When simulating the operating conditions of the rim of a railway wheel, an analysis of change in the structural state from the possible degree of plastic deformation and the heating temperature of steel near the rolling surface was carried out. The development processes of spheroidization and coalescence of cementite during heating of the cold-worked steel change its ability to strain hardening. Substructure changes during heating to temperatures of 500-550°C deformed steel are accompanied by a simultaneous decrease in its ability to strain hardening and the level of plasticity. When heated above 500-550°C, the development of ferrite recrystallization processes provides a gradual transition of the metal from substructure hardening to hardening from grain boundaries with large angles of disorientation. It is shown that regardless of the nature of the main structural element, the ability of steel to strain hardening and the level of plasticity after heating are related by a proportional relationship.
In comparison with low carbon steels, there is increased interest in the use of aluminium-based alloys as materials for the manufacture of welded structures rolling stock of railway transport. During friction stir welding aluminium-based alloy, against the background of the analysis structural transformations, issues of development hardening processes are considered. Under conditions of existence, a temperature gradient at zone of weld formation, shown degree approximation alloy to the conditions of superplastic flow and influence from presence particles of the second phase on grain size of matrix is estimated. Evaluation of the separate influence grain size of matrix and state of solid solution at total hardness of the weld showed dependence of their contributions on temperature of hot plastic deformation. As the temperature of plastic deformation of alloy at area of the weld increases, contribution to the total hardness from grain size increase and on state of the solid solution decreases.
During a study of the combustion process of a direct polarity electric arc, a directly proportional dependence of the electric current value on the degree of cold plastic deformation of carbon steel used as an electrode was found. To calculate the value of the electric current during arc burning, in the indicated ratio, it was proposed to replace the surface tension force of the liquid metal with the surface tension of ferrite of plastically deformed carbon steel. Calculation of the ferrite’s surface tension value on the deformation degree of the steel under study through the size of the coherent scattering regions was used to explain the observed dependence of the electric current during arc burning. From the analysis of the considered correlation ratios, it was found that with an increase in the cold deformation degree, the refinement of the coherent scattering regions results in the ferrite’s surface tension increase and consequently, to an increase in the electric current during arc burning. Comparative analysis of the obtained results of calculating the value of electric current during arc burning through the surface tension of ferrite of cold-deformed carbon steel showed a fairly good coincidence with experimental data. The differences did not exceed 9%.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.