Micromechanical modelling of diamond debonding in composite segments

Ucun I., Aslantas K., Buyuksagis I. S., Tasgetiren S.

Journal of Theoretical and Applied Mechanics

2012

Vol. 50 nr 2

609-626

Diamond debonding in composite segments used in cutting of natural stones was investigated in this study. The finite element method was used for numerical solutions, and the problem was modelled as two dimensional. The problem was investigated under linear elastic fracture conditions. Stress intensity factors and strain energy release rates were obtained. Numerical solutions were performed for different diamond sizes and diamond heights. According to the obtained results, the most effective factor for growth of the interface crack was considered to be the tangential force acting on the diamond.

W pracy omówiono problem odpadania kryształów diamentu od kompozytowej matrycy narzędzi do cięcia naturalnych kamieni. Zagadnienie sformułowano dwuwymiarowo, a do uzyskania wyników symulacji numerycznych wykorzystano metodę elementów skończonych. Zjawisko badano dla warunków liniowego sprężystego pękania. Obliczono współczynniki koncentracji naprężeń oraz tempo uwalniania energii sprężystości. Symulacje przeprowadzono dla różnych wymiarów kryształów diamentu. Zgodnie z otrzymanymi rezultatami, stwierdzono, że głównym czynnikiem odpowiedzialnym za wzrost powierzchni pękania jest styczna składowa siły działającej na diament.

Crack initiation and growth in circular saw made of tool steel

Ucun I., Colakoglu M., Tasgetiren S.

Journal of Theoretical and Applied Mechanics

2008

Vol. 46 nr 2

291-303

Fatigue of a circular saw made of tool steel and used in metal industry to cut, in particular, metal bars and pipes is investigated in this study. Due to having a small tooth root radius, the circular saw is much more likely to get crack damage at the tooth root region. Radial and tangential forces are also effective at this region for fatigue crack initiation. In high cutting speeds and feed rates of the circular saw, higher stress concentration occurs particularly at that region. To examine the fatigue and failure in the circular saw, specimens used in an experiment are prepared from a damaged circular saw are subjected to different mechanical tests. In the theoretical study, stress and fracture behaviour of the saw is determined by the finite element method. Results and causes of the failure are assessed and compared.

Przedmiotem badań jest wytrzymałość zmęczeniowa piły tarczowej wykonanej ze stali narzędziowej i przeznaczonej do pracy w przemyśle metalurgicznym, w szczególności do cięcia prętów i rur. Z powodu niewielkiego promienia zaokrąglenia podstawy zęba tarczy, piły narażone są na pęknięcia właśnie w tym obszarze. Na rozwój procesu pękania mają wpływ obciążenia promieniowe i styczne zęba. Tu występuje największa koncentracja naprężeń przy znacznych prędkościach obrotowych tarczy i dużego tempa posuwu. Do przeanalizowania procesu zmęczenia piły użyto próbek wypreparowanych ze zniszczonego narzędzia i poddano je licznym testom mechanicznym. Równolegle przeprowadzono symulacje teoretyczne za pomocą Metody Elementów Skończonych. Przyczyny i wyniki ilościowe dotyczące zniszczenia zmęczeniowego wyznaczono na podstawie obydwu metod badawczych i następnie je porównano.