Content available Influence of notch (TIP) radius on fatigue crack growth rate
Rozumek D., Macha A., Lazzarin P., Meneghetti G.
Journal of Theoretical and Applied Mechanics
|
2006
|
Vol. 44 nr 1
127-137
EN
The paper deals with the problem of fatigue crack propagation from notches in plates made of FeP04 steel and AA356-T6 aluminium alloy. The tests were performed under different stress ranges by keeping the nominal load ratio (R=0.1) constant. The specimens were weakened by nearly sharp and blunt two sided notches. The results of the fatigue tests were then reanalysed in terms of the J-integral range including influence of the notch. It was observed that the blunter notches are, the higher fatigue crack growth rate is.
PL
W pracy przedstawiono propagację pęknięć zmęczeniowych, w próbkach płaskich z karbami, wykonanych ze stali FeP04 i stopu aluminium AA356- T6. Badania wykonywano przy różnych zakresach naprężeń i stałym współczynniku asymetrii cyklu (R = 0.1). Próbki były osłabione przez dwustronne ostre i łagodne karby. Wyniki badail zmęczeniowych opisano za pomocą zakresu całki J z uwzględnieniem wpływu karbu. Stwierdzono, że im łagodniejszy karb, tym większa prędkość wzrostu pęknięć zmęczeniowych.
2
J-integral range to characterize fatigue crack growth rate in notched specimens
Rozumek D., Lazzarin P., Macha E., Meneghetti G.
Zeszyty Naukowe. Mechanika / Politechnika Opolska
|
2005
|
z. 82
179-186
EN
The paper deals with fatigue crack propagation from notches in plates made of FeP04 steel and AA 356-T6 aluminium alloy. The tests were performed under different stress ranges by keeping constant the nominal load ratio (R=0.1). The specimens were weakened by nearly-sharp and blunt two-sided notches. The results of the fatigue tests are reanalysed here in terms of J-integral range including the notch influence. It was observed that the blunter notches are, the higher fatigue crack growth rate is.
3
Fracture Mechanics and Notch Sensitivity
Atzori B., Lazzarin P., Meneghetti G.
Zeszyty Naukowe. Mechanika / Politechnika Opolska
|
2005
|
z. 79
9-31
first rewind previous Strona / 1 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.