Direction of the rolling of plates made of steel grade 0H18N9 versus welding distortions

Grzesiak Damian

Biuletyn Instytutu Spawalnictwa w Gliwicach

2020

Vol. 64, No. 6

51--56

The article presents the results of tests concerning the effect of the direction of the rolling of plates made in steel 0H18N9 on welding distortions. The research-related analysis was concerned with the rolling direction in relation to the longer edge of specimens. The specimens were welded using the MAG method involving the use of pulsed arc. The acquisition of surface flatness-related data was performed using a GOM ATOS 5M blue light scanner. The analysis of the results revealed that the mean surface flatness of the specimens was similar in relation to all of the rolling directions related to analysis. However, the direction of distortions parallel and perpendicular to the weld varied depending on the direction of rolling.

Przedstawiono badanie wpływu kierunku walcowania blachy gatunku 0H18N9 na odkształcenia spawalnicze. Analizie poddano orientacje kierunku walcowania względem dłuższego brzegu próbki. Próbki spawano metodą MAG łukiem pulsującym. Akwizycji danych płaskości powierzchni dokonano za pomocą skanera światła niebieskiego GOM ATOS 5M. Na podstawie przeprowadzonej analizy stwierdzono, że średnia płaskość powierzchni próbek dla wszystkich analizowanych kierunków walcowania była zbliżona, natomiast kierunek odkształceń w kierunku równoległym i prostopadłym do spoiny różnił się w zależności od kierunku walcowania.

Verification of normal distribution of welding distortions

Grzesiak Damian, Plichta Jarosław

Welding Technology Review

2019

R. 91, nr 3

6--9

The aim of this paper is to answer the question of the distribution of welding distortions. The MIG method was used to make 31 butt welds of 0H18N9 sheet metal, of 6 mm thickness and dimensions 150x350 mm. All joints are made with constant parameters of the welding process. Statistical analysis of the distribution and Kolomogorov-Smirnov test were used in this paper. On the grounds of the analysis it was proved that the distribution of welding deformations is a normal distribution. This justifies the use of experiment planning methods and the use of average values. The relatively high value of the standard deviation makes it necessary to take into account the geometrical parameters of the joint.

Niniejsza praca ma na celu odpowiedź na pytanie, jakim rozkładem opisane są odkształcenia spawalnicze. Metodą MIG wykonano 31 złączy doczołowych z blachy 0H18N9 o grubości 6 mm i wymiarach 150x350 mm. Wszystkie złącza wykonano przy stałych parametrach procesu spawania. W pracy wykorzystano analizę statystyczną rozkładu oraz test Kolomogorowa-Smirnowa. Na podstawie analizy udowodniono, że rozkład odkształceń spawalniczych jest rozkładem normalnym. Uzasadnia to stosowanie metod planowania eksperymentu oraz posługiwania się wartościami średnimi. Stosunkowo duża wartość odchylenia standardowego, stwarza konieczność uwzględnienia parametrów geometrycznych złącza.