Correlation between crystal and magnetic structure of the polycrystalline and nanoparticle TbMnO3 manganite

Bażela W., Dul M., Szytuła A., Dyakonov V.

Czasopismo Techniczne. Nauki Podstawowe

|

2016

|

Y. 113, iss. 1-NP

5--15

EN

On the basis of neutron diffraction data the Mn−O bond lengths and Mn−O−Mn bond angles for the poly- and nanocrystalline TbMnO3 samples are determined. All the samples crystallize in the orthorhombically distorted perovskite structure (space group Pnma) and exhibit antiferromagnetic ordering below 41 K. The Tb atoms and O1 atoms are in (4)c site, Mn atoms − in 4(b) site and O2 atoms − in 8(d) site. The Mn−O2−Mn bond angles for the polycrystalline and nanosize samples are similar, whereas the Mn−O1−Mn bond angles for the nanoparticle samples are larger. The temperature dependencies of the Mn−O bond lengths and the Mn−O−Mn bond angles, the Jahn-Teller distortion parameter (JT) and MnO6 − octahedron distortion parameter (delta) for polycrystalline sample exhibit anomalies at TN temperature for Mn sublattice.

PL

Na podstawie wyników neutronowej dyfrakcji wyznaczono długości wiązań Mn−O oraz kąty wiązania Mn−O−Mn dla polikrystalicznej oraz nanorozmiarowych próbek manganitu TbMnO3. Wszystkie próbki krystalizują w rombowo zdystorsowanej strukturze perowskitu (grupa przestrzenna Pnma) i wykazują antyferromagnetyczne uporządkowanie poniżej 41 K. Atomy Tb i tlenu O1 zajmują pozycję 4(c), atomy Mn pozycję 4(b), a atomy tlenu O2 pozycję 4(d). Wartości kątów wiązania Mn−O2−Mn są zbliżone dla polikrystalicznej i nanorozmiarowych próbek związku TbMnO3, podczas gdy wartości kątów wiązania Mn–Mn−O1–Mn są wyższe dla próbek nanorozmiarowych. Temperaturowe zależności: długości wiązań Mn−O, kątów wiązania Mn–O–Mn, parametru dystorsji Jahna-Tellera (JT) oraz parametru dystorsji oktaedru MnOMn−O6 (delta) wykazują dla próbki polikrystalicznej anomalie w temperaturze Néela dla podsieci Mn.

2

Wpływ dawkowania zewnętrznego źródła węgla organicznego na skuteczność usuwania azotu azotanowego ze ścieków w oczyszczani mechaniczno-biologicznej

Dul M., Wałęga A., Cupak A.

Gaz, Woda i Technika Sanitarna

|

2014

|

Nr 12

472--474

PL

Celem pracy jest analiza wpływu dawkowania zewnętrznego źródła węgla organicznego na skuteczność usuwania azotu azotanowego ze ścieków w oczyszczalni mechaniczno-biologicznej w Chrzanowie. Analizę wykonano w oparciu o sprawozdania z testów technicznych przeprowadzonych przez firmy Brenntag Polska oraz KEMIPOL. Jako zewnętrzne źródło węgla wykorzystano preparaty: Brenntaplus VP1 oraz KEM-DN. Analiza wykazała, że dawkowanie zewnętrznego źródła węgla organicznego skutecznie przyczynia się do zwiększenia efektywności procesu denitryfikacji. Natomiast rodzaj zastosowanego preparatu oraz zwiększenie jego dawki nie wpływa istotnie na uzyskaną już poprawę skuteczności usuwania azotu azotanowego ze ścieków.

EN

The aim of the paper is an analysis of influence of external source of organic carbon dosage on efficiency of nitrate nitrogen removal from sewage at mechanical and biological sewage treatment plant in Chrzanów. The analysis was made basis of reports from technical tests carried out by companies: Brenntag Polska and KEMIPOL. As an external source of carbon Brenntaplus VP1 and KEM-DN preparations were used. The analysis showed, that dosage of external source of organic carbon effectively contribute to increase of denitrification process efficiency. However, the type of used preparation and increase of its dosage doesn’t significantly influence on improvement of effectiveness of nitrate nitrogen removal from sewage.

3

Określenie struktury krystalicznej oraz wielkości ziaren nanokrystalicznych próbek związku La[0.7]Sr[0.3]O[3]

Dul M., Bażela-Wróbel W.

Czasopismo Techniczne. Nauki Podstawowe

|

2010

|

R. 107, z. 1-NP

71-91

PL

Celem artykułu było określenie struktury krystalicznej trzech nanokrystalicznych próbek związku La[0.7]Sr[0.3]MnO[3] otrzymanych metodą zol-żel. Temperatury prażenia żelu wynosiły, odpowiednio: 600, 800 i 1000[stopni]C, co prowadziło do otrzymania próbek o różnych rozmiarach ziaren (od 17 do 90 nm). Za pomocą rentgenowskiej dyfraktometrii proszkowej wyznaczono stałe sieciowe komórki elementarnej i parametry pozycyjne atomów oraz z poszerzenia maksimów dyfrakcyjnych rozmiary ziaren (relacja Scherrera).

EN

Crystal structure of three nanopowders La[0.7]Sr[0.3]MnO[3] carried out by sol-gel method were determined. The annealing temperatures were: 600, 800 and 1000[degrees]C. The nanopowders with the average particle size from 17 to 90 nm were obtained. The constans of elementary cell, position parameters of atoms and grain sizes using the broading of diffraction lines (Scherrer's relation) have been obtained.

4

X-ray diffraction and magnetic properties measurement of nanopowder (La[0.7]Sr[0.3])[0.9]Mn[1.1]O[3] manganite

Bażela-Wróbel W., Dyakonov W., Dul M.

Czasopismo Techniczne. Nauki Podstawowe

|

2009

|

R. 106, z. 1-NP

123-137

EN

We report on the X-ray powder diffraction and magnetic measurements of nanosize (La[0.7]Sr[0.3])[0.9]Mn[1.1]O[3] manganite. The nanoparticles were synthesized with use of co-precipitation method at different (800, 900 and 950[degrees]C) temperatures. Their crystal structure was determined to be perovskite-like with a rhombohedral distortion (the space group R 3c). The phase composition and specific surface nanopowders were determined. The average size of synthesized nanoparticles (from 32 to 88 nm) was estimated by both the method of low temperature adsorption of argon and X-ray diffraction measurements. All the nanosize samples show ferromagnetic-like ordering with close phase transition temperatures. Their magnetization decreases with reducing the particle size. The decrease of magnetization with decreasing particle size is due to increasing the surface contribution to magnetization. The magnetic entropy was shown to increase with increasing applied magnetic field and to be smaller for the small particles.

PL

W artykule przedstawiono wyniki pomiarów dyfrakcji rentgenowskiej oraz uzyskanych metodą magnetometryczną nanorozmiarowego manganitu (La[0.7]Sr[0.3])[0.9]Mn[1.1]O[3]. Próbki otrzymano metodą zol-żel w następujących temperaturach: 800, 900 i 950[stopni]C. Wszystkie próbki krystalizują w układzie romboedrycznym (grupa przestrzenna R 3c). Średni rozmiar ziaren (od 32 do 88 nm) określono za pomocą rentgenowskiej dyfrakcji proszkowej oraz metodą niskotemperaturowej adsorpcji argonu. Wszystkie próbki wykazują ferromagnetyczne uporządkowanie z bliskimi temperaturami przejścia fazowego i ich namagnesowanie maleje wraz ze zmniejszaniem się rozmiarów ziaren. Zmniejszenie namagnesowania wraz ze zwiększaniem się rozmiarów ziaren jest spowodowane wzrostem wkładu powierzchni ziaren do namagnesowania. Magnetyczna entropia rośnie wraz ze wzrostem pola magnetycznego i jest mniejsza dla małych ziaren.

5

Badania nad syntezą i własnościami aplikacyjnymi wybranych amidów kwasu fosforowego

Dul M., Mróz J.

Prace Naukowe Instytutu Technologii Organicznej i Tworzyw Sztucznych Politechniki Wrocławskiej. Konferencje

|

2003

|

Vol. 52, nr 25

585-588

PL

Opracowano metodę syntezy amidoestrów kwasu fosforowego w reakcji difenylochlorofosforanu rozpuszczonego w niepolarnym rozpuszczalniku z odpowiednią aminą I- lub II- rzędową użytą w ilości zapewniającej przereagowanie difenychlorofosforanu oraz wydzielającego sie chlorowodoru w temperaturze do 25 °C. Otrzymane aminoestry z amin II-rzędowych tworzą plastizole z emulsyjnym PCV o stosunkowo niskiej lepkość a otrzymane na ich bazie impregnaty charakteryzują się dużą odpornością ogniową.

EN

There have been synthesed amide esters of phosphoric acid in reaction of diphenyl chloride dissolved in non-polar dissolvant with the proper amine primary of secondary, that has been used in quantity that assured fully reaction of diphenyl chloric Phosphate and enducing hydrogen chloride in temperature up 25 centigrade. The enduced amide-esters from secundary amine formed plastisols with PCV emulsion. The PCV emulsion was of relatively low visosity and the impregnats obtained on the base of them, were characterised by high fire resistance.