The Influence of Temperature and Strain Rate on Flow Stress of Steel 10CrMo9-10 used for Drawing of Tubes

Kapustova M., Sobota R., Bilik J., Moravcik R.

Hutnik, Wiadomości Hutnicze

2017

Vol. 84, nr 8

368--370

The contribution brings an analysis of influence of essential thermomechanical forming conditions of creep resistant steel type 10CrMo9-10 on its flow stress. For experimental purposes the thermomechanical parameters of temperature and strain rate were selected. The mentioned parameters mostly influence the forming process. Cold tensile test was used as well as tensile test at increase temperatures 100°C, 150°C a 200°C at two defined strain rates. Selection of temperatures resulted from process conditions at die drawing of seamless tubes. The experiment result were created flow stress curves which will help achieve reliable numeric simulation of cold die drawing of steel tubes. Research of temperature and strain rate influence on flow stress of creep resistant steel 10CrMo9- 10 is important for increase of precision of required dimensions of final drawn tubes.

Niniejsza praca prezentuje analizę wpływu podstawowych termomechanicznych warunków kształtowania stali odpornej na pełzanie typu 10CrMo9-10 na jej naprężenie uplastyczniające. Dla celów eksperymentalnych wybrano spośród parametrów termomechanicznych temperaturę oraz szybkość odkształcania. Wspomniane parametry najbardziej wpływają na proces kształtowania. Przeprowadzono próbę rozciągania na zimno raz próby rozciągania w temperaturze podwyższonej 100°C, 150°C i 200°C dla dwóch określonych szybkościach odkształcania. Wybór temperatur podyktowany był warunkami procesu ciągnienia w ciągadle dla rur bez szwu. Wyniki testu to krzywe granicy plastyczności które pomogły w przygotowaniu wiarygodnych symulacji numerycznych dla ciągnienia na zimno rur stalowych. Badania wpływu temperatury i szybkości odkształcania odpornej na pełzanie stali typu 10CrMo9- 10 na jej naprężenie uplastyczniające są ważne dla uzyskania lepszej precyzji i wymaganych wymiarów końcowego produktu w postaci rur ciągnionych.

The research of forgeability of magnesium alloy at warm forming temperatures

Kapustova M., Sobota R., Bilik J.

Hutnik, Wiadomości Hutnicze

2016

Vol. 83, nr 9

410--412

The presented contribution is aimed at research of temperature influence on workability of a selected magnesium alloy at temperature interval for warm forming. The magnesium alloy type AZ31 was selected for experimental purposes. The mentioned alloy is used for production of drop forgings. In order to consider forgeability, Židek´s pressure test at warm conditions was selected and used as technological test. The author of mentioned test recommends cylinder shaped test sample with four notches. For magnesium alloy AZ31 hot forming at temperature interval from 250°C to 425°C is recommended. The pressure tests were conducted within the temperature interval of 200−350°C, i. e. at temperatures belonging to lower limit of recommended temperature interval, in order to acquire as much information as possible on behaviour, plasticity and formability of magnesium alloy at lower forming temperatures.

Zakres niniejszej pracy dotyczy wpływu temperatury na kowalność stopów magnezu. Wybrany do badań Stop AZ31 jest kształtowany w procesach kucia, czego efektem jest wytwarzanie odkuwek o zróżnicowanych kształtach. Biorąc pod uwagę kowalność do badań, wybrano metodę testu ciśnieniowego w podwyższonej temperaturze. Autorzy tej metody zalecają badania próbek w kształcie walca z czterema karbami. Dla badanego stopu zaleca się temperaturę obróbki plastycznej w przedziale 250°C do 425°C. Test ciśnieniowy przeprowadzono w zakresie temperatury od 200−350 °C, ze względu na analizę zachowania się stopu podczas kształtowania w temperaturze z dolnego zalecanego zakresu przeróbki plastycznej.