Effects of filament linear density on the comfort related properties of polyester knitted fabrics

Kaynak H. K., Babaarslan O.

Fibres & Textiles in Eastern Europe

2016

Vol. 24, no. 1 (115)

89--94

One of the most important developments seen in the synthetic fibre industry is absolutely producing microfibres. Microfibres provide many distinguishing properties for different end uses. In this study, the effects of filament linear densities on the comfort related properties of polyester knitted fabrics were investigated. For this aim, microfilament polyester textured yarns of 110 dtex with 0.33 dtex, 0.57 dtex and 0.76 dtex filament linear densities and conventional polyester textured yarns of 110 dtex with 1.14 dtex and 3.05 dtex filament linear densities were knitted. Dynamic liquid moisture management, air permeability, water vapour permeability and thermal properties of the fabrics were tested. Consequently it is seen that fabrics with coarser filaments have a better capability of transferring liquid moisture. Lower air permeability results are observed with finer filaments, while there is no considerable difference among the samples for water vapour permeability. Also higher thermal resistance results are obtained for samples of coarser filaments.

Istotnym czynnikiem w rozwoju przemysłu tekstylnego włókien syntetycznych było wprowadzenie mikrowłókien. Mikrowłókna pozwalają na uzyskanie szeregu właściwości istotnych dla oceny właściwości użytkowych produktu. W pracy przedstawiono wpływ masy liniowej włókien na właściwości związane z komfortem poliestrowych dzianin. W tym celu wyprodukowano dzianiny z teksturowanych przędz 110 dtex o masie liniowej włókien 0,33, 0,57 i 0,76 dtex oraz konwencjonalnej przędzy teksturowanej 110 dtex o włóknach 1,14 i 3,05 dtex. Badano opór dzianin na dynamiczny przepływ wilgoci w postaci ciekłej, przepuszczalność powietrza, przepuszczalność pary wodnej i właściwości termiczne. Wyniki badań wskazują jednoznacznie, że dzianiny o większych grubościach włókien posiadają lepsze możliwości transportu cieczy. Mniejsze wartości przepuszczalności powietrza cechują dzianiny o cieńszych włóknach podczas gdy nie ma istotnej różnicy pomiędzy zachowaniem próbek dla przepuszczalności pary wodnej. Większą opornością termiczną charakteryzują się dzianiny wykonane z grubszych włókien.

Comparative Study of the Quality Parameters of Knitted Fabrics Produced from Sirospun, Single and Two-ply Yarns twist multiplier on the properties

Kireçci A, Kaynak H K, Ince M E

Fibres & Textiles in Eastern Europe

2011

Vol. 19, no. 5 (88)

82--86

This study aimed to examine the quality parameters of knitted fabrics produced from sirospun, single and two-ply yarns. To achieve this, knitted fabrics were produced from these yarns with yarn numbers of 29.5 tex, 33 tex and 37 tex. Then sirospun yarn fabrics with 6 mm, 8 mm and 11 mm strand spacings were produced to observe the effect of strand spacing on fabric quality parameters. The experimental results show that the unevenness, hairiness, strength and elongation values of sirospun yarns are similar to or better than those of single and conventional plied yarns for all samples. However, enlarging the strand spacing causes small reductions in hairiness, strength and elongation values. The results of the fabric performance test show that the bursting strength, abrasion resistance and pilling resistance of sirospun yarn fabrics are as good as those of single and conventional plied yarn fabrics. However, the spirality values of plied yarn fabrics are slightly lower than those of sirospun yarn fabrics at finer yarn count values. These results indicate that sirospun yarn may be a good alternative for plied yarn due to its extremely low production cost and high quality values.

Dla przeprowadzenia analizy wyprodukowano dzianiny z przędz o masie liniowej 29.5 tex, 33 tex, 37 tex. Dla oceny wpływu odstępu między tasiemkami stosowano odstępy 6 mm, 8 mm i 11 mm. Wyniki badań wskazują, że nierównomierność, włochatość, wytrzymałość i wydłużenie są podobne dla wszystkich próbek otrzymanych przędz lub korzystniejsze niż dla konwencjonalnie plecionych. Jednakże stwierdzono również, że ze wzrostem odległości między tasiemkami pogarszają się w małym stopniu wyniki w zakresie włochatości, wytrzymałości i wydłużenia . Badanie dzianin wykonanych z przędz sirospun wykazały ,że wytrzymałość na zrywanie, na ścieranie i piling są nie gorsze niż dla przędz pojedynczych i plecionych konwencjonalnie. Jednakże spiralność dzianin wykonanych z przędz pojedynczych lub skręcanych konwencjonalnie jest nieco mniejsza niż spiralność dzianin wykonanych z przędz sirospun o mniejszych masach liniowych. Ogólnie można stwierdzić ,ze przędze typu sirospun są dobra alternatywą do produkcji dzianin biorąc pod uwagę bardzo niskie koszty produkcji i dobrą jakość przędz.