Effect of Delta Ferrite on the Mechanical Properties of Dissimilar Ferritic-Austenitic Stainless Steel Welds

Ghasemi R., Beidokhti B., Fazel-Najafabadi M.

Archives of Metallurgy and Materials

2018

Vol. 63, iss. 1

437--443

The dissimilar welds of AISI 304 to AISI 430 stainless steel was investigated by using gas tungsten arc welding. Three filler metals including ER309L, ER316L and ER2594 were applied. The weakest region of the welds was the heat affected zone of 430 stainless steel due to the formation of martensite. Also, the wide grain growth zone was observed in this side. The ferrite number for type 309L, 316L and 2594 weld metals was about 15, 32 and 57, respectively. The hardness and tensile strength values of the weld metals were higher than that of the heat affected zones and the base metals. The ferrite presented higher hardness values than the austenite in type 316L and 309L joints; while the hardness of austenite and ferrite was comparable in type 2594 weld metal.

Comparing the Physical Properties of Produced Sirospun and New Hybrid Solo-Siro Spun Blend Wool/Polyester Worsted Yarns

Ghasemi R., Mozafari-Dana R., Etrati S. M., Shaikhzadeh Najar S.

Fibres & Textiles in Eastern Europe

2008

Vol. 16, no. 1 (66)

24--27

The aim of this paper is to present the utilisation of a Solospun roller in the Sirospun spinning system in order to improve the properties of worsted wool/polyester yarns, especially the yarn hairiness. In this work, a Solospun roller was used and different worsted yarns (45% wool, 55% polyester) with a yarn linear density (count) of 50 tex and twist factors (αTt) of 2530, 2846, 3162, 3478, and 3795 were produced using the Sirospun spinning system with and without a Solo-spun roller. Afterwards, the yarn physical properties including hairiness, tensile strength, elongation, unevenness and abrasion resistance were measured and compared. The results indicate that increasing the yarn twist factor within the range of 2530 to 3478 decreases the hairiness of Solo-Siro spun yarn. It is also shown that the hairiness of Solo-Siro spun yarns is significantly less than that of Sirospun yarns. The evenness, count and twist of Solo-Siro spun yarns change slightly in comparison with Sirospun yarns. However, other yarn specifications, such as tensile strength, elongation and abrasion resistance remain almost un-changed.

Przedstawiono zastosowania rolek Solospan w systemie przędzenia Sirospun w celu polepszenia właściwości zgrzeblonych przędz mieszankowych bawełniano-poliestrowych, szczególnie ich włochatości. W pracy stosowano przędze 45% wełny/55% poliestru 50 tex i αTt = 2539, 2846, 3162 3476 i 3795. które przędziono systemem Sirospun z rolką i bez rolki Solospun. Oznaczano włochatość, wytrzymałość na zrywanie, wydłużenie przy zrywaniu nierównomierność masy liniowej i odporność na ścieranie. Stwierdzono, że włochatość przędz przędzonych systemem Solo-Sirospun spada ze wzrostem współczynnika skrętu do 3478 i jest mniejsza niż tych przędzionych systemem Sirospun. Masa liniowa, współczynnik nierównomierności masy liniowej i skręt zmieniały się nieznacznie po zastosowaniu rolki, podczas gdy wytrzymałość na zrywanie wydłużenie i odporność na ścieranie pozostały praktycznie na tym samym poziomie.