Preliminary evaluation of producing polymer cladding on glass fiber designated for fiber lasers

Olesik P., Kozioł M., Toroń B., Szperlich P.

Composites Theory and Practice

2018

R. 18, nr 3

140--144

The paper presents a description of preliminary trials of covering glass-ceramic fibers with polymer resins intended for new fiber optics claddings. It occurred to be impossible to obtain a polymer film on the fibers without the effect of forming droplets using an epoxy resin with a relatively low viscosity (0.58 Pa·s). Reducing the thickness of the applied film by immersing the initially covered fiber ina solvent allowed the authors to obtain a uniform thin coat of 0.25 µm, which is too small for the practical application. Applying a gel-coat (high viscosity) as a covering liquid allowed a high thickness coating to be obtained. However, the thickness was very inhomogeneous - it varied from 2 to 30 µm. The most promising coating was gained with an acetone-based dispersion of ceramic powders with a viscosity of 0.8 Pa·s. It allowed the authors to obtain a coating thick enough to be technically applicable (> 10 mm), without the presence of droplets. This is an important guideline for further work on obtaining claddings for new optical fibers. The obtained results show the importance of viscosity and internal cohesion of the applied liquid for the effectiveness of its application to a solid base. Modifying the viscosity of liquids can in many cases be a technically simpler solution than improving wettability between the liquid and the given base.

Przedstawiono opis wstępnych prób nakładania powłok polimerowych na włókna szkło-ceramiczne, docelowo mających stanowić optymalne płaszcze na nowe światłowody dla laserów. Przy zastosowaniu żywicy epoksydowej o relatywnie niskiej lepkości nie udało się uzyskać filmu bez efektu formowania kropel. Zmniejszenie grubości nałożonego filmu poprzez zanurzenie włókna po pokryciu w rozpuszczalniku, pozwoliło uzyskać równomierną cienką warstwę o grubości 0.25 μm. Jest to grubość zbyt mała dla praktycznego stosowania tej metody. Zastosowanie na powłokę żelkotu (duża lepkość) pozwoliło uzyskać dużą grubość filmu, jednak jego grubość była bardzo nierównomierna na przekroju. Najbardziej obiecująca okazała się powłoka na bazie dyspersji acetonowej proszków ceramicznych o lepkości 0.8 Pa·s. Pozwoliła ona otrzymać film o grubości technicznie stosowalnej (> 10 mm) bez obecności kropli. Jest to ważna wskazówka do dalszych prac nad uzyskaniem optymalnego płaszcza na nowe włókna światłowodowe. Uzyskane wyniki uwidoczniły duże znaczenie lepkości i wewnętrznej spójności nakładanej cieczy dla skuteczności jej nałożenia na podłoże. Modyfikacja lepkości cieczy może być w wielu przypadkach rozwiązaniem technicznie prostszym niż poprawienie zwilżalności tą cieczą danego podłoża.

Growth of large SbSI crystals

Szperlich P., Toron B., Nowak M., Jesionek M., Kepinska M., Bogdanowicz W.

Materials Science Poland

2014

Vol. 32, No. 4

669--675

In this paper a novel method of SbSI single crystals fabrication is presented. In this method a sonochemically prepared SbSI gel is used as an intermediate product in a vapour growth process. The main advantages of the presented technique are as follows. First, the SbSI gel source material has lower temperature of sublimation and allows to avoid explosions during SbSI synthesis (the sonochemical synthesis is free of any explosion hazard). Second, but not least, the grown SbSI single crystals have smaller ratio of longitudinal and lateral dimensions. The cross sections of the presented crystals are relatively large (they are up to 9 mm2 ). The crystals have been characterized by X-ray diffraction, angle-resolved optical spectroscopy, and diffusive reflectivity.

Własności optyczne monokryształów SbI3'3S8 otrzymanych z fazy gazowej

Kotyczka-Morańska M., Nowak M., Bober Ł., Kępińska M., Szperlich P., Szala J.

Inżynieria Materiałowa

2008

Vol. 29, nr 3

127-130

Jednymi z obiecujących materiałów dla optoelektroniki, ze względu na nieliniowe własności optyczne, są molekularne kryształy addycyjne. Jednym z takich materiałów jest jodosiarczek antymonu (SbI3'3Sg). Chociaż jest on znany od 1908 roku, to w pracy przedstawiono po raz pierwszy zależności temperaturowo-widmowe jego współczynnika absorpcji (a). Wyznaczenie tego parametru na podstawie badań transmisji i odbicia zwierciadlanego było możliwe dzięki zastosowaniu nowej metodyki otrzymywania monokryształów - hodowli z fazy gazowej. Z dopasowania odpowiednich zależności teoretycznych do charakterystyk widmowych a, w zakresie długości fal od 400 nm do 800 nm, określono po raz pierwszy rodzaj przerwy energetycznej w tym materiale. Wyznaczono szerokość optyczną skośnej przerwy energetycznej oraz energie Urbacha w zakresie temperatur 181 K do 301 K. Wyniki aproksymowano zależnościami półempirycznymi w celu wyznaczenia współczynników temperaturowych. Badania przeprowadzono dla promieniowania liniowo spolaryzowanego o wektorze natężenia równoległym i prostopadłym do osi c badanych monokryształów. Dla tych przypadków wartość szerokości przerwy energetycznej SbI3'3S8 w temperaturze 300 K wynosi Egl = 2,372(2) eV oraz Egš = 2,322(4) eV.

The molecular crystals of addition complexes are promising materials for optoelectronics due to their nonlinear optical properties. The antimony iodide sulfide (SbI3'3S8) belongs to this class of crystals. Despite its description in 1908, in this paper the temperature and spectral characteristics of its absorption coefficient (a) of light are presented for the first time. Determination of this parameter from optical transmittance and mirror reflectance was possible because the single crystals of SbI3'3S8 were produced by physical vapor transport technique that was applied for the first time to this material. Using the fitting of spectral characteristics of a with appropriate theoretical dependences, in the 400 nm to 800 nm spectral range, the mechanism of absorption of light in SbI3'3S8 was determined for the first time. The values of indirect forbidden optical gap and the Urbach energy were determined for the temperature range from 181 K to 301 K. These values were fitted with semiempirical relations to calculate the temperature coefficients. The investigations were performed for linearly polarized light with electric vector parallel and perpendicular to the c axis of the single crystals. In these cases, the values of optical energy gaps at T=300 K were equal E gl = 2.372(2) eV and E š = 2.322(4) eV, respectively.