Preparation and characterization of epoxy resins filled with submicron spherical zirconia particles

Bondioli F., Cannillo V., Fabbri E., Messori M.

Polimery

2006

T. 51, nr 11-12

794-798

Submicron spherical zirconia particles were synthesized and used as a reinforcement for epoxy resins. In fact, recent developments indicate that a significant improvement in the thermoset polymer performance may be obtained by using submicron inorganic filler. In this paper, different composites with weight fraction of the filler in the range 1-5 % were prepared and characterized in terms of mechanical properties. A numerical model suitable for the description of such materials was set up and employed to estimate the properties as functions of the reinforcement content.

Zsyntetyzowano submikroskopowe cząstki ditlenku cyrkonu i scharakteryzowano je metodami analizy rentgenowskiej i elementarnej. Za pomocą transmisyjnego mikroskopu elektronowego (TEM) wykonano zdjęcia (rys. 1) i wyznaczono średnice, powierzchnię właściwą i gęstości (tabela 1) cząstek wytrąconych z roztworów o dwu różnych stężeniach wody (0,35 M i 0,6 M). Otrzymanymi cząstkami napełniano (1, 3 lub 5 % mas.) żywicę epoksydową a produkty badano metodą skaningowej mikroskopii elektronowej (SEM, rys. 2) oraz wyznaczano moduł sprężystości wzdłużnej (E, tabela 2). Opracowano i przetestowano modele pozwalające na przewidywanie wartości E badanych nanokompozytów w zależności od zawartości napełniacza (rys. 3, tabela 3).

Surface modification of unsaturated polyester resins with perfluoropolyethers

Fabbri E., Fabbri P., Messori M., Pilati F., Tonelli C., Toselli M.

Polimery

2004

T. 49, nr 11-12

785-789

Fluorine-modified unsaturated polyester resins were prepared by using polycaprolactone/perfluoropolyether/polycaprolactone triblock copolymers having hydroxyl or methacrylate end-groups. Despite the immiscibility of the perfluoropolyether segment, all the modified resins were fully transparent after curing thanks to the compatibilization effect of the polycaprolactone segments. Contact angle measurements showed a very low water wettability for all investigated resin compositions. Also in the case of system with the lower bulk copolymer concentration (less than 0.3 phr) contact angle was higher than 94°. It has been demonstrated that the presence of methacrylate end-groups tends to hinder the surface segregation of the fluorinated additive.

Handlową nienasyconą żywicę poliestrową modyfikowano mieszając ją z różniącymi się składem trójblokowymi kopolimerami polikaprolakton/poli(perfluoroeter)/polikaprolakton [TXCL(y)] z końcowymi grupami hydroksylowymi lub metakrylanowymi [produkt reakcji TXCL(y)Acr z metakrylanem 2-izocyjanianu etylu]. Przebieg syntezy oraz otrzymane produkty scharakteryzowano metodami FT-IR (rys. 1) i 1H NMR (tabela 1, rys. 2). Pomimo znanego braku mieszalności segmentu poli(perfluoroeteru), wszystkie modyfikowane nim żywice były przezroczyste po utwardzeniu dzięki kompatybilizującemu wpływowi segmentów polikaprolaktonu. Modyfikowane produkty charakteryzowały się bardzo małą zwilżalnością wodą (znacznie większe wartości kąta zwilżania theta niż w przypadku żywic niemodyfikowanych). Wyniki badania kąta theta (rys. 3) wskazują też, że obecność końcowych grup metakrylanowych ogranicza powodującą hydrofobowość migrację segmentów fluorowych na powierzchnię.