1

Investigation of the Electromagnetic Shielding Effectiveness of Needle Punched Nonwoven Fabrics Produced from Stainless Steel and Carbon Fibres

Ozen M. S., Usta I., Yuksek M., Sancak E., Soin N.

Fibres & Textiles in Eastern Europe

|

2018

|

Vol. 26, no. 1 (127)

94--100

EN

The electromagnetic shielding effectiveness (EMSE) of needle punched, nonwoven fabrics produced using staple stainless steel and carbon fibres was investigated. Utilising carding and large scale industrial type needle punching machines, webs of staple stainless steel and carbon fibres were produced, which were subsequently bonded on the needle punching machine at approximately 132 punches/cm2 and 13.5 mm needle penetration depth. The effect of varying the carbon fibre content was studied by varying the blend ratio of stainless steel and carbon fibres between 5-20%. EMSE measurements of as-produced needle punched nonwoven fabrics were carried out using the coaxial transmission line method (ASTM D4935-10) in the frequency range of 15-3000 MHz. Within the range, the EMSE values were enhanced from 22.3 dB (95/5, stainless steel/carbon) to 44.7 dB (80/20, stainless steel/carbon), which was attributed to the enhanced conductivity of the fabrics. In fact, the surface resistivity of the samples decreased from 5.80E + 3 Ω to 2.43E + 2 Ω, enhanced for 95:5 and 80:20 stainless steel/carbon blends.

PL

Zbadano efektywność ekranowania elektromagnetycznego (EMSE) igłowanych włóknin wykonanych z wykorzystaniem stali nierdzewnej i włókien węglowych. Wytworzono włókniny ze stali nierdzewnej i włókien węglowych, które spajano na maszynie do igłowania przy około 132 uderzeniach / cm2 i głębokości penetracji 13,5 mm. Zbadano wpływ zmiany zawartości włókien węglowych poprzez zmianę stosunku mieszanki stali nierdzewnej i włókien węglowych w zakresie 5-20%. Pomiary EMSE wytwarzanych w ten sposób igłowanych włóknin wykonano metodą współosiowej linii transmisyjnej (ASTM D4935-10) w zakresie częstotliwości 15-3000 MHz. Stwierdzono, że wartości EMSE zostały zwiększone z 22,3 dB (95/5, stal nierdzewna / węgiel) do 44,7 dB (80/20, stal nierdzewna / węgiel), co zostało przypisane zwiększonej przewodności wyrobów.

2

Investigation of the Electrical Properties and Electromagnetic Shielding Effectiveness of Polypyrrole Coated Cotton Yarns

Yildiz Z., Usta I., Gungor A.

Fibres & Textiles in Eastern Europe

|

2013

|

Vol. 21, no. 2 (98)

32--37

EN

Polypyrrole (PPy) coated cotton yarns were prepared by the vapour phase polymerisation technique at various initiator concentrations. Iron (III) chloride (FeCl3) was used as the initiator at four different concentrations (0.2, 0.4, 0.6 & 0.8 mol/l) respectively. In this work, the effects of initiator concentration on the tensile, electrical and morphological properties of the cotton yarns were investigated. PPy coated cotton yarns were woven on a handloom for the investigation of electromagnetic shielding effectiveness. The fabric samples prepared were evaluated in terms of shielding behavior. Scanning electron microscopy (SEM) analysis showed that the yarn treated with 0.4 mol/l initiator concentration gave the most uniform PPy layer and highest shielding value. The existence of PPy was proved by using Fourier transform infrared spectroscopy (FTIR) analysis.

PL

Bawełniane przędze pokryte polipyrolem (PPy) wytworzono techniką polimeryzacji w fazie gazowej w różnych stężeniach inicjatora. Jako inicjator zastosowano FeCl3 o czterech różnych stężeniach (0,2; 0,4; 0,6 i 0,8 mol/l). Zbadano wpływ stężenia inicjatora na rozciąganie, oraz elektryczne i morfologiczne właściwości przędz bawełnianych. W celu zbadania efektywności ekranowania pola elektromagnetycznego przędze bawełniane powlekane PPy były tkane ręcznie na krośnie. Przygotowane próbki tkanin oceniano pod względem właściwości ekranujących. Analiza SEM wykazała, że z przędzy z dodatkiem inicjatora o stężeniu 0,4 mol/l uzyskano najbardziej jednolitą warstwę PPy i najwyższą wartość ekranowania. Obecność PPy potwierdzono za pomocą spektroskopii w podczerwieni z transformacją Fouriera (FTIR).

3

Mechanical behaviour of chicken quills and chicken feather fibres reinforced polymeric composites

Uzun M., Sancak E., Patel I., Usta I., Akalin M., Yuksek M.

Archives of Materials Science and Engineering

|

2011

|

Vol. 52, nr 2

82-86

EN

Purpose: The objective of this study is to utilise and evaluate the mechanical properties of the chicken feather quill and fibre reinforced vinylester and polyester composites. Design/methodology/approach: Prior to production of the composites, the chicken feather fibres (CFF) were cleaned, tested and analyzed in terms of physical properties; linear density and tensile behaviour. The unidirectional CFF reinforced composites were produced with vinylester and polyester resins with three fibre reinforcement loadings (2.5, 6, 10wt%). Following experiments were conducted to determine physical properties of the control (0%) and CFF reinforced composites; tensile, flexural and Charpy impact testing. Findings: It was found that the impact properties of the CFF reinforced composites are significantly better than the control composites however both the tensile and the flexural properties of the CFF reinforced composites have poorer values compared to the control composites. For the 10% CFF reinforced vinylester composite, Charpy impact value was 4.42 kgj/mm2 which was 25% higher than the control vinylester composites (3.31 kgj/mm2) and also for the 10% CFF reinforced polyester (4.56 kgj/mm2) composite had three times better impact resistance than the control composite (1.85 kgj/mm2). Practical implications: The CFF reinforced composite have potential applications due to its improved impact behaviour. Originality/value: If the poultry waste can be utilised and used any engineering applications they will be preferred due to low-cost and superior characteristics and the most importantly they will not cause ecological and health problems.

4

Effect of Balloon Angle on the Hairiness and other Yarn Properties of Polyester Ring Spun Yarn

Usta I.

Fibres & Textiles in Eastern Europe

|

2008

|

Vol. 16, no. 5 (70)

40--47

EN

In this research the effects of the yarn balloon angle on yarn hairiness and other yarn properties was investigated. The yarn balloon was changed by use of fivedifferentweightsof C type travellers. The yarn counts chosen were 15 tex, 20 tex and 30 tex. Three spindle speeds were used: 9,000 r.p.m., 10,000 r.p.m. and 11,000 r.p.m. Yarn hairiness, yarn count, balloon angle, yarn surface helix angle, yarn twist, strength and elongation at break, as well as irregularity and imperfection tests were carried out for all the yarn samples. In this research it was noted that as the balloon angle increases, the yarn hairiness and yarn surface helix angle increase. Other yarn properties were also investigated and discussed.

PL

W artykule przedstawiono badania wpływu kąta balonu na włochatość i inne właściwości przędz otrzymywanych z przędzarki obrączkowej. Kąt balonu był zmieniany poprzez zastosowanie pięciu biegaczy typu C o różnej masie. Badano przędzę o masie liniowej 15, 20 i 30 tex. Stosowano trzy prędkości wrzecion: 9000, 1000 i 11000 obr/min. Badano następujące właściwości przędz otrzymanych przy danym kącie balonu; włochatość, masa liniowa, skręt, kąt ułożenia włókien, wytrzymałość właściwą, wydłużenie przy zerwaniu, nieregularność i ilość błędów. Na podstawie badań stwierdzono między innymi, że jeżeli kąt balonu wzrasta również włochatość i kąt ułożenia włókien. Wszystkie otrzymane zależności zbadano statystycznie i poddano dyskusji.

5

Influence of Ring Traveller Weight and Coating on Hairiness of Acrylic Yarns

Usta I., Canoğlu S.

Fibres & Textiles in Eastern Europe

|

2002

|

Vol. 8, no. 4 (39)

20--24

EN

This study involves the results of an investigation concerning the influence of ring travellers of different weights, types and coatings on the hairiness of acrylic yarns spun from microfibres. 30 tex yarn was produced using C-type travellers with a twist factor of αtex=31.6. Travellers of 8 different weights and 4 different coatings were used working with two spindle speeds of 7000 rpm and 10,000 rpm. Yarn hairiness was evaluated with the use of a Shirley Yarn Hairiness Tester. The values of tension, breakage rate, count, twist, evenness, elongation and tensile strength of the yarn produced were measured. In addition the yarns were knitted into fabrics to observe and evaluate pilling. Some conclusions were drawn considering yarn hairiness.

PL

Omówiono wyniki badań, dotyczących wpływu kilku typów biegaczy o różnej masie i pokryciu, na włochatość przędz akrylowych przędzionych z mikrowłókien. Produkowano, używając biegaczy typu C, włókno o masie liniowej 30 tex i współczynniku skrętu 31.6. Stosowano 8 typów biegaczy o różnych masach i 4 różnych pokryciach. Przędziono przy prędkości wrzecion 7.000 obr/min i 10.000 obr/min. Włochatość przędzy określano za pomocą przeznaczonego do tego celu aparatu firmy Shirley. Mierzono również wartości naprężeń, ilość zrywów, masę liniową, gładkość, wydłużenie i siłę zrywającą przędzę. Dodatkowo przędze przerabiano na dzianiny i oceniano na nich pilling. Wyciągnięto wnioski dotyczące powstawania włochatości.