Assessment of pearlite degradation in power industry cast steel after long-term exploitation

Kasińska J., Matusiewicz P., Czarski A., Barwicki L.

Inżynieria Materiałowa

|

2017

|

Vol. 38, nr 5

212--216

EN

The paper presents the results of pearlite degradation analysis. The degradation level was evaluated on three specimens (cuttings) of low alloyed 20HM cast steel, sampled from various locations on the main body of the WP turbine exposed to creep (steam temperature 480°C, pressure 12.7 MPa). The mechanical properties (hardness, impact toughness) were performed. Microscopic observations were performed on nital-etched sections in the scanning electron microscope JSM 7100F. Microstructure analysis involved the characterization of microstructure morphology and quantitative metallography for describing pearlite degradation after a long-term exposure to creep. The measurements were performed using MetIlo image analysis program. There were measured the volume fraction of the regions with lamellar morphology, VV L and the pearlite degradation ratio, Lratio. In addition the microstructure class were determined on the basis of a qualitative assessment of changes in the morphology of pearlite regions.

PL

W wielu krajowych elektrowniach na elementy części ciśnieniowych kotłów, jak np. rury przegrzewaczy, są stosowane głównie normalizowane stale ferrytyczno-perlityczne. Po ich długotrwałej pracy zachodzi potrzeba oceny możliwości dalszej ich eksploatacji w warunkach pracy kotła lub turbiny. W stalach i staliwach o wyjściowej (przedeksploatacyjnej) mikrostrukturze ferrytyczno-perlitycznej już po krótkich czasach eksploatacji w warunkach pełzania obserwuje się początkowe etapy pękania i fragmentacji płytek cementytu w perlicie. Kolejne etapy degradacji struktury to koagulacja wydzieleń, w tym cementytu w perlicie, wzrost wielkości niektórych rodzajów węglików, aż do utworzenia mikrostruktury ferrytycznej z bardzo zróżnicowaną morfologicznie fazą węglikową. Zastosowanie metod metalografii ilościowej do opisu mikrostruktury niewątpliwie rozszerza możliwości interpretacyjne obrazów mikrostruktury i ułatwia przeprowadzenie oceny stopnia ich degradacji zachodzącej w warunkach długotrwałej eksploatacji i pełzania. Obecnie nie istnieje znormalizowana/obliczeniowa ocena degradacji stali ferrytyczno-perlitycznych, a jedynie dokonuje się jej przez ocenę jakościową. Dlatego celem badań było wykorzystanie oraz ocena możliwości narzędzi metalograficznych do określenia stopnia degradacji perlitu w staliwie 25CrMo4 po długotrwałej eksploatacji.

2

Zmęczenie korozyjne przyczyną awarii rurociągów energetycznych

Gajewski M., Furmańczyk P., Barwicki L.

Energetyka

|

2014

|

nr 11

652--655

PL

W pracy przedstawiono mechanizm anodowego rozpuszczania żelaza i powstawania pęknięć powodowanych zmęczeniem korozyjnym. Omówiono dwa charakterystyczne przypadki zmęczenia korozyjnego rurociągu pary wtórnej ze stali 10H2M oraz króćca rury międzywalczakowej kotła ze stali K18. Przeprowadzone badania potwierdziły istotną rolę ogniwa galwanicznego w procesie pękania.

EN

The paper presents the mechanism of anodic dissolution of iron and the formation of cracks caused by corrosion fatigue. Discusses two typical cases of corrosion fatigue secondary steam pipe made of 10H2M steel and pipe nipple of boiler made of K18 type steel. The study confirmed the important role of galvanic cell in the process of cracking.

3

Doświadczenia ze spawania grubościennych rurociągów ze stali P92

Gajewski M., Barwicki L.

Energetyka

|

2012

|

nr 11

671-674

PL

Przedstawiono charakterystykę stali P92. Wykazano zależność twardości i udarności od temperatury odpuszczania dla złączy spawanych ze stali X20CrMoV12-1 i P92. Badano doczołowe złącza spawane rur o średnicy 508 x 34 mm ze stali P92. Omówiono przyczyny uzyskiwania niskich udarności spoin. Określono morfologię wtrąceń niemetalicznych w spoinach i ich oddziaływanie na proces pękania.

EN

This paper presents the characteristics of P92 steel. Demonstrated the dependence of hardness and toughness of the steel tempering temperature of X20CrMoV 12-1 and P92. Butt joints of pipes with a diameter of 508 x 34 mm of steel P92 were studied. The paper presents the reasons for obtaining low toughness welds. Morphology of non-metallic inclusions in joints and their influence on the process of cracking were specilied.

4

Degradacja struktury i uszkodzenia rur kotłowych ze stali 13CrMo4-5 (15HM)

Gajewski M., Kasińska J., Barwicki L.

Energetyka

|

2011

|

nr 11

680-683

PL

Przedstawiono wyniki badań rur łączących komory środkowe przegrzewacza pary z komorą wylotową kotła OP140, które uległy zniszczeniu w wyniku długotrwałej eksploatacji. Określono charakter uszkodzeń eksploatacyjnych. Stwierdzono, że przyczyną ich wystąpienia była zaawansowana degradacja struktury stali 13CrMo4-5 (15HM) wskutek pracy przy parametrach nadkrytycznych.

EN

The work shows the results of the studies of pipe connecting middle chambers of steam superheater with escape chamber of OP140 boiler, which were destroyed as a result of long-term exploitation. The nature of exploitations failure were specified. It was found that the cause of these occurrence has advanced the degradation of 13CrMo4-5 (15HM) steel in the effect of working in supercritical parameters.

5

Uszkodzenia rur ekranowych kotła wodnego WP 120

Barwicki L.

Dozór Techniczny

|

2008

|

z. 3

64--69

PL

Wiele kotłów wodnych eksploatowanych w ciepłowniach posiada zabudowany układ szczelny ekranów komory paleniskowej. Rury ekranowe są elementem kotła wpływajacym na jego niezawodność. Z tego też względu ustalenie przyczyn zaistniałych awarii tych elementów ma szczególnie istotne znaczenie. W artykule zrelacjonowano wyniki badań materiałowych wycinków rur ekranu szczelnego z kotła wodnego WP 120.