Wyniki wyszukiwania - BazTech

1

Leaching of lead and copper from flash smelting slag by citric acid

Gargul K., Boryczko B., Bukowska A., Jarosz P., Malecki S.

Archives of Civil and Mechanical Engineering

|

2019

|

Vol. 19, no. 3

648--656

EN

As a direct-to-blister copper flash smelting slag contains important levels of copper (14%) and lead (2–4%) it is subjected to a process of high temperature reduction. To recover copper as well as lead the slag is subjected then to a process of decopperization by reducing the oxide metal compounds in an electric furnace. This study presents an alternative to the above process by recovering Pb and Cu from the slag by a hydrometallurgical route using citric acid solutions. The objective of this study was to determine process parameters at which the effectiveness of the lead leaching process is greatest with the minimum transfer of copper to the solution. This paper presents the results of laboratory tests on flash smelting slag leaching with citric acid solutions. Process parameters (time, temperature, citric acid concentration, l/s ratio) at which the Pb concentration decreases from the initial value (3.05%) to the value of 0.41–0.6% in the post-leaching sediment were determined. Analogous values for copper were 12.44% (before leaching) and 11.5–11.8% (after). The lead and copper content was determined by atomic absorption spectrometry (AAS). The hydrometallurgical method could successfully replace the existing treatment of slag in an electric furnace and converter.

2

Hydrometallurgical recovery of lead from direct-to-blister copper flash smelting slag

Gargul K., Boryczko B., Bukowska A.

Archives of Civil and Mechanical Engineering

|

2017

|

Vol. 17, no. 4

905--911

EN

Furnace slag from direct-to-blister smelting of copper concentrates contains 12–15% of copper and 2.5–4% of lead. In this form it cannot be deemed as waste material, and thus it is subjected to a high-temperature process of slag decopperization; after this, converting process is performed on the Cu–Pb–Fe alloy being the product of decopperization process in electric furnace. An interesting alternative to the presently used processing of flash smelting slag would be its hydrometallurgical processing and selective recovery of Pb and Cu. This paper presents the results of laboratory tests on flash smelting slag leaching with acetic acid solutions and acetic acid with urea additive. The experiments performed allowed to optimize the process parameters to such an extent that Pb content in the post-leaching sediment is practically equal to the value obtained through the high-temperature process performed in electric furnace.

3

Forecasting in the presence of microstructural changes for the case of P91 steel after long-term ageing

Zieliński A., Miczka M., Boryczko B., Sroka M.

Archives of Civil and Mechanical Engineering

|

2016

|

Vol. 16, no. 4

813--824

EN

The statistical analysis of experimental data was presented and the precipitate diameter forecast for selected steel grade was developed in this paper. The investigations of changes in the material microstructure were carried out under high-temperature conditions. Therefore, this material was characterised by increasing instability over time. Long-term ageing tests were carried on P91 steel for 103, 104, 3 × 104 and 7 × 104 h at 600 and 650 °C. The recorded microstructure images allowed the quantitative analysis of precipitates that occur mainly at the former austenite grain boundaries and martensite laths. The statistical distribution forecast was developed for the ageing time of 105 h. The forecasting under the conditions of material structure changes requires repealing classic assumptions adopted in the theory of prediction. Such methodology was proposed in this article. This article is the basis for the development of further research in this field. The proposed methodology can be used for diagnostic purposes and in the equipment failure risk assessment.

4

Analiza informacji wizyjnej jako elementu wspomagającego proces zarządzania i prognozowania w przedsiębiorstwie

Boryczko B.

Logistyka

|

2015

|

nr 6

19--22, CD

PL

Wiele przedsiębiorstw przemysłowych posiada obecnie systemy telewizji przemysłowej wykorzystywane przede wszystkim do celów ochrony, monitorowania. Uzupełnienie funkcjonujących systemów o specjalistyczne urządzenia z oprogramowaniem pozwalającym na rozpoznawanie i analizę obrazów, umożliwia pozyskanie wielu danych, które mogą być wykorzystane w procesie zarządzania i przygotowywania prognoz dla przedsiębiorstwa. Przedmiotem artykułu jest przedstawienie w jaki sposób można automatycznie analizować informacje z systemów telewizji przemysłowej i uzyskiwać w wyniku tych analiz dane przydatne w procesach zarządzania i prognozowania w przedsiębiorstwie.

EN

Many industrial plants, factories have Close Circuit Television systems used for security and monitoring purposes. Extension of existing systems with specialized devices with software for recognition and image analysis, allows to acquire multiple data that can be used in the management and preparation of forecasts for the company. The article describes how automatically analyze information from CCTV systems and obtain as a result of these analyzes data useful for business management and forecasting.

5

The reliability of long – term energy forecasts

Boryczko B., Kolenda Z., Nowak W.

Gospodarka Surowcami Mineralnymi

|

2015

|

T. 31, z. 4

111--137

EN

The paper demonstrates that the possibilities of producing reliable long-term energy forecast are limited. Global economic growth is so dynamic that the changes resulting from scientific and technological progress, which we experience, do not allow for the identification of goals over longer time intervals. For this reason, forecasting up to 2035, 2040, 2060 is devoid of its fundamental value, which is the reliability of results obtained. Are predictions to be conservative (this applies to richer countries) or are they to produce a paradigm shift by, for example, strongly imposing the requirement of increasing energy security, which is important for our country? In light of the broadness of the issues, this paper is limited to considerations relating to forecasting the primary energy demand. Detailed examples are presented for the Polish energy system.

PL

Prognozy rozwojowe różnych dziedzin stanowią istotny element w planowaniu rozwoju cywilizacyjnego społeczeństw. Trudno wyobrazić sobie podjęcie decyzji przez instytucje rządowe bez jakichkolwiek przewidywań dotyczących przyszłości. W obecnej chwili prognozy określające kierunki rozwoju systemów energetycznych odgrywają istotną rolę w zapewnieniu suwerenności ekonomicznej i politycznej krajów. Wiąże się to bezpośrednio z zamierzeniami i decyzjami w zakresie inwestycyjnym dotyczącym nowych źródeł na energię pierwotną, jak i energię finalną. Dołączyć należy wszystkie aspekty oddziaływania, zwykle niekorzystne, na środowisko naturalne. Waga problemu jest szczególnie wyraźna jeżeli uwzględni się oczywistą zależność pomiędzy wartością GNP (Gross National Product) a zużyciem energii pierwotnej. Niestety, wszelkiego rodzaju prognozowanie, jak każda ekstrapolacja, obarczone jest zawsze błędami. W wielu przypadkach wartości błędów są tak duże, że proponowane prognozy tracą sens. Przykładami są m. in. nieudane prognozy cen ropy naftowej. Dobrze opracowane modele prognoz rozwojowych powinny również uwzględniać potencjalne zagrożenia, które mogą wystąpić w przyszłości, wskazując sposoby obniżenia negatywnych skutków takich zmian. Przykładem może być skokowy wzrost cen ropy na rynkach światowych w wyniku działań krajów arabskich w 1972 roku. Niebezpieczne sytuacje wynikają również w przypadkach, gdy kraje importujące nośniki energii pierwotnej ograniczają się do jednego kierunku nie rozwijając systemów dywersyfikacji. Taka sytuacja jest charakterystyczna dla Polski w zakresie importu gazu naturalnego i ropy. W artykule omówiono wybrane elementy tworzenia wiarygodnych prognoz energetycznych. Przedstawiono historię prognoz energetycznych dla Polski.

6

Światowa energetyka w... 2035, 2040, 2060. Prognozy energetyczne cz. 1

Boryczko B., Kolenda Z., Nowak W.

Energetyka Cieplna i Zawodowa

|

2015

|

Nr 1

76--83

PL

Dynamika rozwoju gospodarczego świata jest tak duża, że zmiany będące wynikiem odkryć naukowych i postępu technologicznego, które obserwujemy, uniemożliwiają określenie celów w dłuższych przedziałach czasu. Z tego względu prognozowanie do roku 2035, 2040, 2060 jest pozbawione podstawowej wartości, jaką stanowi wiarygodność otrzymywanych wyników.

7

Przewidzieć przyszłość… Prognozy energetyczne cz. 2

Boryczko B., Kolenda Z., Nowak W.

Energetyka Cieplna i Zawodowa

|

2015

|

Nr 2

51--54

PL

Polska stoi przed dylematem istotnych zmian wynikających z konieczności zwiększenia bezpieczeństwa energetycznego. Prognoza kontynuacji nie jest dla nas możliwa do przyjęcia. Alternatywą dla kraju jest znacząca zmiana miksu energetycznego, czyli sformułowanie nowego paradygmatu. Opracowany przez rząd projekt Polityki energetycznej Polski do 2050 roku, opublikowany w sierpniu 2014 roku [19], powiela wszystkie błędy poprzednich prognoz i stanowi zbiór ogólnie znanych faktów.

8

Removal of zinc from dusts and sludges from basic oxygen furnaces in the process of ammoniacal leaching

Gargul K., Boryczko B.

Archives of Civil and Mechanical Engineering

|

2015

|

Vol. 15, no. 1

179--187

EN

More than 20 kg of dust and sludge per 1 ton of produced metal are generated in the basic oxygen furnaces used in steel metallurgy. In this type of waste there may be many non-ferrous metals, including also zinc. The content of this metal in dusts ranges from 1 to 6%. After lowering the zinc content to a level of about 1%, such type of waste may become a full-fledged iron-bearing material used in ferrous metallurgy. There is also a possibility to recover and manage the zinc removed from waste materials. Recycling of these materials also reduces the risk to the natural environment, resulting from e.g. the transition of metal compounds contained in stored waste materials into the groundwater and soil. The article presents the results of ammonia leaching of wastes from basic oxygen furnaces where the zinc content is 2.82%. Ammonia leaching allows the turn zinc into the liquid phase with minimal loss of iron in this process. The examinations apply three compounds of ammonia (NH4Cl, (NH4)2CO3 and NH4OH) to analyze the efficiency of the leaching process at different times, temperatures, concentrations of applied compounds and ratios of liquid phase to the solid phase.

9

Analiza kosztów produkcji odkuwek matrycowych

Boryczko B., Grzyb J., Kwaśniewski Ł.

Rudy i Metale Nieżelazne Recykling

|

2014

|

R. 59, nr 3

135--140

PL

Koszty produkcji odkuwek matrycowych stanowią istotny element wyceny wytwarzanego wyrobu. Szczegółowa analiza tych kosztów pozwala na określenie czynników pozwalających na ich obniżkę, a co za tym idzie na zwiększenie zysku ze sprzedaży wyrobu lub na obniżenie ceny zbytu wytworzonego wyrobu, przez co oferta przedsiębiorstwa staje się bardziej atrakcyjna dla potencjalnych odbiorców. W artykule przedstawiono istotę przeprowadzenia rachunku kosztów, opis i podział kosztów ze szczególnym uwzględnieniem kosztów produkcji, analizę procesu produkcji odkuwek matrycowych oraz obliczenia ostatecznych kosztów produkcji odkuwek matrycowych dla przykładowego wybranego rodzaju asortymentu. Wnioski zawarte w artykule pokazują w jaki sposób poprawić efektywność działania przedsiębiorstwa na rynku poprzez obniżenie kosztów w dziale produkcji odkuwek matrycowych.

EN

Forgings production cost is an important part of the valuation of manufactured product. Detailed analysis of these costs allows to determine the factors for their reduction so an increase of profit from the product selling or reduce the manufactured product price is possible, and the company offer becomes more attractive to potential buyers. The paper presents the essence of carrying out cost analysis, description and cost-sharing with particular emphasis on production costs, an analysis of the production process forgings and calculations of the die forgings final production costs for the selected sample product. The conclusions of the article show how to improve the efficiency of the company on the market by reducing costs in forgings manufacturing.

10

Analysis of tube deformation process in a new pilger cold rolling process

Pociecha D., Boryczko B., Osika J., Mroczkowski M.

Archives of Civil and Mechanical Engineering

|

2014

|

Vol. 14, no. 3

376--382

EN

The paper presents the results of an experiment and numerical simulation in a new pilger tube cold-rolling process, in which the rolling stand is stationary and the rolled tube is placed on a slide and between the rollers. The experiment was conducted in a laboratory pilger mill operating according to a new concept of rolling. Numerical simulations were performed with the registration of the entire history of deformation of the rolled tube. Despite a simplification in the mathematical modelling, the obtained results were very similar to the experiment results. Pilger rolling, carried out according to a new concept, can be successfully used for the industrial production of non-ferrous metal pipes. Pipes obtained after the rolling process are suitable for further processing or for direct sale. Particular attention, however, should be paid to ensure sufficient structural rigidity in the mill, as well as to the quality and accuracy of the tools used in the pilger process.

11

Technologie identyfikacji radiowej RFID w przemyśle wydobywczym

Boryczko B., Szarek S.

Rudy i Metale Nieżelazne

|

2013

|

R. 58, nr 4

186-191

PL

RFID — Radio Frequency IDentification — technologia identyfikacji radiowej jest obecnie coraz częściej stosowana w wielu gałęziach gospodarki jako rozwiązanie wspomagające logistykę, zarządzanie zasobami i produkcją. Technologia wykorzystująca fale radiowe do wymiany danych pomiędzy etykietą (identyfikatorem) a czytnikiem znalazła zastosowanie wszędzie tam, gdzie wymagana jest niezawodna, bezstykowa, zdalna identyfikacja osób, zwierząt, maszyn, przedmiotów niezależnie od warunków otoczenia. RFID jest również powszechnie stosowana w przestrzeni publicznej obejmującej paszporty biometryczne, karty transportu publicznego, systemy płatności zbliżeniowej i inne. Szczególnie interesujące wydaje się zastosowanie tej technologii w trudnych warunkach występujących w przemyśle wydobywczym, gdzie obszar jej zastosowania nie został jeszcze do końca zdefiniowany. Unikatowe cechy identyfikacji radiowej i ich wykorzystanie w systemach zarządzających pozwalają między innymi na poprawę bezpieczeństwa w kopalniach i na efektywne zarządzanie sprzętem, maszynami i dystrybucją paliwa. W artykule przestawione zostały podstawy działania RFID oraz wybrane rozwiązania dla przemysłu wydobywczego.

EN

RFID — Radio Frequency IDentification — RFID technology is now increasingly being used in many sectors of the economy as a solution to support logistics and production management. Technology that uses radio waves to exchange data between a label (identifier), and the reader has been used wherever required is a reliable, non-contact, remote identification of persons, animals, machines, objects regardless of ambient conditions. RFID is also widely used in public spaces including biometric passports, public transport cards, contactless payment systems, and more. A particularly interesting to use this technology in the difficult conditions encountered in the mining industry, where the area of its application is not yet fully defined. Unique features of RFID and its use in the management systems allow, inter alia, to improve safety in the mines and on the effective management of equipment, machines and distribution of fuel. This article has been converted basics of RFID and selected solutions for the mining industry.

12

Diagnoza struktury organizacyjnej przedsiębiorstwa z branży metalowej jako narzędzie wspomagające proces zarządzania przedsiębiorstwem i podejmowania decyzji

Boryczko B., Lichota M.

Rudy i Metale Nieżelazne

|

2013

|

R. 58, nr 1

34-40

PL

Struktura organizacyjna jako narzędzie zarządzania. W artykule zdefiniowano strukturę, podano najważniejsze jej funkcje. Zaprezentowano podstawowy rodzaj rozwiązania strukturalnego - strukturę liniową, wymieniono jej wady i zalety. Diagnoza struktury organizacyjnej - cel i zakres badania. W artykule zamieszczono ramowy układ procesu oceny struktury organizacyjnej Zakładu oraz szczegółowe opracowanie diagnozy wg uporządkowanej procedury, zawierającej charakterystykę faz wymienionych w ramowym układzie procesu oceny.

EN

Organizational structure as instrument of management. It define structure in article, it serve most important functions. Basic kind of structural solution present - structure linear, it mention defect and advantages. Diagnosis of organizational structure - purpose and range of research. Frame match of process of estimate of organizational structure the plant place in article and detailed elaboration of diagnosis according to regularized procedure, included in frame match of process of estimate characteristic of phase mentioned inclusive.

13

Czynniki kształtujące ceny wybranych metali nieżelaznych w latach 2008-2012

Boryczko B.

Rudy i Metale Nieżelazne

|

2013

|

R. 58, nr 9

497-508

PL

W artykule przedstawiono ceny wybranych metali nieżelaznych w latach 2008-2012. Zaprezentowano czynniki kształtujące owe ceny w danym okresie. Artykuł zawiera przegląd takich metali jak: aluminium, miedź oraz cynk. Uwzględnia również wielkość produkcji, konsumpcji oraz inne dane statystyczne dotyczące metali nieżelaznych w podanym zakresie czasowym.

EN

This article presents prices of selected non-ferrous metals in 2008-2012. Presented factors shaping these prices in a given period of time. The article contains an overview of metals such as aluminum, copper, zinc. Included the volume of production, consumption and other statistical data on the non-ferrous metals in the given time range.

14

Wykorzystanie modelowania fizycznego i matematycznego do określenia odkształceń w nowym procesie walcowania pielgrzymowego rur na zimno

Pociecha D., Mroczkowski M., Osika J., Boryczko B.

Prace Naukowe Politechniki Warszawskiej. Mechanika

|

2013

|

z. 253

141--146

PL

W pracy przedstawiono wyniki modelowania fizycznego i matematycznego umożliwiające określenie odkształceń w nowym procesie walcowania pielgrzymowego rur na zimno. Modelowanie fizyczne przeprowadzono na prototypowej walcarce pielgrzymowej pracującej według koncepcji prof. nadzw. dra hab. inż. Jana Osiki. Materiałem badawczym były rury aluminiowe ze znacznikami pomiarowymi. Do określenia odkształceń wykorzystano system wizyjny, który umożliwia pomiar odkształceń z uwzględnieniem zmian grubości ścianki badanej rury. System umożliwia śledzenie odkształceń w jednym pełnym cyklu roboczym. Modelowania matematycznego dokonano przy użyciu programu Abaqus. W symulacjach procesu walcowania pielgrzymowego uwzględniona została pełna historia odkształcenia walcowanej rury umożliwiająca określenie odkształcenia materiału w całej kotlinie walcowniczej.

EN

The paper presents results of physical modelling and numerical simulation, which allows to determinate strain fields in the cold pilger rolling process. Physical modelling was carried out on prototype pilger mill, which work according to the conception of Professor Jan Osika. Aluminium tubes with copper wire inserts as markers have been investigated. To measure strain fields optical system, which take into account variation of tube thickness, was used. Strains were analysed during one full cycle of pilgering process. Abaqus software was used for numerical simulation. Taking into account history of deformation in the working zone, the strain fields have been calculated.

15

Prototypowy system pomiaru odkształceń w procesie walcowania pielgrzymowego rur na zimno

Pociecha D., Osika J., Mroczkowski M., Boryczko B.

Prace Naukowe Politechniki Warszawskiej. Mechanika

|

2013

|

z. 253

25--30

PL

Pomiary odkształceń w procesach przeróbki plastycznej mogą zostać wykonane na wiele sposobów. W ostatnich latach, ze względu na dużą dokładność oraz szybkość, bardzo popularne stały się optyczne systemy pomiarowe. Niestety, w większości wypadków, za pomocą tego typu systemów można realizować jedynie pomiar odkształceń na powierzchni zewnętrznej jak np. w przypadku pomiarów odkształceń tłoczonych blach. W niniejszym artykule zaprezentowano prototypowy system, umożliwiający pomiar odkształceń w procesach przeróbki plastycznej z uwzględnieniem trzech wymiarów, oraz zmian grubości badanego elementu. System jest w znacznym stopniu zautomatyzowany poprzez zastosowanie dedykowanego oprogramowania, będącego integralną częścią systemu. Pomiary testowe wykonane zostały na przykładzie wyrobów uzyskanych w procesie walcowania pielgrzymowego, jednak system może zostać przystosowany do pomiarów w innych procesach przeróbki plastycznej metali.

EN

Strain measurement in cold plastic working processes can be performed in many ways. In recent years, due to the high accuracy and sped, optical measuring systems have become very popular. Unfortunately, in most cases, such systems can be used only to measure strain on the element outer surface, in example metal sheet pressing process. This paper present a prototype system which allow to measure deformation in cold plastic working processes, taking into account the three dimensions, and variation o the element thickness. Most of tasks are fully automated, due to using dedicated software which is integral part of this system. Test measurements were made on the sample tubes from pilger rolling process, however system can be adapted to measure deformation in any cold working process.

16

Zastosowanie roztworów KOH do ługowania szlamów i pyłów stalowniczych

Gargul K., Palimąka P., Boryczko B.

Hutnik, Wiadomości Hutnicze

|

2013

|

Vol. 80, nr 11

735--738

PL

W pracy przedstawiono wyniki badań ługowania szlamów i pyłów stalowniczych o niskiej zawartości cynku. Czynnikiem ługującym był roztwór KOH, próby przeprowadzono dla różnych wariantów zmiennych parametrów (czas, temperatura, stężenie KOH, stosunek faza ciekła/faza stała). Przeprowadzone badania wskazują na możliwość obniżenia zawartości Zn w ługowanym materiale do poziomu około 1% i zastosowania go jako komponentu wsadu do produkcji żelaza i stali. Elektroliza roztworu po ługowaniu prowadzi do odzysku cynku i regeneracji roztworu ługującego.

EN

This paper presents the results of leaching steelmaking sludge and dust with a low zinc content. Leachant was KOH solution, tests were performed for various combinations of variables (time, temperature, KOH concentration, the ratio of the liquid phase/solid phase). Research has indicated the possibility of reducing the content of Zn in leaching material to approximately 1% and use it as a feed component for the production of iron and steel. Electrolysis of the leach solution leads to zinc recovery and regeneration of the leaching solution.

17

Klastry jako narzędzie stymulujące rozwój przemysłu metali nieżelaznych

Boryczko B., Gargul K., Palczewski M.

Rudy i Metale Nieżelazne

|

2012

|

R. 57, nr 12

851-856

PL

Klastry są nowoczesną formą wspierającą prowadzenie przedsiębiorstwa, powodującą wzrost jego konkurencyjności, przy zmniejszeniu kosztów prowadzenia działalności firmy. W artykule zdefiniowano i scharakteryzowano klastry. Dokonano analizy klastrów pod względem struktury, powstania oraz działania. Podano przykłady istniejących klastrów w Polsce i Europie, zanalizowano szanse rozwoju inicjatyw klastrowych oraz uwarunkowania niezbędne do ich powstania. Przedstawiono możliwości pozyskania środków finansowych, dokonano analizy SWOT (Strengths, Weaknesses, Opportunities, Threats) powstania klastra branży metali nieżelaznych. Wskazano działania w obszarze powstania klastra jako element rozwoju polskiej innowacyjności i przedsiębiorczości.

EN

Clusters as a modern form of corporate management support, increasing its competitiveness and reducing the costs of doing business. Cluster definition and features. Cluster analysis in terms of structure, formation, action. Examples of clusters existing in Poland and Europe, the chances of development of cluster initiatives, conditions necessary for their creation. Possibilities of obtaining financial resources, the creation of a SWOT analysis of non-ferrous metals industry cluster. Activities in the area as part of the creation of a cluster development of Polish innovation and entrepreneurship.

18

Wspomaganie projektowania produkcji i optymalizacja procesu wytwarzania rur

Boryczko B., Osika J., Rabczuk M.

Rudy i Metale Nieżelazne

|

2010

|

R. 55, nr 11

789-795

PL

W niniejszym artykule przedstawiono system wspomagania projektowania wyboru wariantów technologicznych, racjonalnego wykorzystania urządzeń i realizacji zamówień w procesie wytwarzania rur miedzianych. System ten oparty został na modelu matematycznym planowania produkcji rur, opisującym funkcję celu i ograniczenia. Zadanie optymalizacji jednokryterialnej przyjmujące jako kryterium maksimum zysku pozwala na realizację zamówień przy wyborze racjonalnych wariantów technologicznych i wykorzystaniu urządzeń. Przedstawiono przykładowe rozwiązanie metodą Simplex. Po analizie wyników opisano koncepcję dalszego rozwiązania postawionego problemu metodą optymalizacji wielokryterialnej.

EN

The paper presents technological variants projecting assistance system, the rational using of the devices and the process of the copper-tubes production order realization. This system is based on the tube production mathematical model which describes the objective function and limitations. Problem of optimization witch take maximum gain as a criterion, allows completing an order when technological rational variants and devices utilization were taken into account. Example of method Simplex solution was presented. After results analysis, the conception of future solution method - using multicriteria optimization - was presented.

19

Analiza stanu naprężenia i odkształcenia w procesie wyciskania rur o przekroju kwadratowym ze stopów aluminium

Rękas A., Libura W., Galanty M., Zasadziński J., Boryczko B.

Rudy i Metale Nieżelazne

|

2010

|

R. 55, nr 11

767-769

PL

Analizę stanu naprężenia, odkształcenia i temperatury przeprowadzono w oparciu o metodę elementów skończonych (MES) wykorzystując program DEFORM 3D. Rozważaniami objęto wyciskanie współbieżne na gorąco wlewka o różnej temperaturze początkowej ze stopu w gatunku 2024 z zastosowaniem matryc mostkowych. Przeprowadzone obliczenia pozwoliły na ustalenie poziomu naprężeń i ich rozkładu w komorze zgrzewania podczas wyciskania stopu w gatunku 2024 przez matryce mostkowe.

EN

The analysis was performed by the use of the computer program DEFORM based on a finite element method. The direct hot extrusion of 2024 aluminum alloy was investigated with the use of the porthole dies of different geometry. The calculations allowed determining both pressure and temperature levels and their distributions within the welding chamber leading to the best welding conditions for the alloy tested. Particularly valuable information, that can be used in design of bridge dies for extrusion of such alloys is that the welding stress depends on the height of the welding chamber.

20

Thermo -Ecological Cost analysis of shaft and flash smelting processes of copper production - general approach

Norwisz J., Boryczko B., Hołda A., Kolenda Z.

Archives of Metallurgy and Materials

|

2009

|

Vol. 54, iss. 1

153-159

EN

Thermo-ecological cost method, formulated by Szargut, has been proposed to be applied for comparison of two different and most frequently used technologies of copper production. The method, based on minimization of depletion of nonrenewable natural resources takes also under consideration the problem of the deleterious ecological impact of highly aggressive waste products. The further is especially important as the copper technologies belong to the group of highly hazardous from ecological point of view, nonferrous metals industry. Two technologies – shaft furnace and flash smelting Outokumpu technologies have been analyzed considering all step from copper mine to final product (copper cathodes). The method of calculation is based on the set of balance equations determining the value of specific thermo-ecological cost. To recommend copper technology a minimum value of the thermo-ecological cost is proposed to be criterion.

PL

W artykule przedstawiono wyniki analizy porównawczej dwóch pełnych technologii otrzymywania miedzi katodowej, opartej na pojęciu kosztu termoekologicznego. Rozważania dotyczą procesów szybowego i zawiesinowego. W proponowanej metodzie podstawe stanowią skumulowane zużycia energii prowadzące do minimalizacji wyczerpywania nieodnawialnych zasobów bogactw naturalnych z uwzględnieniem szkodliwego wpływu emisji szkodliwych produktów do otoczenia. Analiza obejmuje rudy miedzi w kopalni do wyprodukowania miedzi katodowej. Obliczenia przeprowadzone przez rozwiązanie układów równań bilansowych strumieni egzergii typu input – output. Wykorzystano wyniki bezpośrednich pomiarów w hutach miedzi po uzgodnieniu bilansów substancji i energii. Zaproponowano kryterium wyboru technologii o najmniejszej wartości kosztu termoekologicznego przez co uwzgledniono problemy degradacji energii wynikajace z II zasady termodynamiki.