Influence of core component on the properties of friction spun yarns

Rameshkumar C., Anandkumar P., Kavinmurugan P., Manojkumar B., Anbumani N.

Autex Research Journal

2008

Vol. 8, no. 4

106--110

Friction (DREF II) spinning system is one of the promising spinning methods to produce yarns for technical textile applications. The core positioned exactly center and the spinning tension will be very less compare to ring and rotor spinning systems. In an experimental study to produce 6's Ne core spun yarns in DREF II spinning machine, the polyester /viscose (70/30%) sliver was used as sheath component and drawn polyester filaments (150 denier/36) were used as core component. Yarns were produced with the different core/sheath components (0/100%, 16/84%, 30/70%, 50/50% and 70/30% respectively).Friction ratio was kept at 3.33 and the feed rate was changed to produce above 6's Ne core spun yarns. Core spun yarns found that more even and high modulus than the parent friction spun yarn. The filament-core in the yarn appeared to have twisted configuration. The direction and level of twist was difficult to ascertain in these yarns. High core component yarns were found less hairy. S3 values of the yarn found minimum with increment in the core proportion in the yarn. Sheath strength contribution was analyzed with respect to the core filaments and found that the less core proportion yarns have high contribution to the tenacity.

Comparitive studies on ring rotor and vortex yarn knitted fabrics

Rameshkumar C., Anandkumar P., Senthilnathan P., Jeevitha R., Anbumani N.

Autex Research Journal

2008

Vol. 8, no. 4

100--105

Ring, Rotor and Air vortex spinning systems provide yarn with different structures and properties. Each system has its limitations and advantages in terms of technical feasibility and economic viability. 30's Ne, 100%cotton yarns were produced from the above systems and knitted in single jersey machine. The Rotor Spun yarns found with frequent breakage during knitting. Comparatively good knitting performances have shown by the Ring and Air vortex yarns. Tensile, evenness and hairiness of the yarns and bursting strength, abrasion resistance, pilling, drapability and color matching of the knitted fabrics were studied. The Ring spun yarns have high strength, low imperfection, and good bursting strength. It has high 'S3' value. Abrasion resistance of Rotor and Vortex yarns made fabrics were found higher than the ring spun yarns. Ring yarn knitted fabric has high bursting strength, Air-vortex yarn knitted fabric has poor drape due to stiffer yarn structure and the MVS yarn fabric has poor pilling resistance. Rotor, MVS yarns made fabrics have good abrasion resistance. Drapability of Vortex yarn knitted fabrics was poor than ring and Rotor yarn knitted fabrics. Good and equal depth of dye shade was found with Ring and Air vortex yarn made knitted fabrics. Ring yarn knitted fabric has shown smooth feeling than the other two fabrics.