanej tkaniny bazaltowej. Wyniki pokazały, że gdy grubość powłoki grafenowej wynosiła 2.0 mm, polaryzacja, zdolność do strat i zdolność tłumienia tkaniny w odniesieniu do fal elektromagnetycznych były największe. Wraz ze wzrostem grubości powłoki grafenowej wzrastała również skuteczność ekranowania elektromagnetycznego dwuwarstwowo powlekanej tkaniny bazaltowej z włókien bazaltowych, a następnie zdolność ekranowania przed falami elektromagnetycznymi stała się silniejsza.

11

Influence of the Needle Depth and Frequency on the Thermal Insulation Performance of Pre-Oxidised Fibre Felts

Zhao Xiaoming, Liu Yuanjun, Liang Tenglong, Zheng Zhenrong

Fibres & Textiles in Eastern Europe

|

2020

|

Vol. 28, no. 4 (142)

57--66

EN

In this paper, the influence of the needle depth and frequency on the thermal insulation performance of pre-oxidised fibre felts was mainly investigated. The results showed that pre-oxidised fibre felts of a needle depth of 8 mm at a room temperature and working temperature of 100-200 °C had the best thermal insulation performance, while fibre for those of different needle depths with increasing temperature, the steady-state temperature difference increased linearly. With an increasing needle frequency, the thickness and gram weight of the pre-oxidised fibre felts showed a decreasing trend, while the coefficient of thermal conductivity exhibited an increasing one. For pre-oxidised fibre felts of different needle frequencies with increasing temperature, the steady-state temperature difference showed a linearly increasing trend.

PL

W pracy zbadano wpływ głębokości i częstotliwości igłowania na wydajność izolacji termicznej wstępnie utlenionych filców. Wyniki wykazały, że wstępnie utlenione filce igłowane na głębokość 8 mm w temperaturze pokojowej i temperaturze roboczej 100-200 °C miały najlepszą izolację termiczną. Wraz ze wzrostem częstotliwości igłowania grubość i gramatura wstępnie utlenionych filców wykazywały tendencję spadkową, podczas gdy współczynnik przewodności cieplnej wzrastał. W przypadku wstępnie utlenionych filców różnych częstotliwościach igłowania ze wzrostem temperatury różnica temperatur w stanie ustalonym wykazywała liniowo rosnący trend.

12

Discussion on the Tensile and Bending Properties of PAN-based Pre-oxidised Fibre Felt Composite Materials

Liu Yuanjun, Bao Wenli, Zhao Xiaoming

Fibres & Textiles in Eastern Europe

|

2020

|

Vol. 28, no. 2 (140)

57--60

EN

The impact of the mass percentage of PAN-based pre-oxidised fibre felt in a composite material and of the curing temperature on the composite material’s mechanical properties were studied in order to optimise the preparation method of epoxy resin composite material. The results showed that when the dosage of PAN-based pre-oxidised fibre felt was 15% of the mass of epoxy resin and the curing temperature was 170 °C, the tensile and bending properties of the composite materials produced were the best. This study has addressed the absence of reports on this type of composite material, and is expected to lead to the development of applications for this new type of composite material.

PL

W celu zoptymalizowania metody przygotowania materiału kompozytowego z żywicy epoksydowej zbadano wpływ procentu masy wstępnie utlenionego filcu z włókien PAN w materiale kompozytowym i temperatury utwardzania na właściwości mechaniczne materiału kompozytowego. Wyniki pokazały, że najlepsze właściwości rozciągania i zginania wytwarzanych materiałów kompozytowych otrzymano dla 15% ilość wstępnie utlenionego filcu z włókien PAN w stosunku do masy żywicy epoksydowej, a optymalna temperatura utwardzania wynosiła 170 °C. Autorzy pracy oczekują, że przeprowadzone badanie doprowadzi w przyszłości do opracowania aplikacji dla nowego rodzaju materiału kompozytowego.

13

Preparation of a Kind of Non-Woven Viscose Colour Absorbing Material and Research of its Colour Absorption Properties

Wang Xueyan, Liu Yuanjun, Lv Rong

Fibres & Textiles in Eastern Europe

|

2019

|

Vol. 27, no. 3 (135)

71--77

EN

A non-woven viscose material was modified with self-made cationic gelatin protein auxiliary by the padding process. The material prepared was then used as an environmentally friendly colour absorbent for the decolourisation of dye wastewater. The effects of the sodium hydroxide swelling pretreatment process and cationic padding modification process on the colour absorption and decolourisation rate were discussed. Moreover an optimal preparation process for the colour-absorbing material was determined. This was as follows: In order to make the non-woven viscose material swell and improve the subsequent modification effect, first the non-woven viscose material was pretreated with an aqueous solution containing 50 g/l of sodium hydroxide, at room temperature, for 5 min. Then the material was padded in a mixed aqueous solution containing 80 g/l of cationic gelatin and 18 g/l of sodium hydroxide by means of a laboratory padder with two dips and two nips. After treatment, the material was dried and steamed for 4 min. Lastly the material was washed with water and dried. The results show that the colour-absorbing material prepared by this process has the advantages of a high colour absorption rate and high decolourisation percentage. And it could be applied to the decolourisation of printing and dyeing wastewater, or to prevent washed off dyestuff staining on light colour clothes in the process of laundry.

PL

W pracy otrzymano włókninowy materiał wiskozowy, a następnie zmodyfikowano go przy zastosowaniu białka żelatynowego wspomagającego proces napawania. Przygotowany materiał został następnie użyty jako przyjazny dla środowiska absorbent koloru do odbarwiania ścieków barwników. W artykule omówiono wpływ procesu wstępnej obróbki wodorotlenkiem sodu i procesu modyfikacji na absorpcję koloru i szybkość odbarwiania. Ponadto określono optymalne parametry procesu przygotowania materiału pochłaniającego kolor. W celu spęcznienia włókninowego materiału wiskozowego i poprawy późniejszego efektu modyfikacji, najpierw poddano go wstępnej obróbce wodnym roztworem zawierającym 50 g/l wodorotlenku sodu, w temperaturze pokojowej, przez 5 minut. Następnie materiał napawano roztworem wodnym zawierającym 80 g/l żelatyny i 18 g/l wodorotlenku sodu. Po obróbce materiał wysuszono i poddano działaniu pary przez 4 minuty. Na końcu materiał przemyto wodą i wysuszono. Wyniki pokazały, że materiał absorbujący kolor przygotowany tym sposobem szybko pochłania kolor i posiada wysoki procent odbarwiania. Materiał może być zastosowany do odbarwiania druku i ścieków barwiarskich, lub do zapobiegania farbowania jasnych ubrań w procesie prania.

14

Investigation into the Dielectric Properties of Polypyrrole Coated Fabrics Composites

Ge Chuanbing, Liu Yuanjun, Qian Xiaoming, Zhao Xiaoming

Fibres & Textiles in Eastern Europe

|

2019

|

Vol. 27, no. 5 (137)

75--81

EN

Flexible polypyrrole coated fabric composites with good dielectric properties were produced using pyrrole as a monomer by in-situ polymerisation on polyester fabric. Initially, the influence of the pyrrole concentration, temperature and time on the dielectric constant of the real and imaginary parts, the loss tangent, and the surface resistance of the composites were investigated. Subsequently, exterior morphologies was analysed. The results show that the pyrrole concentration, the reaction temperature and time had a significant influence on the real and imaginary parts of the dielectric constant, the loss tangent, and the surface resistance of the composites. The polypyrrole composites produced show good performance in terms of dielectric properties and electrical conductivity.In the 0-106 Hz frequency range, the values of the real and imaginary parts of the dielectric constant of the 0.8mol/L group are both at their largest. Moreover, the value of the surface resistance of the 0.8 mol/L group is at its smallest, and the value of the surface resistance of the 0.2 mol/L group is at its largest, which is 12 times the value given by the 0.8mol/L group.Values of the real and imaginary parts of the dielectric constant, and the loss tangent for the experimental group produced by polymerisation at ambient temperature are at their largest, which is superior to the other groups. The value of the surface resistance for the experimental group produced at ambient temperature is at its smallest and the electrical conductivity is at its strongest; the higher the reaction temperature, the larger the value of the resistance. The various dielectric properties of the 150 min group are better than for the other groups.

PL

W pracy wytworzono kompozyty z elastycznych tkanin powlekanych polipirolem. Oceniono właściwości dielektryczne wytworzonych tkanin. Badano wpływ stężenia pirolu, temperatury i czasu na stałą dielektryczną i odporność powierzchni kompozytów. Następnie przeanalizowano morfologię zewnętrzną. Wyniki pokazały, że stężenie pirolu, temperatura i czas reakcji miały znaczący wpływ na stałą dielektryczną i odporność powierzchni kompozytów. Wytworzone kompozyty wykazywały dobrą wydajność pod względem właściwości dielektrycznych i przewodności elektrycznej. W zakresie częstotliwości 0-106 Hz wartości stałej dielektrycznej dla stężenia polipirolu 0,8 mola/l były największe. Wartość rezystancji powierzchniowej dla stężenia polipirolu 0,8 mol/l była najmniejsza, a wartości rezystancji powierzchniowej dla stężenia polipirolu 0,2 mol/l były największe, co stanowiło 12-krotność wartości podanej dla stężenia polipirolu 0,8 mola/l. Dla próbki wytworzonej przez polimeryzację w temperaturze otoczenia wartości stałej dielektrycznej były największe, natomiast wartość rezystancji powierzchniowej była najmniejsza, a przewodność elektryczna najsilniejsza. Stwierdzono, że im wyższa temperatura reakcji, tym większa wartość oporu. Różne właściwości dielektryczne próbki uzyskanej z czasem reakcji 150 min były lepsze od innych grup.

15

Influence of the Yarn Fineness and Stitch Length of Polyester Knitted Fabric on the Dielectric Constant

Liu Yuanjun, Li Wenyue, Zhao Xiaoming

Fibres & Textiles in Eastern Europe

|

2019

|

Vol. 27, no. 6 (138)

63--66

EN

The influence of the yarn fineness and stitch length of polyester knitted fabrics on the dielectric constant was investigated by the single factor test method. As a result of the investigation, polyester knitted fabric parameters were chosen so as to obtain a polyester knitted fabric with the maximum real part and imaginary part of the dielectric constant. The results show that when the yarn fineness is 59 tex and the mark of the stitch length is 75, the polyester knitted fabric displayed the maximum real part and imaginary part of the dielectric constant. Finally, the polyester knitted fabric with these parameters had good microwave absorbing properties.

PL

W pracy, metodą testu jednoczynnikowego, badano wpływ grubości przędzy i długości oczka dzianin poliestrowych na stałą dielektryczną. W wyniku badań dobrano parametry dzianiny poliestrowej, tak aby uzyskać dzianinę o maksymalnej stałej dielektrycznej. Wyniki pokazały, że przy grubości przędzy wynoszącej 59 tex i długości oczka 75, dzianina poliestrowa charakteryzowała się najwyższą stałą dielektryczną i miała dobre właściwości pochłaniania mikrofal.