From waste to treat waste : exploitation of marble dust as a harmful pollutant to a green adsorbent for dyes and heavy metals from industrial wastewater

Attia H.A., Farghaly Mohamed G., Saleh A.M., Abdel Khalek M.A.

Physicochemical Problems of Mineral Processing

|

2022

|

Vol. 58, iss. 6

art. no. 154007

EN

The marble dust as a harmful industrial waste of marble fabrication was evaluated as aneconomical and efficient green adsorbent for Acid Red-1 dye and lead ions. The XRD, XRF, particle size, surface area and zeta-potential measurements were used to characterize the marble dust. The removal efficiency was optimized by studying several parameters such as pH, temperature, contact time, adsorbent dose and initial concentration. The optimum removal was achieved at pH 6, 20°C after 60 min in the presence of 2.5g/L marble dust. The rates of adsorption were found to follow the pseudo-second-order model. The results showed better fitting to Freundlich isotherm. The thermodynamic studies revealed that the adsorption process is spontaneous, exothermic and favorable at low temperature. The free energy (∆G°), enthalpy (∆H°), and entropy (∆S°) changes were calculated to predict the nature of adsorption.The removal efficiency was improved by calcination of the marble at 700°C. Application for textilewastewater showed high removal efficiency up to 99.9%of inorganic and organic pollutants. The product of treatment was used in the concrete and bricks manufactured, so there is nogeneration of second-order pollutants.

2

A study on the performance of second order models and two phase models in iron ore flotation

Saleh A. M.

Physicochemical Problems of Mineral Processing

|

2010

|

Vol. 44

215-230

EN

In this study, the fit to the experimental data of two second order models and two phase model were compared with first order models. The best fit was observed with the two parameter model with rectangular distribution of floatabilities (model II) and the three parameter fast/slow floating particles model (model I). Also, the three parameter gamma distribution model (model VI) showed good fit to the experimental data. The worst fit was observed with first order two stage kinetic model (model V) which indicates that there is no need to divide the flotation rate into two flotation rates. Model VII which includes six parameters gave acceptable fit to experimental data. This result is in contrast with the results obtained by other investigators which states that increase of parameters in model leads to parameter dilution and increase on model error. Hence, it may be concluded that the number of parameters to obtain an adequate model needs more investigation. The confidence intervals for the three best models (model I, model II and model VI) were estimated at 95% confidence level. Also, model II shows more discrete regions with regard to flotation rate and recovery than model VI. This result indicates the ability of such model to express the changes in flotation reagents and/or flotation conditions over other tested models.

PL

Porównano wierność opisu danych pomiarowych za pomocą kinetycznych modeli drugiego rzędu i modeli dwufazowych. Najlepszy opis odnotowano za pomocą modelu dwuparametrowego z potęgową dystrybucją flotowalności (model II) oraz trójparametrowego modelu dla szybko/wolno flotujących ziarn (model I). Także trójparametrowy model oparty o .-dystrybucję (model VI) dobrze opisywał dane pomiarowe. Najgorsze dopasowanie obserwowano dla modelu pierwszego rzędu dwustopniowego modelu kinetycznego (model V), co wskazuje, że nie ma potrzeby dzielenia szybkości flotacji na dwie części. Model VII, który zawiera sześć parametrów, także daje poprawny opis danych. Wynik ten kontrastuje z wynikami otrzymanymi przez innych badaczy twierdzących, że wzrost liczby parametrów modelu prowadzi do rozmycia oraz wzrostu błędu modelu. Przy 95% poziomie ufności wyznaczono przedziały ufności dla najlepszych modeli I, II oraz VI. Ponadto model II wykazał więcej dyskretnych obszarów w odniesieniu do prędkości flotacji i uzysku, niż model VI. Wskazuje to na lepszą zdolność tych modeli do opisu zmian w procesie flotacji.

3

Corrosion inhibition of iron by polystyrene polymeric nanofibers

Abdel-Aziz A., Saleh A. M., Klingner A.

Ochrona przed Korozją

|

2010

|

nr 12

663-665

EN

Recently, nanofibers and their applications have received a significant interest particularly in coating purposes. The aim of this paper is to modify surface properties of materials using polymeric nanofibers. Nanofibers were deposited on iron surface by electrospinning. Electrospinning is a relatively simple and efficient technique to produce submicron to nanometer fibers from solutions of polymers. In our case polystyrene (PS) was used. Different tests such as scanning electron microscopy (SEM) and contact angle were conducted to characterize the nanofibers. Corrosion behaviour of iron covered with different amount of nanofibers indicated by deposition time was measured in 3.5% NaCl solution. The stability of the passive nanofibers layer was investigated using Tafel polarization curves and potential cyclic measurements. The results were compared with non-coated iron and iron coated with casted polymeric film. An increase of the corrosion resistance was recorded as transition from partially covered film to complete coverage. Complete and full compact layer of PS fibers was achieved after 20 min. of deposition. Therefore, no pitting attack and excellent corrosion resistance with inhibition efficiency 98.8% was obtained.

PL

W ostatnim czasie zwiększyło się zainteresowanie nanowłóknami oraz możliwościami ich stosowania, szczególnie w materiałach powłokowych. Niniejsza publikacja przedstawia w jaki sposób można wpływać na właściwości powierzchni różnych materiałów dzięki zastosowaniu nanowłókien polimerycznych. Nanowłókna osadzono na powierzchni żelaza metodą elektrospinningu. Jest to stosunkowo prosta i skuteczna technika umożliwiająca wytworzenie w skali submikronowej i nanometrycznej włókien z roztworów polimerów. W naszym przypadku był to roztwór polistyrenu (PS). Charakterystyki nanowłókien dokonano stosując skaningową mikroskopię elektronową (SEM) oraz pomiar kąta zwilżania. Zachowanie korozyjne żelaza pokrytego różną ilością nanowłókien, wynikających z czasów osadzania, badano w 3,5% roztworze NaCl. Stabilność pasywnych warstw nanowłókien zbadano stosując krzywe polaryzacji Tafela oraz pomiary cyklicznej polaryzacji. Otrzymane wyniki porównano z tymi dla żelaza o niemodyfikowanej nanowłóknami powierzchni oraz dla żelaza z laną warstwą polimeru. Odnotowano zwiększoną odporność na korozję przy przejściu od częściowo do całkowicie pokrytej nanowłóknami powierzchni. Całkowita i zwarta warstwa włókien PS powstawała po 20 minutach osadzania. Tak więc uzyskano brak korozji wżerowej oraz znakomitą odporność na korozję o wydajności inhibicji 98,8%.

4

An attempt to improve mechanical properties of brick produced from El-Maghara coal washing plant waste

Ramadan A. M., Saleh A. M., Taha T. A., Moharam M. R.

Physicochemical Problems of Mineral Processing

|

2001

|

Vol. 35

153-160

EN

Treatment of wastes became a vital demand to maintain the environment as clean as possible . The treatment of wastes and reuse of their constituents in industry will be helpful for this trend as well as for economy. Flotation technique is one of the important separation techniques that can be applied for treatment of wastes efficiently. The filter cake of El-Maghara coal washing plant was one of these wastes which contains a considerable amount of clay. This filter cake was treated in a previous work by flotation in order to clean it from the contained fine coal. The residual clay was tested as a raw material to produce brick models with acceptable mechanical properties. Improvement of the mechanical properties of such brick models by mixing such clay with sand is exactly the main objective of this work. The effect of different factors such as, weight percent of sand and its particle size on the mechanical properties of the brick models was investigated. It was found that 20 % and 60 % of sand sample characterized by size distribution of - 1500 + 0 žm and - 500 + 0 žm respectively are enough to achieve a considerable extent of improvement in the mechanical properties of the clay brick produced.

PL

Poprawa mechanicznych właściwości cegieł wykonanych z mułu węglowego przez dodanie piasku, stanowiła główny cel badań. Wpływ takich parametrów jak zawartość piasku, skład ziarnowy na właściwości mechaniczne produkowanych cegieł był badany. Zostało ustalone, że obecność 20% piasku o uziarnieniu –1500 žm oraz 60% piasku o uziarnieniu –500 žm pozwala na wyraźną poprawę mechanicznych właściwości produkowanych cegieł.