Shear bands formation in C-oriented aluminium single crystals.

Pakul H.

Inżynieria Materiałowa

2001

R. XXII, nr 5

704-707

Changes of the crystallographic orientation have been observed in high purity C{112}<111> oriented aluminium single crystals deformed in plain strain compression (PSC) test at 77K. Local orientation measurements by the TEM/CBED and SEM/EBSD methods clearly show that initially C-oriented Al single crystals are stable only in a global sense. In accordance with the formation of two nearly symmetrically situated sets of MSBs, two oposite directed tendencies of scattering of the initial matrix orientation towards (100)[011] and (110)[001] can be observed. The activation of new, highly stressed co-planar (CP) slip systems situated along shear plane (SP) is documented.

Badano zmiany orientacji krystalograficznej w wysokiej czystości monokryształach aluminium o orientacji początkowej {112}<111>, odkształcanych w próbie nieswobodnego ściskania w temperaturze 77K. Pomiary orientacji lokalnych metodą TEM/CBED oraz SEM/EBSD pokazały, że kryształy te są stabilne jedynie w sensie globalnym. Stosownie do formowania się dwu w przybliżeniu symetrycznie usytuowanych rodzin MSBs, obserwowano dwie przeciwstawne tendencje rozmywania początkowej orientacji kryształu w kierunku położeń (001)[110] oraz (110)[001]. Proces ten związany jest z aktywowaniem wzdłuż płaszczyzny ścięcia nowych, uprzywilejowanych systemów leżących na wspólnej płaszczyźnie poślizgu.

Crystallographic aspects of the shear bands formation in C-oriented Cu-2%Al single crystals.

Pakul H., Piątkowski A., Jasieński Z., Driver J.H., Pawełek A.

Inżynieria Materiałowa

2001

R. XXII, nr 5

708-711

High purity Cu-2%Al single crystals with initial C{112}<111> orientation have been deformed by plane strain compression (PSC) at 77K and 293K to develop fine shear bands (SB) in a twin-matrix (T-M) substructure. The microstructural and microtextural changes during deformation have been studied in detail mostly by TEM/CBED method. Local orientations measurements show that the scattering of the original T-M orientations within shear bands inclined at (+/-) 35 degrees is due to the elementary, local rigid lattice rotation around the transverse direction (TD)II<011> axis.

W pracy analizowano metodami mikroskopii elektronowej wpływ umocnionej struktury matryca-bliźniak na proces formowania się pasm ścinania w monokryształach stopu Cu-2%Al, odkształcanych w próbie nieswobodnego ściskania w temperaturze 77K i 293K. W szczególności badania orientacji lokalnych metodą TEM/EBSD pokazały, że rozmycie początkowej orientacji płytek matryca-bliźniak wewnątrz pasm ścinania jest związane z procesem sztywnej rotacji sieci dookoła kierunku poprzecznego TDII<011>.