A study of nickel and cobalt silicides formed in the Ni/Co/Si(1 0 0) system by thermal annealing

Sedrati C., Bouabellou A., Kabir A., Haddad R., Boudissa M., Taabouche A., Fiad H., Hammoudi A.

Materials Science Poland

2020

Vol. 38, No. 3

394--399

In this work, the Ni/Co/Si system was annealed at temperatures ranging from 300 °C to 800 °C. The samples were characterized by means of X-ray diffraction (XRD), Raman spectroscopy, Rutherford backscattering spectroscopy (RBS), atomic force microscopy (AFM) and sheet resistance measurement. The XRD and Raman spectroscopy results showed that the formation of nickel and cobalt silicides (CoSi, Co2Si, Ni2Si, NiSi, NiSi2, CoSi2) is an annealing temperature dependent diffusion process. The diffusion phenomenon was evidenced by RBS. The low values of the sheet resistance which were correlated with the films surface roughness were attributed to the formation of both CoSi and NiSi phases.

Mechanical properties and low temperature degradation resistance of alumina-doped 3Y-TZP fabricated from stabilizer coated powders

Kern F., Kabir A., Gadow R.

Materiały Ceramiczne

2017

T. 69, nr 3

279--285

In this study nanoscale monoclinic zirconia was coated with 3 mol % yttria via the nitrate route. Up to 2 vol.% of alumina were added by either coating or mixing and milling. The mechanical properties of the materials, microstructure and phase composition were studied. Low temperature degradation resistance was determined by an accelerated autoclave test. The TZP materials showed a high toughness of > 10 MPa√m combined with a strength of ~ 740-1000 MPa. Low temperature degradation resistance improved with alumina addition, here the introduction of alumina by mixing and milling was more efficient than by powder coating; the maximum monoclinic fraction in the mixed composite was only 6 vol.% after 100 h of autoclave ageing at 134 °C and the monoclinic phase did not form a fully connected layer.

W niniejszym badaniu jednoskośny nanometryczny dwytlenek cyrkonu pokrywano tlenkiem itru w ilości 3% mol., wykorzystując ścieżkę azotanową. Poprzez pokrywanie lub mieszanie i mielenie dodano aż do 2% obj. tlenku glinu. Zbadano właściwości mechaniczne, mikrostrukturę i skład fazowy materiałów. Za pomocą przyśpieszonego testu autoklawowego określono niskotemperaturową degradację. Materiały TZP pokazały wysoką odporność na pękanie przekraczającą 10 MPa√m w połączeniu z wytrzymałością wynoszącą ~ 740-1000 MPa. Odporność na niskotemperaturową degradację została poprawiona dodatkiem tlenku glinu, gdzie wprowadzenie tlenku glinu drogą mieszania i mielenia było bardziej efektywne niż przez pokrywanie proszku; maksymalna frakcja jednoskośnia w kompozycie stanowiła jedynie 6% obj. po starzeniu w autoklawie przez 100 h w 134 °C a faza jednoskośna nie utworzyła całkowicie spójnej warstwy.