Impact of the acidity of the medium on the corrosion resistance of the boronized surface layer – based on the cross-section of the boronized layer obtained on X6CrNiTi18-10 steel

Jagielska-Wiaderek Karina, Klimecka-Tatar Dorota

Ochrona przed Korozją

|

2023

|

nr 10

324--328

EN

The paper presents the results of research on the impact of the acidity of the environment on the corrosion resistance of X6CrNiTi18-10 steel after the boronizing process. The assessment of the corrosion resistance of the surface layer was carried out using the method of progressive thinning, which consists in performing corrosion tests on increasingly deeper areas of the layer. The use of such methodology in corrosion tests allows to track changes in individual parameters read from the potentiokinetic polarization curves and, consequently, to plot their depth profiles. The resistance of the boronized layer to general corrosion was tested in acidified sulphate solutions with three pH values: 1, 2 and 4. The structure and properties of the resulting surface layer were assessed on the basis of structural tests and microhardness changes on the cross-section of the surface-treated material. It has been found that the corrosion rate of the general surface layer is 3–4 times higher than the corrosion rate of core material, but only for strongly acidic environments. The characteristics of the passive state of steel deteriorate in particular, which is visible by the increase in the value of the critical passivation current, the minimum current in the passive range and by limiting the tendency to secondary passivation. For less acidic environments, boronization generally leads to deterioration of corrosion resistance, however, this deterioration is less than expected.

PL

W pracy przedstawiono wyniki badań dotyczących wpływu kwasowości środowiska na odporność korozyjną warstwy wierzchniej na stali typu X6CrNiTi18-10 po procesie naborowywania. Ocenę odporności korozyj nej warstwy przeprowadzono, wykorzystując metodę postępującego ścieniania, która polega na wykonywaniu testów korozyjnych na coraz głębiej położonych obszarach warstwy. Zastosowanie takiej metodyki w badaniach korozyjnych pozwala śledzić zmiany poszczególnych parametrów odczytywanych z potencjokinetycznych krzywych polaryzacji oraz wykreślić ich profile głębokościowe. Badania odporności na korozję ogólną warstwy naborowanej wykonano w zakwaszonych roztworach siarczanowych o trzech wartościach pH: 1, 2 i 4. Budowę i własności powstałej warstwy wierzchniej oceniono na podstawie badań strukturalnych oraz zmian mikrotwardości na przekroju poprzecznym obrobionego powierzchniowo materiału. Stwierdzono, że szybkość korozji ogólnej warstwy wierzchniej jest 3–4-krotnie większa niż szybkość korozji osnowy tylko dla silnie kwaśnych środowisk. Szczególnemu pogorszeniu ulegają charakterystyki stanu pasywnego stali, co uwidacznia się przez wzrost wartości krytycznego prądu pasywacji, minimalnego prądu w zakresie pasywnym oraz przez ograniczenie tendencji do pasywacji wtórnej. W wypadku środowisk mniej kwaśnych naborowanie prowadzi generalnie do pogorszenia odporności korozyjnej, jednak pogorszenie to jest mniejsze od oczekiwanego.

2

Głębokościowa charakterystyka odporności korozyjnej azotowanego stopu Ti6Al4V

Jagielska-Wiaderek Karina

Ochrona przed Korozją

|

2021

|

nr 2

34--37

PL

W pracy przedstawiono elektrochemiczną ocenę odporności korozyjnej azotowanego stopu tytanu Ti6Al4V. Badania korozyjne wykonano w 0,5M roztworze siarczanowym zakwaszonym do pH = 2 wykreślając krzywe potencjokinetyczne na różnych głębokościach warstwy wierzchniej. Grubość powstałej warstwy wierzchniej oceniono na podstawie badań strukturalnych oraz zmiany mikrotwardości na przekroju poprzecznym obrobionego powierzchniowo materiału. Stwierdzono, że przeprowadzona obróbka azotująca poprawia odporność korozyjną oraz znacznie utwardza powierzchnie badanego materiału. Uzyskana warstwa wierzchnia posiada budowę strefową przy czym najwyższą odporność korozyjną jak i najwyższą mikrotwardość wykazuje najbardziej zewnętrzna strefa azotków.

EN

The paper reports the electrochemical assessment of the corrosion resistance of the titanium alloy Ti6Al4V. Corrosion tests were carried out in a 0.5M sulphate solution acidified to pH = 2, while plotting potentiometric curves at varying depths of the top layer. The thickness of the produced top layer was assessed based on structural examination and change in microhardness over the cross-section of the surface treated material. It has been found that the nitriding treatment improves the corrosion resistance and considerably hardens the surface of the material under study. The obtained top layer exhibits a zonal structure, with the greatest corrosion resistance and the highest microhardness being shown by the outermost nitride zone.

3

Odporność korozyjna utlenianego anodowo stopu tytanu Ti6Al4V

Sitkowska Nikoletta, Jagielska-Wiaderek Karina

Archiwum Wiedzy Inżynierskiej

|

2021

|

T. 6, Nr 1

9--12

PL

Celem pracy było zbadanie wpływu parametrów anodowania stopu tytanu na jego odporność korozyjną w roztworze sztucznej śliny. Stwierdzono, że w środowisku kwasu fosforowego, narastanie warstw tlenowych zależało od czasu i gęstości prądu anodowania. Zaobserwowano, że warstwy pasywne pełnią funkcje ochronne i zwiększają odporność na korozję stopu tytanu. Odporność korozyjna materiału wzrastała wraz ze wzrostem grubości tworzonych warstw.

EN

The objective of the work was to investigate the effect of anodizing parameters of titanium alloy on its corrosion resistance in artificial saliva solution. It was found that in the environment of phosphoric acid, the growth of oxygen layers depended on the time and density of the anodizing current. It has been observed that the passive layers perform a protective function and increase the corrosion resistance of the titanium alloy. The corrosion resistance of the material increased with the thickness of the created layers.

4

Budowa strukturalna oraz odporność korozyjna na przekroju poprzecznym warstwy wierzchniej borowanej stali nierdzewnej

Jagielska-Wiaderek Karina

Ochrona przed Korozją

|

2019

|

nr 11

372--375

PL

W pracy przedstawiono badania zmian mikrostruktury i właściwości korozyjnych na przekroju poprzecznym naborowanej stali nierdzewnej typu X6CrNiTi18-10. Proces naborowywania prowadzono metodą kontaktowo-gazową w temperaturze 900 °C przez 6 godzin. Grubość powstałej warstwy wierzchniej oceniono na podstawie badań strukturalnych oraz zmiany mikrotwardości na przekroju poprzecznym obrobionego powierzchniowo materiału. Badania odporności korozyjnej wykonano w 0,5M roztworze siarczanowym zakwaszonym do pH = 4 wykreślając krzywe potencjodynamiczne na różnych głębokościach warstwy wierzchniej. Stwierdzono, że niezwykle wysokiej twardości warstwy naborowanej towarzyszy pogorszenie odporności korozyjnej. Szybkość korozji ogólnej warstwy wierzchniej jest 3-4-krotnie większa niż szybkość korozji osnowy. Szczególnemu pogorszeniu ulegają charakterystyk stanu pasywnego stali co uwidacznia się przez wzrost wartości krytycznego prądu pasywacji, minimalnego prądu w zakresie pasywnym oraz przez ograniczenie tendencji do pasywacji wtórnej.

EN

The effect of the boronized AISI 321 steel on its structure, mechanical properties and corrosion resistance in a deaerated sulphate solution is presented. The AISI 321 steel was boronized with the use of the gas-contact method for 6 hours at a temperature of 900°C. After completion of the boronizing process, the steel surface was examined by optical microscopy and with a scanning electron microscope. The thickness of the boronized coating was evaluated based on the microhardness of the cross-sectional surface layer. Potentiokinetic polarization tests were carried out in an acidified (pH = 4) 0.5M sulphate solution. It has been shown that the boronizing of the AISI 321 steel results in a substantial improvement in the hardness of the surface layer of the material treated and impairs the corrosion resistance. The rate of the corrosion of the thermochemically treated outer layers of the examined steel is 3-4 times higher than the corrosion rate of the matrix. The passive-state characteristics are particularly impaired, which manifests itself in an increase in the values of the critical passivation current and the minimum passive-range current, and in a reduction in the tendency to secondary passivation.