As demonstrated in recent years, one of the major factors of oxidative stress, generated in the circulatory system, in both acute and chronic pathological conditions, is peroxynitrite (ONOO –) [4]. Peroxynitrite is a strong biological oxidant and nitrating compound, generated in vivo from a rapid reaction of two relatively less reactive, but commonly found, of free radicals: nitrogen monoxide (NO ) and superoxide (O2–) [8]. This reaction occurs spontaneously and is not catalyzed by any enzyme. A fundamental reaction of ONOO – in biological systems is its fast reaction with carbon dioxide (k = 5,7 ź 104 M–1 s–1) and yields a short-lived intermediate, nitrosoperoxycarbonate (ONOOCO 2 –), which homolyzes leads to the formation of carbonate (CO 3–) and nitrogen dioxide (NO 2) radicals (yield ~35%) [29, 30] (Fig. 1), which are one-electron oxidants. ONOO – is responsible for oxidative modifications in a wide variety of biomolecules and is capable to induce of nitrative changes in sulfur and aromatic amino acids, especially 3-nitrotyrosine and dityrosine formation [17] (Fig. 2). This article describes the formation, reactivity and biological action of peroxynitrite.

2

Odkształceniowe zachowanie monokryształów stopu aluminium Al-1%Mn

Wajda W., Bijak M., Paul H., Madej Ł. Ł., Trębacz L.

Rudy i Metale Nieżelazne

|

2007

|

R. 52, nr 11

664-668

PL

Badano wpływ pasmowych niejednorodności odkształcenia na umocnieniowe zachowanie się monokryształów stopu Al-1%Mn odkształcanego w próbie nieswobodnego ściskania. Wybrano orientacje niestabilne: sześcienną-{100}<001>, ścinania-{100}<011> oraz C-{112}<111>. Odkształcenie przeprowadzono w temperaturze pokojowej w matrycy kanalikowej, w kilku etapach, do sumarycznego zgniotu wynoszącego ok. 85 %. Zmiany mikrostruktury i tekstury badano za pomocą mikroskopii elektronowej skaningowej i transmisyjnej i skorelowano je z wynikami symulacji numerycznej z wykorzystaniem Metody Elementów Skończonych

EN

Influence of band-like deformation heterogeneities on hardening behaviour of Al-1wt.%Mn alloy single crystals deformed in plane strain compression was studied in this work. Unstable orientations were chosen: cube {100}<001>, shear {100}<011> and C {112}<111>. Deformation in stages adding up to 85 % has been carried out in channel-die device in ambient temperature. Changes of microstructure and texture have been observed with scanning electron microscopy and transmission electron microscopy and were correlated with results from numerical simulations using Finite Element Method.

3

Deformation and recrystallization behaviour of Al-1wt.%Mn alloy single crystals with unstable initial orientations

Bijak M., Paul H.

Inżynieria Materiałowa

|

2007

|

Vol. 28, nr 3-4

364-369

EN

The nucleation of recrystallized grains in deformed Al-lwt.%Mn alloy was examined in relation to the microstructural heterogeneities characteristic of specific grain orientations. The experiments concerned single crystals with unstable orientations of C{112}<111>, shear{100}<011> and cube{100}<001> deformed to strains of about 85% in channel-die plane strain compression at room temperature. The character of the bands and the new grain orientations were determined by systematic local orientation measurements in scanning electron microscopy (SEM) equipped with field emission gun (FEG) and electron backscattered diffraction (EBSD) facilities. During deformation the band-like strain inhomogeneities modify global texture by rotation towards characteristic texture components specific of particular crystallites. The shear bands developed within C oriented grains tend to rotate towards {100}<011>. Very strong deformation banding observed in the cube grain gives an initial orientation rotation about (+/-) TD towards {110}<011>. The shear orientation breaks up by deformation banding creating (+/-) TD rotated slices separated by transition bands which rotate ultimately to two symmetrical {112}<111> orientations. The initial recrystallization growth stage is characterized by new grains which possess orientations misoriented with respect to the orientations identified within the neighbouring deformed state by rotation around <112>, <111>, <110> and <123> axes. In most observed cases the migration of the newly formed grain boundaries occurred by mechanism linked to dislocation movement on the {111} planes, the most active in the deformation process.

PL

Monokryształy Al-l%wag. Mn o trzech różnych orientacjach początkowych: C{112}<111>, ścinania{100}<011> i sześciennej{100}<001> ściskano nieswobodnie do sumarycznych odkształceń ok. 85%, a następnie wyżarzano w celu uzyskania stanu częściowej rekrystalizacji. Naturę procesu formowania się określonych niejednorodności odkształcenia oraz związki krystalograficzne w początkowych stadiach rekrystalizacji analizowano z użyciem mikroskopii orientacji. Analizowano najbardziej typowe relacje orientacji pomiędzy nowymi ziarnami a ich zdeformowanym sąsiedztwem wynikające z rotacji dookoła selektywnie wybranych osi typu <112> oraz <111> ze zróżnicowanymi wartościami kąta dezorientacji. Dodatkowo wskazano na możliwość formowania się bardziej złożonych relacji wynikających z rotacji dookoła osi <110>, <221> i <123>, które zinterpretować można jako złożenie obrotów dookoła osi typu <112>.

4

Large strain deformation substructures and local crystallography in {100}<001>/{110}<001> aluminium bicrystals

Paul H., Driver J. H., Maurice C., Bijak M.

Archives of Metallurgy and Materials

|

2006

|

Vol. 51, iss. 1

43-53

EN

Symmetrically oriented bicrystals of pure Al(99.998%) have been deformed in channel-die compression up to strains of 1.5 to correlate the dislocation substructures and the slip system distributions. The study has focused on structure development in f100g<001>/f110g<001> (cube/Goss) – oriented bicrystals with the grain boundary situated parallel to the compression plane. Both orientations have the same nominal Taylor factor and deform macroscopically by the same amount but have stable (Goss) and unstable (cube) micro-deformation behavior. The character of the deformation substructure was determined by systematic local orientation measurements using high resolution EBSD in a SEM-FEG scanning electron microscope and also by transmission electron microscopy (TEM) and the CBED technique at specific locations. The bicrystal deformation analysis shows that the microtexture evolution within neighboring grains is quite different. Very strong deformation banding is observed within crystallites with the unstable orientation, i.e. cube-oriented grain forms classical deformation bands of slightly and strongly dislocated areas. The Goss-oriented grains within bicrystals are more stable under plane strain conditions and do not show any tendency to strain inhomogeneties except for the zone near the grain boundary.

PL

W pracy analizowano umocnieniowe zachowanie się bikryształów Al(99.998%) o orientacji krystalitów {100}<001>/ {110}<001>, odkształcanych w próbie nieswobodnego ściskania do zakresu odkształceń ∼1.5. Granica rozdziału pomiędzy ziarnami usytuowana była równolegle do płaszczyzny ściskania. Obydwa krystality formujące bikryształ scharakteryzowane są tą samą wartością współczynnika Taylora. Jednakże ich zachowanie umocnieniowe jest odmienne, tj. orientacja {110}<001> pozostaje stabilna podczas gdy {100}<001> jest silnie niestabilna. W oparciu o pomiary orientacji lokalnych w TEM a także z wykorzystaniem techniki EBSD w SEM wyposażonym w działo o emisji polowej dokonano charakterystyki mikrostrukturalnej i tekturowej. W krystalicie o orientacji {100}<001> obserwowano formowanie się pasm odkształcenia złożonych z obszarów o wysokiej i niskiej gęstości dyslokacji. Orientacja G{110}<001> pozostawała stabilna nie przejawiając tendencji do formowania pasmowych niejednorodności odkształcenia za wyjątkiem wąskich obszarów w pobliżu granicy pomiędzy ziarnami.

5

Crystal lattice rotation in channel-die deformed al bicrystals with {100}<001>/{100}<011> AND {100}<001>/{110}<001> orientations

Paul H., Litwora A., Bijak M.

Inżynieria Materiałowa

|

2004

|

R. XXV, nr 3

540-544

EN

The issues of band-like inhomogeneties of deformed structure and the evolution of their microtexture components are addressed. The analysis is based on bands development by plane strain compression in {100}<001>/{100}<011> and {100}<001>/{110}<001> oriented high purity aluminium bicrystals with boundary planes situated nearly perpendicular to the compression plane. Substantial progress in understanding the character of these bands was possible due to systematic local orientation measurements using scanning electron microscopy (SEM) equipped with field emission gun (FEG). Goss {110}<001> oriented grains are stable within the range of applied deformations whereas the 'cube' {100}<001> and 'shear' {100}<011> grain orientations are very unstable under plane strain conditions and develop band-like inhomogeneities of deformation.

PL

W pracy analizowano formowanie się niejednorodności odkształcenia oraz ewolucję ich wewnętrznej mikrotekstury. Badania prowadzono na bikryształach aluminium o układzie orientacji {100}<001>/{100}<011> i {100}<001>/{110} <001> z granicą ziaren usytuowaną równolegle do płaszczyzny ściskania. Opisu dominujących systemów poślizgu odpowiedzialnych za obserwowane tendencje rotacji sieci krystalicznej dokonano w oparciu systematyczne pomiary orientacji w mikroskopie skaningowym wyposażonym w działo o emisji polowej. Ziarna o orientacji 'goss'{110}<001>są stabilne w szerokim zakresie odkształceń podczas gdy krystality o orientacjach 'cube'{100}<001> oraz 'shear' {100}<011>są silnie niestabilne w próbie nieswobodnego ściskania i sprzyjają rozwojowi pasmowych niejednorodności odkształcenia.

6

Stres w pracy zawodowej a zagrożenie stanu zdrowia osób z przewlekłymi chorobami układu krążenia i przemiany materii

Nazar K., Kaciuba-Uściłko H., Wójcik-Ziółkowska E., Kruk B., Pawłowska-Jenerowicz W., Bijak M., Kodrzycka A., Krzysztofiak H., Niewiadomski W., Cybulski G.

Bezpieczeństwo Pracy : nauka i praktyka

|

2001

|

nr 3

6-9

PL

Stres w pracy zawodowej jest czynnikiem ryzyka nadciśnienia tętniczego i choroby niedokrwiennej serca. Sprzyja też rozwojowi cukrzycy i otyłości. Słabo znany jest wpływ obciążeń psychospołecznych na stan zdrowia systematycznie leczonych pacjentów z przewlekłymi chorobami układu krążenia i przemiany materii. W badaniach własnych, którymi objęto pacjentów wykonujących zawodowo pracę wymagającą podejmowania odpowiedzialnych decyzji, koncentracji uwagi i powodującą napięcie emocjonalne, wykazano (na podstawie 24-godzinnych zapisów EKG i ciśnienia tętniczego) występowania znacznych wzrostów ciśnienia tętniczego, arytmii serca i epizodów niedokrwienia mięśnia sercowego, pomimo regularnego przyjmowania leków. Zmiany występowały częściej w czasie dni pracy określanych przez badanych jako stresogenne. U chorych na cukrzycę stwierdzono podwyższone stężenie glukozy we krwi w godzinach największej aktywności zawodowej.

EN

Job strain is a risk factor for hypertension and coronary heart disease. It can also contribute to the development of diabetes and obesity. Little is known about the effect of psycho-social factors and especially occupational stress on the health status of regularly medicated patients with chronic cardiovascular and metabolic diseases. An analysis of 24-hour registration of ECG and blood pressure in patients engaged in jobs with high mental demands and extensive responsibility showed that during „stressful” days in many of them large increases in blood pressure, ischemic changes in ECG, cardiac arrhythmias occurred in spite of pharmacological treatment. Some diabetic patients also showed high levels blood glucose during the most active part of the working day.