Effect Of The Desorption-Recombination Temperature On The Microstructure And Magnetic Properties Of HDDR Processed Nd-Fe-B Powders

Lee J.-G., Cha H.-R., Liu S., Yu J.-H., Baek Y.-K., Kwon H.-W.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 2B

1499--1501

The effect of the desorption-recombination temperature on the microstructure and magnetic properties of hydrogenation-disproportionation-desorption-recombination (HDDR) processed Nd-Fe-B powders was studied. The NdxB6.4Ga0.3Nb20.2Febal (x=12.5-13.5, at.%) casting alloys were pulverized after homogenizing annealing, and then subjected to HDDR treatment. During the HDDR process, desorption-recombination (DR) reaction was induced at two different temperature, 810°C and 820°C. The higher Nd content resulted in enhanced coercivity of the HDDR powder, and which was attributed to the thicker and more uniform Nd-rich phase along grain boundaries. But this uniform Nd-rich phase induced faster grain growth. The remanence of the powder DR-treated at 820°C is higher than that DR-treated at 810°C. In addition, it was also confirmed that higher DR temperature is much more effective to improve squareness.