Retention of two dialkyl alkylphosphonates and a phosphoramidate utilized as chemical weapons agents simulants in a polyurethane rubber matrix

Gavilán Garcia I., Gimenez D., Quagliano J. C.

Aparatura Badawcza i Dydaktyczna

2013

T. 18, nr 3

223-228

In this article we report the retention of two dialkyl alkylphosphonates and a phosphoramidate in a polybutadiene-based polyurethane rubber matrix. Two dialkyl akylphosphonates, which are degradation products of nerve chemical weapons agent (CWA) and a phosphoramidate, were tested in this study for penetration into the rubber matrix. They are often used as a symulant of CWA. One of the dialkyl alkylphosphonates and the phosphoramidate were synthesized and the rubber matrix was challenger with these chemicals for retention and penetration using three different thickness of barrier material. Under the experimental conditions tested, no penetration of chemical simulants on the rubber was observed. Our results suggested that this polyurethane matrix could be a potential barrier material for protection against CWA.

Opisano zatrzymywanie dwóch dialkiloalkilofosfonianow i fosforoamidu w gumie polbutadienowopoliuretanowej. Dwa dialkiloalkilofosfoniany, które są produktami degradacji bojowych środków trujących (BST) z grupy trucizn nerwów i fosforoamidu badano pod kątem ich wnikania do gumy. Przeprowadzono syntezę jednego dialkiloalkilofosfonianu i fosforoamidu, które wraz z handlowym dialkiloalkilofosfonianem nanoszono na gumę w celu określenia ich zatrzymywania oraz przenikania stosując różne grubości gumy. W warunkach doświadczenia nie stwierdzono przenikania symulatorów przez gumę. Otrzymane wyniki pozwalają sądzić, że guma poliuretanowa może być stosowana do ochrony przed BST.

Synthesis and performance of organophosphorus fire retardants from the reaction of trimethylolpropane and dimethyl methylphosphonate

Quagliano J. C., Cruz G., Bocchio J. A., Witkiewicz Z.

Biuletyn Wojskowej Akademii Technicznej

2011

Vol. 60, nr 2

393-405

Organophosphorus fire retardants were synthetised from transesterification reaction of a bicyclic phosphite and dimethylmethyl phosphonate. Different reaction times were tested with the aim to reduce duration of the reactions. It was observed that 11 hours of heating at 200°C was enough for reaction completion, in contrast to previous studies where heating was performed for 24 hours at the same temperatures. Differential scanning calorimetry studies were performed and relevant thermal changes were identified. Infrared spectra were also registered and compared for the obtained substances. Finally, fire retardancy of oligomer phosphonates synthetised was verified testing polyurethane treated samples.

Wykonano syntezę fosforoorganicznych substancji ogniouodporniających. Synteza polegała na reakcji transestryfikacji dicyklicznych fosfonianów. Badano wpływ różnych czasów reakcji w celu zminimalizowania tego czasu. Stwierdzono, że 11 godzin ogrzewania w 200°C było wystarczające do zakończenia reakcji. Z wcześniejszych badań wynikało, że reakcję należy prowadzić przez 24 godziny. Przeprowadzono badania za pomocą różnicowej kalorymetrii skaningowej i określono zmiany zachodzące w otrzymanych substancjach w wyniku ich ogrzewania. Zarejestrowano też i porównano widma w podczerwieni tych substancji. W końcu sprawdzono działanie otrzymanych oligomerów fosfonianowych jako substancji przeciwzapalnych na próbkach poliuretanów w standardowych warunkach.