Investigation on Evolution of Microstructures and Characterization During FSW of AZ80A Mg Alloy

Sevvel P., Jaiganesh V.

Archives of Metallurgy and Materials

2017

Vol. 62, iss. 3

1779--1785

Experimental investigation was conducted to find out microstructural characteristic changes arising in the weldments AZ80A Mg alloys obtained using the friction stir welding. Tools with three different pin profile geometries were employed during this investigation at constant tool rotational speed and feed rate. Tensile tests are performed and the tensile fracture surfaces are examined using the Scanning Electron Microscope (SEM) and the obtained SEM images are used for microstructural investigations. From the experimental results, it was observed that the geometry of the tool pin plays a significant role in producing essential stirring action there by regulating the flow of the plasticized material and leading to the formation of small sized grains having equally distributed fine strengthening precipitates. These structured grains have a direct reflecting impact in increasing the hardness and mechanical properties of the fabricated joints at the nugget zone of the friction stir welded AZ80A Mg alloy joints.

Influence of the Arrangement of Materials and Microstructural Analysis During FSW of AZ80A & AZ91C Mg Alloys

Sevvel P., Jaiganesh V.

Archives of Metallurgy and Materials

2017

Vol. 62, iss. 3

1795--1801

The main objective of this paper is to produce defect free weldments with improved properties during friction stir welding of dissimilar Mg alloys. The influence of the anisotropic arrangement of materials when AZ80A Mg alloy is taken as advancing side and AZ91C Mg alloy as retreating side and vice versa with respect to their mechanical properties and microstructural characteristics were investigated. The effects of various FSW parameters on the quality of these joints were also analyzed and best optimized FSW parameters were suggested. Defect free sound joints with excellent mechanical properties were produced when AZ80A Mg alloy was positioned at retreating side. At the same time, it seems a little bit difficult to obtain good quality joints with the contrary arrangement of materials. These investigations revealed that materials having inferior plastic deformability must be kept at the advancing side to obtain sound joints during FSW of dissimilar alloys of Magnesium.