Application of ceramic preforms to the manufacturing of ceramic-metal composites

Jach K., Pietrzak K., Wajler A., Sidorowicz A., Brykała U.

Archives of Metallurgy and Materials

2013

Vol. 58, iss. 4

1425--1428

This paper presents new solution to manufacturing Cu-Al2O3 composites with a dispersed reinforcement phase. It consists in substituting commonly used commercial alumina powder with crushed ceramic foam. Very low strength of thin-walled Al2O3 porous foams results in both their easy destruction and isolation of fragments <200 μm. The addition of the ceramic phase is 3-10 vol.%. The sintering process is performed for 30 min in a hot-press at 1050°C and 30 MPa. The aim of the presented paper is to study the effect of the volume content of the ceramic phase on the microstructure and selected physical and thermal properties of copper - alumina composites.

Artykuł przedstawia nowatorskie rozwiązanie wytwarzania kompozytów Cu-Al2O3 z rozproszoną fazą wzmacniającą. Polega ono na wykorzystaniu zamiast powszechnie stosowanego handlowego proszku tlenku glinu, rozkruszonej pianki cera- micznej. Wysoka kruchość cienkościennych, porowatych pianek Cu-Al2O3 pozwoliła na łatwe ich rozdrobnienie i wyodrębnienie frakcji o fragmentach wielkości < 200 /im. Dodatek fazy ceramicznej wynosił 3-10%obj. Proces spiekania prowadzono w temperaturze 1050°C w czasie 30 min i pod ciśnieniem 30 MPa. Celem pracy było określenie wpływu ilości dodatku fazy ceramicznej na mikrostrukturę oraz wybrane właściwości otrzymanych kompozytów.