Influence of finish rolling temperature on properties of middle-and high-carbon steels

Rusz S., Kawulok P., Schindler I., Cizek L., Legerski M., Cmiel K.

Hutnik, Wiadomości Hutnicze

2008

Vol. 75, nr 8

508-510

The influence of a change of the finish rolling temperature on the structural characteristics and mechanical properties of 3 selected types of the medium to high-carbon steel (H02C050, H09C070, H09C080) in relation to the intended normalized or thermomechani-cal rolling in the continuous wire rod mill at Trinecke żelezarny a.s^ (further TZ) was assessed. The laboratory rolling mill Tandem in the Institute of modelling and control of forming processes at VSB-Technical University of Ostrava was used for the laboratory experiments. All the rolled products were evaluated on the basis of the metallographic investigations and tensile tests. The resulting properties are a function of the carbon equivalent; they are not dependent, however, on the parameters of the finish rolling.

Oceniono wpływ zmiany temperatury walcowania wykańczającego na charakterystykę strukturalną i właściwości mechaniczne dla 3 wybranych gatunków stali (H02C050, H09C070, H09C080) z grup stali średnio- i wysokowęglowych, w odniesieniu do założonych warunków walcowania normalizującego oraz walcowania z obróbką ćieplno-mechaniczną, realizowanych na walcarce walcówki ciągłej w Trinecke żelezarny a.s. (TZ). W badaniach laboratoryjnych wykorzystano walcarkę Tandem, będącą w posiadaniu Instytutu Modelowania i Sterowania Procesami Przeróbki Plastycznej VSB-Technical University w Ostrawie. Dla próbek pobranych z wszystkich wyrobów walcowanych wykonano badania metalograficzne oraz próby rozciągania. Otrzymane właściwości stali są funkcją równoważnika węgla, są niezależne, natomiast pośrednio zależą od parametrów walcowania wykańczającego.

Mathematical description of the strain-rate sensitivit index at hot forming of steel

Schindler I., Hadasik E., Cmiel K., Marek M.

Archives of Metallurgy

2003

Vol. 48, iss. 4

455-466

The methodology of determination of strain-rate sensitivity index was developed, based on hot rolling of a set samples with the same draft but different speed at defined temperature levels. It was proved that initial grain size had nearly negligible influence on the investigated variable, in contrast to phase composition whose influence was remarkable. Combined influence of strain rate and temperature on deformation resistance of various types of steel was studied. For a selected group of steels an universal equation was set up, which described with a good accuracy impact of reciprocal temperature and chemical composition, expressed simply by nickel equivalent, on strain-rate sensitivity in hot state.

Opracowano metodykę wyznaczania wskaźnika czułości naprężenia na prędkość odkształcenia bazując na wynikach walcowania na goraco zestawu próbek dla zadanych temperatur i prędkości walcowania, przy zachowaniu stałego gniotu. Udowodniono, że początkowa wielkość ziarna praktycznie nie ma wpływu na wyznaczony wskaźnik w odróżnieniu od składu fazowego, którego wpływ jest znaczny. Badania realizowano dla zróżnicowanych wartości prędkości odkształcenia i temperatury dla różnych typów stali. Dla wybranych grup stali opracowano uniwersalne równania, które z dobrą dokładnością opisuje wpływ temperatury i składu chemicznego, wyrażonego przez równoważnik niklu, na wskaźnik czułości naprężnia na prędkość odkształcenia podczas walcowania na gorąco.