Influence of microstructure and Laser Shock Processing (LSP) on the corrosion behaviour of AA2050-T8

Vignal V., Amar H., Krawiec H., Peyre P., Dick L. F.

Ochrona przed Korozją

2010

nr 11

524-527

The corrosion behaviour of AA2050-T8 was studied after polishing and after LSP treatment using microcapillaries and the SVET. After polishing, both pitting at constituent particles and intergranular corrosion were observed. By contrast, no intergranular corrosion / pits developed in the matrix after LSP. In addition, there is an anodic shift of the pitting potential of sites containing particles. Beneficial influence of LSP on corrosion behaviour of AA2050-T8 was also demonstrated using the SVET. The local current was systemically lower after LSP treatment.

Korozyjne zachowanie się stopu aluminium AA2050-T8 było badane po mechanicznym polerowaniu i po obróbce laserowej, za pomocą Techniki Skaningowej Elektrody Wibrującej (SVET) i mikro-kapilar. Na próbkach polerowanych zaobserwowano korozję wżerową i międzykrystaliczną w 0,1M NaCl. Z kolei osnowa próbek poddanych obróbce laserowej była odporna na korozję międzykrystaliczną i wżerową. Dla miejsc zawierających wydzielenia obserwowano przesunięcie potencjału przebicia w kierunku anodowym. Korzystny wpływ obróbki laserowej na odporność korozyjną stopu aluminium AA2050-T8 wykazały badania za pomocą SVET. Dla próbek po laserowej obróbce zawsze rejestrowano niższy prąd niż dla próbek polerowanych.

Effect of laser shock processing (LSP) on the corrosion resistance of aluminum alloy 2050-T8

Amar H., Vignal V., Krawiec H., Popa I., Peyre P.

Ochrona przed Korozją

2009

nr 11

447-450

Aluminium alloys are very important category of materials due to their high mechanical properties and wide range of industrial applications. It is well known that aluminum alloys are prone to microstructural corrosion (pitting corrosion, intergranular corrosion, etc.). Laser shock processing (LSP) is a serious candidate versus conventional surface treatments to preserve their integrity and to protect them from pitting corrosion damages. In the present paper, the influence of LSP on the resistance to localized corrosion of AA2050-T8 is investigated in chloride media. After polishing, sites containing precipitates show lower pitting potentials (around 0 mV vs Ag/AgCl) than the pure matrix (of about 300 mV). Surface observations indicate that pits initiated at Al-Cu-Fe-Mn precipitates. Oxides were not dissolved and no pits were found around them. After LSP, AFM and FE-SEM/EDS observations revealed that some precipitates were debonded from the matrix, resulting in the formation of cavities at the specimen surface. The anodic current measured in sites containing the matrix or cavities was lower than after polishing (0.01 mA/ cm2 instead of 0.1 mA/cm2). A passive domain was found and the current increases from 0 mV. However, no pitting potential could be determined. This indicates that LSP increases the corrosion resistance of such sites. Pitting was detected in a few sites at potential values close to the pitting potentials found on the polished specimens (of about -250 mV).

Stopy aluminium ze względu na swoje bardzo dobre właściwości mechaniczne są ważną grupą materiałów znajdujących zastosowanie w przemyśle. Wiadomo, że stopy aluminium są podatne na korozję mikrostrukturalną (korozja wżerowa, korozja międzykrystaliczna itp.). Obróbka laserowa jest jedną z technik obróbki powierzchni podnoszącą odporność stopu na korozję wżerową. W artykule przedstawiono wpływ obróbki laserowej przeprowadzonej na stopie AA2050-T8 na jego odporność korozyjną w roztworze zawierającym jony chlorkowe. W przypadku stopu po mechanicznym polerowaniu, miejsca zawierające wydzielenia wykazywały niższy potencjał przebicia (około 0 mV) niż osnowa (około 300 mV). Obserwacje powierzchni stopu wykazały, że wżery powstają przy wydzieleniach typu Al-Cu-Fe-Mn. Z kolei tlenki nie uległy roztwarzaniu i nie zaobserwowano wokół nich wżerów. Laserowa obróbka stopu aluminium spowodowała usunięcie wydzieleń z osnowy, co spowodowało pojawienie się wnęk. Prąd anodowy zarejestrowany w miejscach zawierających wnęki był jednak niższy niż prąd mierzony dla osnowy po mechanicznym polerowaniu (0,01 mA/cm2 zamiast 0,1 mA/cm2). Ponadto na próbkach poddanych obróbce laserowej zaobserwowano szeroki obszar pasywny i tylko w niektórych miejscach zarejestrowano potencjał przebicia. Wyniki te wskazują, że laserowa obróbka podnosi odporność na korozję lokalną stopu AA2050-T8 w roztworze jonów chlorkowych.