Alumina/graphene composite in friction and wear tests. Part 2

Wojteczko A., Wiązania G., Michalska K., Łuszcz M., Wojteczko K., Rutkowski P., Ziąbka M., Kot M., Pędzich Z.

Composites Theory and Practice

2018

R. 18, nr 4

245--248

The presented work is a continuation of tribological research on alumina/graphene composites. In our previous publication the results of wear tests on the above mentioned composite at room temperature, but also at temperatures of 150, 300 and 500°C were presented. The studies showed that this composite is promising in relation to pure alumina at ambient temperature and 150°C. In order to determine more precisely the temperatures at which the tested material can work, abrasion tests were carried out at two additional temperatures, 80 and 200°C, and the results are presented in the following paper. Noticeable plastic deformation and wear greater than at room temperature was detected already at 80°C but it was still significantly lower than at 150°C when the composite wore significantly less than pure alumina. The test carried out in 200°C gave results similar to those for 300°C, which indicates significant degradation of the material at this temperature.

Prezentowana praca jest kontynuacją badań tribologicznych nad kompozytem tlenek glinu/grafen. W naszej poprzedniej publikacji prezentowano wyniki badań ścieralności dla wspomnianego kompozytu w temperaturze pokojowej, ale również temperaturach 150, 300 oraz 500°C. Badania wykazały, że kompozyt ten jest obiecujący w odniesieniu do czystego korundu w temperaturze otoczenia oraz 150°C. W celu dokładniejszego wyznaczenia temperatur, w których może pracować badany materiał, przeprowadzono próby ścieralności w dwóch dodatkowych temperaturach, 80 oraz 200°C, i wyniki przedstawiono w niniejszej publikacji. Już temperatura 80°C prowadziła do wyraźnej deformacji plastycznej i zużycia większego niż w temperaturze pokojowej, ale wciąż było wyraźnie niższe niż to w 150°C, dla których kompozyt zużywał się mniej niż czysty tlenek glinu. Natomiast test przeprowadzony w temperaturze 200°C dał wyniki zbliżone do tych dla 300°C, co świadczy o wyraźnej degradacji materiału w tej temperaturze.

Alumina/graphene composite in friction and wear tests at elevated temperatures

Wojteczko A., Wiązania G., Michalska K., Łuszcz M., Wojteczko K., Rutkowski P., Ziąbka M., Kot M., Pędzich Z.

Composites Theory and Practice

2018

R. 18, nr 3

162--166

Alumina materials are of great interest due to their high wear resistance, resistance to corrosion, high strength and low friction. However, studies show that a graphene addition can significantly reduce wear and friction. Even a small addition of platelets results in noticeable changes in the material properties. The presented work describes the results of the ball-on-disc test conducted on two friction pairs: alumina-alumina and alumina/graphene composite - alumina. The tests were conducted at four temperatures: 20, 150, 300 and 500°C in air. Surface profile geometry measurements after the test were used to determine the wear rate. Observation of the surface microstructure after friction was carried out using a scanning electron microscope. The tests showed improvement in the wear resistance and a decrease in the friction coefficient of the composite tested at room temperature compared to pure alumina, while the use of elevated temperatures adversely affected the composite.

Materiały z tlenku glinu cieszą się dużym zainteresowaniem ze względu na wysoką odporność na zużycie, odporność na korozję, wysoką wytrzymałość i niewielkie tarcie. Badania pokazują jednak, że dodatek grafenu może znacznie zmniejszyć zużycie i tarcie. Nawet niewielki dodatek płytek powoduje zauważalne zmiany właściwości. W pracy przedstawiono wyniki badań w teście Ball-on-Disc przeprowadzonych na dwóch parach ciernych: tlenek glinu-tlenek glinu oraz kompozycie tlenek glinu/grafen- tlenek glinu. Badania przeprowadzono w czterech temperaturach: 20, 150, 300 i 500°C w powietrzu. Pomiary geometrii profili powierzchni po próbach wykorzystano do wyznaczenia wskaźnika zużycia. Obserwację mikrostrukturalną zużytych powierzchni prowadzono za pomocą skaningowego mikroskopu elektronowego. Badania wykazały poprawę odporności na zużycie i zmniejszenie współczynnika tarcia kompozytu badanego w temperaturze pokojowej w porównaniu z czystym tlenkiem glinu, natomiast zastosowanie podwyższonych temperatur miało negatywny wpływ na kompozyt.