Dependence of magnetic properties on the chemical composition of the Fe65-xCo5+xMo5Zr8Nb2B15 (x = 0, 5, 10) and Fe60Co10Mo5Cr10-xNbxB15 (x = 2, 4, 6, 8) bulk amorphous alloys.

Wójcik N., Winczura L., Kolano R., Szynowski J., Haneczok G.

Archives of Materials Science

|

2004

|

Vol. 25, nr 4

499-505

EN

Fe65-xCo5+xMo5Zr8Nb2B15 (x = 0, 5, 10) and Fe60Co10Mo5Cr10-xNbxB15 (x = 2, 4, 6, 8) bulk amorphous alloys with different contents of Co, Zr, Nb and Cr were investigated. Samples of the alloys were prepared in a form of amorphous ribbons 4-8 mm wide and 22-65 micrometers thick, obtained by the melt-spinning technique. Chemical composition of the ribbons was examined using JEOL X-ray microanalyser, and their amorphous state was checked by the X-ray diffractometer. Dependence of the magnetisation M and Curie temperature Tc on the chemical composition of the alloys was determined. Moreover, such alloy parameters as density, resistivity and coercivity were measured.

2

Własności magnetyczne nanokrystalicznego materiału typu Finemet

Kolano-Burian A., Kolano R., Szynowski J., Wójcik N., Winczura L.

Archiwum Nauki o Materiałach

|

2003

|

T. 24, nr 1

79-93

PL

Przedstawiono wyniki badań dotyczących sposobu wytwarzania stopu Finemet (Fe73,5Cu1Nb3Si13,5B9) oraz kształtowania jego struktury i wynikających z niej znakomitych właściwości magnetycznie miękkich. Na uwagę zasługują wyniki badań wpływu prędkości chłodzenia po obróbce cieplnej taśmy (MS) na strukturę i przenikalność magnetyczną stopu oraz badania wpływu pola magnetycznego działającego w czasie obróbki cieplnej na strukturę domenową i kształt pętli histerezy. Ponadto zamieszczono wyniki badań wpływu częstotliwości pola magnesującego na zmiany niektórych parametrów magnetycznych (Bm, Ps, Hc, Br).

EN

Results of a research work related to preparation of the Finemet-type Fe73,5Cu1Nb3Si13,5B9 alloy and formation of its structure resulting in excellent soft magnetic properties have been presented. Particularly interesting are results of a study of an effect of the cooling rate for a ribbon after heat treatment on the structure and magnetic permeability of the alloy, and of a study of the influence of the magnetic field present during heat treatment on the domain structure and shape of the hysteresis loop. Moreover, results of the investigation on magnetizing field frequency dependence of the main magnetic parameters, i.e. Bm, Ps, Hc and Br, have been presented.

3

The effect of production conditions on superparamagnetic properties of the FeCrMoCuNbSiB alloys

Kolano R., Olszewski J., Szynowski J., Kolano-Burian A., Winczura L.

Archiwum Nauki o Materiałach

|

2002

|

T. 23, nr 3

209-216

EN

The aim of this investigation was to choose the chemical composition and to determine the heat treatment conditions for the nanocrystalline Fe72.5-xCrxMo1Cu1Nb3Si13.5B9 (x=4 or 6) and Fe65Cr7Mo1Cu1Nb3Si12B10.5 alloys in order to get the lowest possible temperature of transition (Tc) from the ferromagnetic to superparamagnetic state. On the basis of magnetic and Moessbauer measurements it was found that the temperatures of transition from ferromagnetic to superparamagnetic state in Fe66,5Cr6Mo1Cu1Nb3Si13.5B9 and Fe65.5Cr7Mo1Cu1Nb3Si12B10.5 alloys were 450 K and 424 K, respectively.

PL

Badania przedstawione w niniejszym artykule miały na celu wybranie odpowiedniego składu chemicznego oraz warunków obróbki cieplnej dla nanokrystalicznych stopów Fe72.5-xCrxMo1Cu1Nb3Si13,5B9 (x=4 lub 6) oraz Fe65Cr7Mo1Cu1Nb3Si12B10,5, aby osiągnąć możliwie niską temperaturę przejścia (Tc) ze stanu ferromagnetycznego do superparamagnetycznego. Na podstawie pomiarów magnetycznych, a także badań Moessbauerowskich została wyznaczona temperatura przejścia stopów Fe66,5Cr6Mo1Cu1Nb3Si13,5B9 oraz Fe65,5Cr7Mo1Cu1Nb3Si12B10,5 ze stanu ferromagnetycznego do superparamagnetycznego. Dla stopu Fe66,5Cr6Mo1Cu1Nb3Si13,5B9 wyniosła ona 450 K, natomiast dla Fe65,5Cr7Mo1Cu1Nb3Si12B10,5 424 K.