The purpose of the study was to determine the impact of thermo-mechanical treatment on absorption and absorption speed of iroko (Milicia exelsa (Welw.) C.C. Berg) and tauari (Couratari spp.) wood. Wood was densified in a hydraulic press in the radial direction at 100 oC and 150 oC. The modification temperature had greater impact on the density of tauari wood than on the density of iroko wood. Water absorption process depended on the wood species, the type of material (non-densified, densified), densification temperature. Iroko wood was characterized by a greater dynamic of changes in water absorption over time than tauari wood. The densified tauari wood at the maximum saturation had lower moisture content than the non-densified tauari wood. Speed of water absorption in thermo-mechanically modified wood was lower than in non-densified wood, especially noticeable in the first 30 seconds of soaking.
2
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
European oak and tauari wood were subjected to thermomechanical modification. One treatment cycle consisted of three stages: heating the wood in a hydraulic press; wood densification; and cooling the wood samples in unheated hydraulic press without exerting pressure. The treatment temperature was 100 °C or 150 °C. The modification temperature significantly affected the compressive strength parallel to the grain of oak and tauari wood. Such dependencies were not found in the case of compressive modulus of elasticity parallel to the grain of tested wood species. The compressive strength of tauari wood modified at 100 oC and 150 oC was, respectively, 16% and 20% greater than the compressive strength of oak wood modified at the same temperatures. The compressive strength parallel to the grain of the oak and tauari wood depended linearly on wood density and load.
PL
Drewno dębu i tauari poddano obróbce termo-mechanicznej. W pierwszym etapie drewno ogrzewano kontaktowo w prasie hydraulicznej, następnie zagęszczano, po czym poddawano chłodzeniu w nieogrzewanej prasie hydraulicznej bez użycia ciśnienia. Temperatura półek prasy, przy której prowadzono proces zagęszczania drewna wynosiła 100°C lub 150°C. Temperatura obróbki wykazała istotny wpływ na wytrzymałość na ściskanie wzdłuż włókien drewna dębu i tauari. Zależności tych nie stwierdzono w przypadku modułu przy ściskaniu wzdłuż włókien badanych gatunków drewna. Wytrzymałość na ściskanie drewna tauari zagęszczanego w temperaturze 100°C i 150°C była odpowiednio o 16% i 20% wyższa niż wytrzymałość na ściskanie drewna dębu modyfikowanego w tych samych temperaturach. Wytrzymałość na ściskanie wzdłuż włókien drewna dębu i tauari zależała liniowo od gęstości drewna i obciążenia wywieranego na próbkę.
The study examined the effect of UV radiation on the colour and wettability of cedar, gaboon, meranti and Scots pine wood. The tested species of exotic wood are mainly used in European countries for facades. For this kind of usage they act as a substitute for pine wood. In the study, the colour parameters were determined using the CIE L*a*b* colour space model. The tests showed that the most significant changes in the lightness of the wood occurred after 20 hours of UV radiation exposure. After that time, the L* value change was linear. The cedar wood turned the darkest and it also showed the greatest total change of colour ΔE. Comparable colour changes ΔE, and thus the greatest colour stability of all the tested wood species, were shown by the gaboon and meranti. In addition, it should be noted that all the tested wood species were characterized by a much smaller susceptibility to colour change under UV radiation than the pine sapwood and heartwood. The results also revealed that UV radiation significantly affects the contact angle, and therefore the surface free energy of the cedar and pine sapwood.
4
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Przedstawiono trendy w zastosowaniu grafenu jako napełniacza kompozytów polimerowych oraz wpływu na ich właściwości mechaniczne, elektryczne, barierowe oraz stabilność termiczną. Omówiono zagadnienia związane z pozyskiwaniem grafenu w skali umożliwiającej jego przemysłowe wykorzystanie. Zaprezentowano przykłady metod otrzymywania nanokompozytów polimerowych zawierających napełniacz grafenowy (metoda in situ, metoda rozpuszczalnikowa, metoda mieszania w stanie stopionym). Wyniki dotychczasowych badań wskazują na dużą atrakcyjność warstwowych materiałów węglowych w zastosowaniu jako potencjalnych napełniaczy wyrobów polimerów.
EN
A review, with 85 refs., covering uses of graphene as a filler for polymer-matrix composites and its effect on electrical, mech. and barrier properties of the materials. In particular, various methods for synthesis of graphene-reinforced composite materials were presented.