The structure of intermediate layers of hot-dipped Al-Zn coatings on carbon steel sheets

Hamankiewicz M., Król J., Tałach-Dumańska M., Dutkiewicz J.

Archives of Metallurgy and Materials

|

2006

|

Vol. 51, iss. 3

503-509

EN

The high efficient method to protect the steel sheets is an Al-Zn coating by hot – dipping. Good properties of the coatings layer were obtained from the baths of Al-Zn alloys with silicon addition. Three baths were used: AlZn44Si1, AlZn43Si2 and AlZn42Si3 at the temperatures 630 and 670C in different dipping times between 15 to 180 s. The optical, scanning microscopy and XRD analysis were applied. The best layers were obtained from the AlZn43Si2 bath in which the reaction zone was very thin. The main phases formed as a result of the reactions in diffusion zone were identified as: Al20Fe5Si2, Al5Fe2and Al13Fe4.

PL

Zastosowanie pokrywania blach stalowych metodą zanurzeniową w kąpielach aluminiowo-cynkowych jest wydajną metodą stosowana dla ich ochrony przed korozją. Wysokie własności pokryć uzyskano w kąpielach aluminiowo-cynkowych przy zastosowaniu dodatku krzemu. Badania prowadzono dla kąpieli o składach: AlZn44Si1, AlZn43Si2 i AlZn42Si3 dla temperatur 630 i 670C i różnych czasów zanurzania od 15 do 180 sek. Badania prowadzono metodami: mikroskopii optycznej i skaningowej oraz rentgenowskiej analizy fazowej. Najlepsze warstwy uzyskano w kąpieli AlZn43Si2 uzyskując bardzo cienkie warstwy reakcyjne. Podstawowymi fazami wygenerowanymi na drodze reakcji w warstwie dyfuzyjnej były: Al20Fe5Si2, Al5Fe2 i Al13Fe4.

2

Influence of intermetallic compounds on grain refinement in 2XXX alloys after different thermomechanical treatment

Król J., Tałach-Dumańska M., Socjusz-Podosek M.

Archives of Metallurgy

|

2003

|

Vol. 48, iss. 4

407-420

EN

Fine equiaxial grain structure is a consequence of designing a material with a large contribution of intermetallic compounds of certain size and distribution. A 2XXX alloy with Fe, Ni, Mn and Zr additions was cast obtaining large amounds of Al-Fe-Ni and Al-Cu-Mg precipitates, in which the Al-Zr compounds appeared as dispersoids. After the application of a modified thermomechanical procedure, an alloy with average grain size 12 microm with a large contribution of grains smaller than 10 microm has been obtained. Apart from that, elongated precipitates of 0.8-4.0 microm in size as well as globular ones about 0.3 microm large were produced in the alloy after recrystallization. The alloy revealed high resistance to grain growth at high temperatures, which was due to the apperance of intermetallic compounds (mostly Al-Fe-Ni) in grain boundaries.

PL

Wytworzenie struktury o drobnym, równoosiowym ziarnie jest związane głównie z uzyskaniem stopu o znacznym udziale wydzieleń związków miedzymetalicznych o określonej wielkości i rozłożeniu. W tym celu odlano stop typu 2XXX z dodatkami żelaza, niklu i manganu oraz cyrkonu, uzyskując znaczne ilości zwiazków Al-Fe-Ni oraz Al-Cu-Mg. Dodatek cyrkonu tworzył dyspersoidy typu Al3Zr. Po zastosowaniu odpowiednio zmodyfikowanej obróbki termomechanicznej uzyskano stop w stanie po rekrystalizacji o średniej wilekości ziarna ok. 12 mikrom z dużym udziałem ziarn poniżej 10 mikrom i wydzieleń o kształtach wydłużonych wielkości 0.8-4 mikrom oraz globularnych ok. 0.3 mikrom. Stop ten charakteryzował się wysoką odpornością na wzrost ziarna w wysokich temperaturach, co zawdzięczał obecności wydzieleń związków międzymetalicznych Al-Fe-Ni zlokalizowanych głównie na granicach ziarn.

3

Wpływ nadplastycznych właściwości stopu typu 7475 na odkształcenie w procesie formowania ciśnieniem gazu.

Król J., Tałach-Dumańska M., Malczewski P.

Inżynieria Materiałowa

|

2002

|

R. XXIII, nr 2

61-65

PL

Proces odkształcenia nadplastycznego znajduje coraz częściej zastosowanie w przemyśle pozwalając na wytwarzanie elementów o złożonych kształtach w jednej tylko operacji, co prowadzi do oszczędności czasu pracy i energii. Podstawą jest określenie parametrów obróbki prowadzącej do uzyskania stopu w stanie nadplastycznym oraz wyznaczenie optymalnych parametrów odkształcenia nadplastycznego, uzyskiwanych na drodze badań laboratoryjnych. Stop typu 7475 w stanie nadplastycznym pozwala na uzyskanie wysokich odkształceń przy niskich naprężeniach płynięcia, co umożliwia zastosowanie go do produkcji elementów o złożonych kształtach metodą pneumatyczną. Stop typu 7475 był odlewany metodą ciągłą, odkształcany metodą wyciskania i obrabiany w procesie termomechanicznym. W wysokotemperaturowych próbach rozciągania określono optymalne parametry odkształcenia nadplastycznego: odpowiednio temperaturę i szybkość odkształcenia wynoszące: 813 K i 2,8 x 10 do -4 s do -1. Z blach tak przygotowanego stopu wykonano metodą pneumatyczną (z zastosowaniem argonu), wyznaczywszy uprzednio optymalny przebieg wzrostu ciśnienia, wypraski w kształcie kopuł o średnicy 100 mm i wysokości 50 mm stosując ciśnienia do 0,8 MPa. Stop po odkształceniu nadplastycznym i dwustopniowej obróbce cieplnej typu T76 wykazywał wysoką wytrzymałość przy dobrej plastyczności, odpowiednio: Rm=529 MPa i A5=9,85%. Powyższy wynik w odniesieniu do danych z literatury technicznej należy uznać za zdecydowanie dobry.

EN

The superplastic deformation process is nowadays more and more frequently applied in the industry as one enabling the production of elements of complicated shapes in single operation and saving time and energy. Establishing the proper parameters of thermomechanical treatment and conditions of superplastic deformation, is essential to obtain the desired superplastic structure. The pneumatic method (gas - forming) was used to produce elements of complicated shape from the 7475 type alloy in superplastic state (highly deformable at low flow stress). The 7475 alloy was continuously cast, extruded and thermomechnically treated, after which the fine-grained, superplastic structure with Al3Zr dispersoids was formed. The most favoured parameters of the superplastic deformation were determined in the high-temperature tension test: temperature of 813 K and deformation rate equal 2.8 x 10 to the -4 s to the -1. Using gas forming method domes of the 100 mm diammeter and 50 mm high at pressure up to 0.8 MPa, were produced from the superplastic sheets, at 813 K. Ealier, the dependence of the optimal increase of the pressure in time was determined. The domes show very good projection of the mould but with thickness decreasing from the bottom to the pole. The increase of cavitation effect in the thinned zones was observed. After the superplastic deformation and two-step thermal treatment of the T76 type the investigated alloy revealed high strength Rm=529 MPa and plasticity: As=9.85%. These results are satisfying regarding the data from the literature.

4

The superplstic state in A7475 alloy related to the structure and mechanical properties

Król J., Tałach-Dumańska M.

Archives of Metallurgy

|

2002

|

Vol. 47, iss. 1

17-26

EN

The superplastic deformation process is interesing not only from scientific point of view but also because of benefits it offers when appied in industry. The generation of superplastic structures in aluminium alloys of the 7XXX type depends on the formation of precipitates in suitable amount, size and dispersion which may be obtained by thermomechanical treatment. The A7475 alloy was continuously cast, extruded and thermomechanically treated. The investigations on creating precipitates and microstructure of the AlZnCuMgCr alloy were performed using optical, scanning and transmission electron microscopy and X-ray phase analysis. The morphology of the alloy after a full thermomechanical treatment showed fine, equiaxial average grain about 12 µm in size. The strain rate sensitivity coefficient m determined from tensile tests was estimated between 0.56-0.70. About 495 pct elongation was obtained in a tension test at the flow stress of 3 MPa, strain rate 8x10-3s-1 and temperature 790K. It demonstrates that material of good superplastic properties was elaborated.

PL

Wytworzenie struktury superplastycznej w stopach aluminium typu 7XXX jest zależne od powstania wydzieleń o odpowiedniej wielkości, dyspersji i ilości, co może zostać uzyskane na drodze obróbki termomechanicznej. Stop A7475 odlewany metodą ciągłą i wyciskany, był następnie obrabiany w procesach termomechanicznych. Badania tworzących się wydzieleń i mikrostrukr\tury w stopieAlZnCuMgCr przeprowadzono metodami mikroskopii optycznej, skanningowej i elektronowej oraz rtg. analizy fazowej. Morfologia stopu po pełnej obróbce termomechanicznej charakteryzowała się drobnymi, równoosiowymi ziarnami o wielkości ok. 12 µm. Współczynnik czułości na szybkość odkształcenia określony w teście rozciągania osiągnł wartość m=0,56-0,70. Maksymalne wydłużenie uzyskane w teście rozciągania przy naprężeniu płynięcia ok. 3 MPa, szybkości odkształcenia 8x10-3s-1 i w temperaturze 790K osiągnęło wartość 495%. Świadczy to o uzyskaniu materiału o dobrych własnościach superplastycznych.

5

Characteristics of superplastic state of the 2XXX - type alloy after thermomechanical treatment

Król J., Tałach-Dumańska M., Paul H.

Archives of Metallurgy

|

2002

|

Vol. 47, iss. 4

433-444

EN

The suitable structure of an alloy affects its superplastic properties due to a basic mechanisms of superplastic deformation. A fine structure of equiaxial grains appears in the alloy provided there are dispersoids and intermetallic compounds of certain size and distribution. The composition of the 2XXX - type alloy (with Ni - addition) as well as a special thermomechanical treatment allowed to obtain a suitable structure of 15 microm-grain size and an equiaxial shape. The formation of such microstructure was investigated using optical, scanning and electron microscopy, as well as X-ray phase analysis techniques. The X-ray and electron microscopy with EDAX analyser allowed to deterniine the type and morphology of the intermetallic cornpounds, very important to generation the fine-grained structure. The superplastic state regarding quality of the structure was verified in tensile tests performed at the range of deformation rates between 1.4 x 10-4 to 7 x 10-3s-1 and at temperatures from 789 K to 839 K, which allowed to attain the elongation above 300% and strain rate sensitivity coefficient m = 0.509.

PL

Podstawowy mechanizm odkształcenia nadplastycznego, poslizg po granicach ziarn, jest ściśle związany ze strukturą i własnościami nadplastycznymi stopu. Wygenerowanie drobnokrystalicznej, równoosiowej struktury w badanym stopie jest związane z obecnością w nimdyspesoidów i związków międzymetalicznych o okreslonej ilości, wielkości i rozłożeniu. Tak skład stopu jak i okreslona obróbka termomechaniczna pozwoliły na otrzymanie struktury o średniej wielkości ziarna ok. 15 mikrom.i równoosiowym kształcie. Badania strukturalne stopu prowadzono z zastosowaniem optycznej, skanningowej i elektronowej mikroskopii oraz rtg. analizy fazowej. metody rtg. analizy fazowej oraz elektronowej mikroskopii z analizatorem EDAX pozwoliły na okreslenie typu i morfologii związków międzymetalicznych istotnych do wytworzenia drobnoziarnistej struktury stopu. Jakość struktury stanu nadplastycznego, weryfikowana w próbach rozciągania przeprowadzonych w temperaturach od 789K do 839K i przy szybkościach odkształcenia od 1.4 x 10-4 to 7 x 10-3s-1, pozwoliła na uzyskanie wydłużenia powyżej 300% i współczynnika czułości na szybkość odkształcenia m=0.509.