On the phase equilibria in the system Ag-Sn-Zn

Vassilev G. P., Tedenac J.-C., Dobrev E. S., Evtimova S. K.

Archives of Metallurgy

2001

Vol. 46, iss. 3

249-254

The phase equilibria in the system Ag-Sn-Zn have been studied using scanning electron microscope. X-ray and microharness measurements, difrerential scanning calorimetry and optical microscopy. 27 alloys have been prepared and annealed for 3 months at 380°C. All ternary phases arc based on the binary ones. The microhardness values of the γ phase arc the highest in the system Ag-Sn-Zn, The ternary β phase (formed on the base of the binary AgZn β phase) contains up to = 13 at.% Sn, while the γ and ε phases - up to = 0.2 at.% Sn only. The solubility of Zn in the Ag-Sn-based intermetallic ε (Ag3Sn) and ζ (Ag4Sn) phases is also significant. An isothermal section of the phase diagram at 380°C has been constructed.

Równowagi międzyfazowc w układzie Ag-Sn-Zn zbadano przy pomocy skaningowej mikroskopii elektronowej (SEM), dyfrakcji rentgenowskie (XRD), pomiarów mikrotwardości, kalorymetrii skanningowej (DSC) oraz mikroskopii optycznej. Przygotowano 27 stopów, które wyżarzano następnie w 380°C przez 3 miesiące. Wszystkie rozpatrywane fazy trójskładnikowe wywodzą się z faz podwójnych. Najwyższa twardość w układzie stwierdzono dla fazy γ. Faza potrójna β (powstała na bazie fazy podwójnej β-AgZn) zawiera aż do - 13 at.%Sn. podczas gdy fazy: γ i ε zawierają tylko do - 0.2 at.%Sn. Rozpuszczalność cynku w fazach międzymetalicznych układu Ag-Sn: ε -Ag3Sn i ζ-Ag4Sn jest również znaczna. Na podstawie badan własnych skonstruowano przekrój izotermiczny układu potrójnego w 380°C.