Ability of a Cellobiohydrolase I+II Mixture and Endoglucanase of the Trichoderma reesei Strain to Change Lyocell Fibres

Öztürk H. B., Ehrhardt A., Vu-Manh H, Oksanen T., Široká B, Suurnakki A, Bechtold T.

Fibres & Textiles in Eastern Europe

2011

Vol. 19, no. 5 (88)

23--27

Lyocell fibers were treated for 24 h with two different types of cellulase enzymes, endoglucanase (EG) and a mixture of cellobiohydrolases (CBH I+II) from the Trichoderma reesei strain. After treating the fibers with 0.5 and 2 mg/g of EG and 2 mg/g of CBH, the fiber surface was damaged (observed by optical microscope), the fibers became brittle, and hence mechanical properties such as the tensile strength, elongation at break and abrasion resistance decreased. The weight loss (WL) test using 6 % NaOH alone, 4 % urea alone and their mixture showed that the WL of the fibers was not affected by the enzymatic treatments. The moisture regain, degree of polymerisation, crystallinity index, measured by ATR (attenuated total reflectance), and the FTIR of the enzyme treated fibers also did not change.

Włókna lyocell poddano 24 godzinnej obróbce dwoma różnymi rodzajami enzymów celulazy, endoglukonazy (EG) i mieszaniną celobiohydrolazy (CBH I+II) uzyskanych ze szczepu Trichoderma reesei. Po poddaniu włókien działaniu 0.5 i 2 mg/g EG oraz 2 mg/g CBH powierzchnia włókien została uszkodzona, co zaobserwowano mikroskopem optycznym, włókna stały się bardziej kruche a ich mechaniczne właściwości takie jak wytrzymałość na zerwanie i wydłużenie przy zerwaniu zmniejszyły się podobnie jak wytrzymałość na ścieranie. Stwierdzono brak utraty masy przy teście z użyciem 6% NaOH, 4% mocznika i ich mieszaniny. Również nie zmieniły się właściwości wchłaniania wilgoci, stopień polimeryzacji, indeks krystaliczności mierzone za pomocą ATR, jak i widma FTIR włókien potraktowanych enzymami.

Effect of NaOH Treatment on the Interfibrillar Swelling and Dyeing Properties of Lyocell (TENCEL®) Fibres

Öztürk H. B., Bechtold T.

Fibres & Textiles in Eastern Europe

2007

Vol. 15, no. 5-6 (64)

114--117

The effect of interfibrillar swelling on swelling degree, carboxyl content, split number, weight loss and dyeing properties by using NaOH solution up to 2.5 M concentration of lyocell fibres was investigated. The Split number and weight loss show the behaviour of fibres during alkali treatment, whereas the water retention value (WRV), carboxyl content and dyeing give information about the properties of samples after alkali treatment. By increasing alkali concentration, the swelling degree, weight loss, split number, total colour difference and K/S values of fibres increased when compared to untreated samples; on the other hand carboxyl content decreased.

Badano wpływ międzyfibrylarnego pęcznienia na stopień spęcznienia, zawartość grup karboksylowych, liczbę rozszczepień, stratę masy i właściwości barwienia przy stosowaniu roztworów NaOH o stężeniu do 2.5 M do obróbki włókien typu Lyocell. Liczba rozszczepień i strata masy charakteryzują zachowanie się włókien podczas obróbki alkaliczne, podczas gdy wartość retencji wody i zawartość grup karboksyloeyvj, jak również barwienie dostarczają informacji o właściwościach próbki po obróbce alkalicznej. Przy wzroście stężenia alkalii, wzrastały również stopień spęcznienia, strata masy, liczba rozszczepień, całkowita różnica wybarwienia i wartość K/S obrabianych włókien, w stosunku do próbek nie obrabianych, natomiast ilość grup karboksylowych zmniejszała się.