Mechanical Characterisation of Carbon Fibre-Reinforced Plastics with Defined Defects

Ashir M., Bardl G., Hahn L., Nocke A., Cherif C.

Fibres & Textiles in Eastern Europe

|

2018

|

Vol. 26, no. 6 (132)

126--132

EN

A steadily increasing application of fibre-reinforced plastics in the field of lightweight construction has been observed in the course of the past two decades. Currently a major challenge in the growing high technology market is the quality assurance of manufactured fibre-reinforced plastic components. During different stages in the manufacturing process of fibre-reinforced plastics, defects of different types and sizes are enclosed in them, exerting a destructive influence on the performance of fibre-reinforced plastics in various practical applications in terms of strength, stiffness and brittleness. Thus the aim of this research project was to investigate the effect of defined local defects on the mechanical properties,such as tensile, flexural and impact properties, of fibre-reinforced plastics, in particular carbon fibre-reinforced plastics. Results show that these mechanical properties depend significantly on the type and size of defect.

PL

W ciągu ostatnich dwóch dekad zaobserwowano stale rosnące zastosowanie w dziedzinie lekkich konstrukcji tworzyw sztucznych wzmocnionych włóknami. Obecnie dużym wyzwaniem na rosnącym rynku wysokich technologii jest wyprodukowanie wysokiej jakości komponentów z tworzyw sztucznych wzmocnionych włóknami. Podczas różnych etapów procesu wytwarzania tworzyw sztucznych wzmacnianych włóknami pojawiają się defekty różnego rodzaju i rozmiarów wywierające destrukcyjny wpływ na działanie tworzyw sztucznych wzmacnianych włóknami w różnych praktycznych zastosowaniach pod względem wytrzymałości, sztywności i kruchości. Celem pracy było zbadanie wpływu określonych defektów lokalnych na właściwości mechaniczne, takie jak właściwości rozciągające, zginające i uderzeniowe. Wyniki pokazały, że właściwości mechaniczne zależą w znacznym stopniu od rodzaju i rozmiaru defektu.

2

Measurement methods of dynamic yarn tension in a ring spinning process

Hossain M., Abdkader A., Nocke A., Unger R., Krzywinski F., Hasan M. M. B., Cherif C.

Fibres & Textiles in Eastern Europe

|

2016

|

Vol. 24, no. 1 (115)

36--43

EN

The most common measuring method to characterise the dynamic yarn path in the ring spinning process is to measure the yarn tension, where the yarn path is almost straight. However, it is much more complex to measure the yarn tension at the other positions, for example, between the yarn guide and traveller (balloon zone) and between the traveller and winding point of the cop (winding zone), as the yarn rotates continuously around the spindle axis. In this paper, two new methods of yarn tension measurement in the balloon zone are proposed. In the first method, the balloon shape was first recorded with a high speed camera. The balloon tension was then calculated by comparing the yarn strain (occurring in the balloon zone) measured by a digital image analysis program with the stress-strain curve of the yarn produced. In the second method, the radial forces of the rotating balloon were measured by using modified measurement techniques for measurement of yarn tension. Moreover a customised sensor was developed to measure the winding tension between the traveller and cop. The values measured were validated with a theoretical model and a good correlation between the measured and theoretical values could be revealed.

PL

Najczęściej stosowaną metodą pomiarową dla scharakteryzowania dynamiki przędzy podczas przędzenia obrączkowego jest pomiar naprężenia przędzy w miejscu gdzie jej przebieg jest prawie prostoliniowy. Jednakże znacznie bardziej skomplikowany jest pomiar naprężenia przędzy pomiędzy prowadnikiem i biegaczem (strefa balonu) oraz pomiędzy biegaczem i punktem skręcania przed cewką nawojowa (strefa skręcania) ponieważ przędza wiruje w sposób ciągły wokół osi wrzeciona. W pracy przedstawiono dwie nowe metody pomiaru naprężenia przędzy w strefie balonu. W pierwszej wstępnie określano kształt balonu za pomocą kamery o dużej prędkości powtarzania. Następnie określano naprężenie balonu przez porównanie odkształceń przędzy powstających w strefie balonu a mierzonych za pomocą cyfrowej analizy obrazu i programu wykorzystującego krzywą zależności naprężenie-odkształcenie produkowanej przędzy. W drugiej metodzie promieniowe siły wirującego balonu były mierzone przy zastosowaniu zmodernizowanej techniki pomiaru naprężenia przędzy. Pomierzone wartości były porównywane z wartościami modelu teoretycznego przy czym stwierdzono istnienie bardzo dobrej korelacji.

3

Miniaturized textile-based multi-layer pH-sensor for wound monitoring applications

Nocke A., Schröter A., Cherif C, Gerlach G.

Autex Research Journal

|

2012

|

Vol. 12, no. 1

20--22

EN

Wound assessment has become an important issue in the wound treatment procedure. One important indicator of the wound status is the pH value. Our approach to assess this quantity is through use of a fiber sensor coated with a pH-responsive hydrogel, which functions as a sensitive layer for impedance measurements. An advantage of this is its integratability into wound dressings using standard textile technologies. The pH characteristic shows a pH-dependent behavior of the absolute impedance at certain frequencies. The fabrication technology and sensor characteristics are discussed. The values of almost 14% impedance change demonstrate the potential for improvement by optimizing fabrication technologies. The presented sensor meets all requirements necessary for wound pH assessment.