Resistance to high-temperature corrosion of new materials for power industry

Hernas A., Piliszko B., Imosa M.

Archiwum Energetyki

|

2008

|

T. 38, nr 1

157-170

EN

The high temperature corrosion resistance of heat-resisting alloys in simulated combustion atmosphere containing sulphur and chlorine was studied. The investigations were carried out in laboratory conditions in N2 + 9%02 + 0,2%HC1 + 0,08%SO2 atmosphere. The hot-corrosion test was carried out at a temperature 400-800° C during 1200 hours. The corrosion products were characterized by scanning electron microscopy and energy-depressive x-ray spectroscopy. The article includes the investigation of mass changes upon the corrosion test.

PL

Artykuł przedstawia wyniki badań odporności korozyjnej standardowych i nowych stali i stopów żarowytrzymałych w warunkach wysokotemperaturowej korozji siarkowo-chlorowej. Badania przeprowadzono w warunkach laboratoryjnych w atmosferze gazowej zawierającej- N2 + 9%C2 + 0,2%HC1 + 0,08%SO2 oraz w popiołach, a także w testach wykonanych w warunkach rzeczywistych spalarni odpadów. Temperatura testów laboratoryjnych mieściła się w zakresie 400-800°C, a czas do 1200 godz. Przedstawiono kinetykę i charakterystyki procesów korozyjnych badanych materiałów. Metodami mikroskopii skaningowej określono strukturę produktów korozji, ich skład chemiczny oraz fazowy.

2

Resistance to High- Temperature Corrosion of New Materials for Power Industry

Hernas A., Dytkowicz B., Imosa M.

Archivum Combustionis

|

2007

|

Vol. 27 nr 1-2

33-44

EN

Development of materials engineering of creep-resisting materials is strictly connected with many technical branches, first of all with thermal power and nuclear energetics, aviation, chemical industry, municipal waste neutralization and other related fields. However, the main application of creep-resistant steels and alloys falls to thermal power industry. The requirements imposed on steels and alloys for work at elevated temperature considerably overstep the standard characteristics utilized in constructional calculations. Their range subjected to extension mainly due to required high hardness of those alloys. Material fitness for use as constructional components of power engineering systems is determined by four basic groups of properties described as mechanical, physicochemical, technological and ductility that is schematically presented in the figure 1 [1].

3

Morphology of the ash corrosion products on the P92 steel

Hernas A., Imosa M.

Inżynieria Materiałowa

|

2004

|

R. XXV, nr 3

721-723

EN

The P92 steel, owing to its high mechanical strength at an elevated temperature, is one of the new steel types intended for the components of modern boilers in the power engineering industry. Currently, attempts are being undertaken to use the P92 steel for the components of boiler units in municipal waste incineration plants. Therefore, it is important that an analysis be made of the P92 steel resistance to the high-temperature chlorine - sulphur corrosion impact, the latter being the main factor which limits durability of boilers in waste incineration plants. The present article presents the investigation of the P92 steel corrosion resistance under the conditions of high-temperature chlorine - sulphur corrosion in an atmosphere of flue gas with ashes. The analyses were conducted by means of laboratory tests in an atmosphere containing sulphur and chlorine compounds. The morphology of corrosion products was determined by scanning microscopy and X-ray analysis methods.

PL

Stal P92 jest jedną z nowych stali na elementy urządzeń energetycznych konwencjonalnych kotłów ze względu na swoje wysokie własności wytrzymałościowe w podwyższonej temperaturze. Obecnie podejmuje się próby zastosowania stali P92 na elementy instalacji kotłów spalarni odpadów komunalnych. Dlatego ważne jest zbadanie odporności stali P92 na oddziaływanie wysokotemperaturowej korozji chlorowo -siarkowej, która jest głównym czynnikiem ograniczającym trwałość kotłów spalarni odpadów. Artykuł przedstawia badania odporności korozyjnej stali P92 w warunkach wysokotemperaturowej korozji chlorowo-siarkowej w atmosferze spalin z popiołami. Badania przeprowadzono w testach laboratoryjnych w atmosferze zawierającej zwiqzki siarki i chloru. Metodami mikroskopii skaningowej i analizy rentgenowskiej określono morfologię produktów korozji.