Aging of carbon nanotube-filled fluoroelastomer in oil-based drilling fluid

Heidarian J.

Polimery

2018

T. 63, nr 3

191--212

Carbon nanotube (CNT)-, carbon black (CB)-filled fluoroelastomer (FE) and unfilled FE compounds were prepared (CNT/FE, CB/FE and FE). The oil-based drilling mud (OBD) aging resistance of these elastomers were assessed by tests of atomic force microscopy (AFM), optical microscopy and X-ray diffractometry (XRD). Weight gain, swelling and hardness were also determined. The whole conclusion is that CNT/FE can be used as O-rings in OBD drilling while FE and CB/FE can not.

Metodami mikroskopii optycznej, mikroskopii sił atomowych (AFM) i dyfraktometrii rentgenowskiej (XRD) badano odporność starzeniową kompozytów na bazie fluoroelastomeru (FE) napełnianego nanorurkami węglowymi (CNT) lub sadzą węglową (CB), poddanych działaniu płuczki wiertniczej na bazie oleju (OBD). Oznaczano też przyrost masy, stopień spęcznienia i twardość próbek poddanych starzeniu w środowisku płynu wiertniczego. Stwierdzono, że fluoroelastomer napełniony nanorurkami węglowymi jest odporny na działanie płynu wiertniczego i można go stosować w materiale uszczelek w urządzeniach wiertniczych wykorzystujących płuczki na bazie oleju.

Improving heat aging and mechanical properties of fluoroelastomer using carbon nanotubes

Heidarian J., Hassan A.

Polish Journal of Chemical Technology

2017

Vol. 19, nr 1

132--142

Carbon nanotube (CNT)-, carbon black (CB)-filled fluoroelastomer (FE) and unfilled-FE compounds were prepared (CNT/FE, CB/FE and FE). The compounds were subjected to heat air aging and characterized by tensile test and X-Ray Diffraction (XRD) analysis. Results show that CNT improved tensile properties of FE before and after aging. All samples show stress induced crystallization (SIC) during tension. XRD results show that under all conditions, the crystals were in the form of γ-phase. For both aged and un-aged specimens, the degree of crystallinity (Xc) is low. After tensile stretching, Xc of un-aged specimens increases tremendously, with larger crystal size. Under the same conditions, the order of elongation at break (EL) was FE > CB/FE > CNT/FE. Normal modulus (NM) and tangent modulus (TM) at the same conditions was in the order of CNT/FE > CB/FE > FE. Tensile strength had the order of CNT/FE > CB/FE > FE.