Use Of Pulsed IR Thermography For Determination Of Size And Depth Of Subsurface Defect Taking Into Account The Shape Of Its Cross-Section Area

Wysocka-Fotek O., Maj M., Oliferuk W.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 2A

615--620

The paper is devoted to reconstruction of size and depth (distance from the tested surface) of artificial defects with square and rectangular cross-section areas using the pulsed IR thermography. Defects in form of flat-bottom holes were made in austenitic steel plate. The defect size was estimated on the basis of surface distribution of the time derivative of the temperature. In order to asses the depth of defects with considered geometries on the basis of calibration relations (i.e. dependence of time of contrast maximum vs. defect depth for given defect diameter) obtained for circular defects, the ‘equivalent diameter’ describing not only the defect cross-section area but also its shape was assigned. It has been shown that presented approach gives satisfactory results.

Praca dotyczy wyznaczania wielkości i głębokości (odległości od badanej powierzchni) symulowanych defektów o przekroju kwadratowym i prostokątnym przy użyciu impulsowej termografii podczerwieni. Defekty, w formie nieprzelotowych otworów o płaskim dnie, wykonano w blasze ze stali austenitycznej. Wielkość defektów określano analizując powierzchniowy rozkład pochodnej temperatury względem czasu. Aby wykorzystać zależności kalibracyjne (zależności czasu odpowiadającemu maksimum kontrastu temperatury od głębokości defektu o danej średnicy) dla defektów o przekroju kołowym do oszacowania głębokości defektów kwadratowych i prostokątnych, przyporządkowano im „ekwiwalentną średnicę” uwzględniającą nie tylko pole przekroju defektu, ale także kształt defektu. Pokazano, że dla rozpatrywanych geometrii defektów, zaproponowane podejście daje satysfakcjonujące rezultaty.

Use of pulse IR thermography for detection and quantitative description of subsurface defects in austenitic steel

Wysocka-Fotek O., Oliferuk W., Maj M.

Rudy i Metale Nieżelazne

2009

R. 54, nr 11

684-687

Pulsed IR thermography is a non-destructive method that allows detection of subsurface defects in material. In this method the surface of the tested specimen is stimulated by heat pulse and its self-cooling process is analyzed. The temperature decrease rate is different for surface over defect with comparison to that over the sound material. It is caused by difference between values of heat diffusivity of defected zone and sound one. The purpose of this work is to determine the size and depth of the defects in austenitic steel on the basis of thermal contrast analysis. Because the thermal contrast is dependent on both these parameters, two independent experimental methods of defect size and depth determination were proposed.

Termografia impulsowa jest nieniszczącą metodą badań, stosowaną do wykrywania defektów w warstwie podpowierzchniowej materiału. Polega ona na analizie rozkładu temperatury na powierzchni badanego materiału podczas jej stygnięcia po nagrzaniu impulsem cieplnym. Szybkość stygnięcia obszaru powierzchni nad defektem jest różna w porównaniu z szybkością stygnięcia powierzchni materiału jednorodnego. Jest to spowodowane różnicą pomiędzy wartościami dyfuzyjności cieplnej wymienionych obszarów. Celem pracy jest oszacowanie wielkości i głębokości defektu w stali austenitycznej na podstawie analizy kontrastu termicznego. Kontrast termiczny zależy od tych dwóch parametrów, dlatego w pracy zaproponowano dwie niezależne metody eksperymentalne ich szacowania.