Modifcation of PA 6 Fibres with Bentonite, Cloisite and Concentrates (Copolyamide + Bentonite)

Krištofč M., Ujhelyiová A., Vassová I., Ryba J.

Fibres & Textiles in Eastern Europe

|

2011

|

Vol. 19, no. 1 (84)

24-29

EN

This contribution outlines the preparation and properties of PA 6 fbres modifed with two types of montmorillonite - organophilic Bentonite 11958 or Cloisite 15A alone, as well as with concentrates consisting of copolyamides and Bentonite. The concentrates were synthesised with ?-caprolactam (CL) and two minor comonomers - nylon salts from adipic acid + diethylenetriamine (ADETA) and from adipic acid + 1-(2-aminoethyl) piperazine (AN2) in the presence of Bentonite. Three concentrates containing copolyamide from CL + 10.7 wt. %, 21.4 wt.% and 23.4 wt.% of minor comonomers + 5 wt.% of Bentonite were prepared. The basic properties of PA 6 and the concentrates were evaluated. Blends PA 6 + 10 - 50 wt.% of each concentrate, PA 6 + 0.25 - 2.5 wt.% of Bentonite and PA 6 + 0.25 - 5 wt.% of Cloisite were prepared, and the apparent viscosity of the blend melts with Bentonite was measured. Experimental PA 6 fbres modifed with Bentonite, Cloisite and the concentrates were prepared and drawn. The mechanical properties - tensile strength, elongation at break and Young's modulus of non-modifed and modifed PA 6 fbres were compared.

2

Mechanical Properties of PA 6 Fibres Modified with Copolyamides and Nanoclays

Kristofič M, Ujhelyiová A, Vassová I, Michlík P, Brejka O, Ryba J

Fibres & Textiles in Eastern Europe

|

2011

|

Vol. 19, no. 4 (87)

41—45

EN

This contribution deals with the preparation of concentrates consisting of copolyamides from ε-caprolactam and nylon salts prepared from adipic acid and 1-(2-aminoethyl) piperazine, and from adipic acid and diethylenetriamine, as well as the evaluation of their basic properties. PA 6 fibres modified with 5, 10 and 20 wt. % of these concentrates were prepared by two drawing processes, and their mechanical properties,( tensile strength, Young modulus and elongation at break) and orientation factors were evaluated. With respect to their thermal properties, all the concentrates are more or less semicrystalline compounds suitable as additives for semicrystalline PA 6 fibres. Mechanical properties depend on the type of concentrate and conditions of the drawing process. A lower amount of concentrate in modified fibres and concentrates with a lower amount of comonomers in copolyamide, Cloisite nanoadditive, a lower speed of drawing and an optimal drawing ratio assure the same or better mechanical properties, mainly the tensile strength, in comparison with non modified PA 6 fibres.

PL

Opisano sporządzanie koncentratów opartych na poliamidzie otrzymanym z ε-kaprolaktamu i kwasu nylonowego oraz 1-(2-aminoetylenu) piperazyny, kwasu adypinowego i dietylenotriaminy oraz badano ich właściwości. Wyprzędziono przy zróżnicowanym rozciagu włókna poliamidowe z udziałm 5, 10 i 20% wyżej wspomnianego koncentratu a nastęnie okreśono ich włściwości mechaniczne (wytrzymałść właściwą wydłżenie przy zerwaniu, moduł oraz współczynnik orientacji. Wszystkie koncentraty są mniej lub bardziej krystaliczne i mogą być stosowane do otrzymywania częściowo krystalicznych włóien PA6. Właściwości mechaniczne zależą od ilości dodanego koncentratu oraz parametrów procesu rozciągania. Niższa ilość koncentratu i koncentraty o mniejszej ilości komonomeru w kopoliamidzie, dodatek Cloisite, niższą prędkość rozciągania i optymalny stopień rozciąu zapewniają takie same lub lepsze właściwości (głónie wytrzymałść właściwą w stosunku do włókien niemodyfikowanych.

3

Functionalisation of Polypropylene. Part I. Mechanical, Electric and Sorptive Properties of PP Fibres Modifed with Concentrates Consisting of Copolyamides and Nanoclay

Krištofč M., Vassová I., Ujhelyiová A., Ryba J.

Fibres & Textiles in Eastern Europe

|

2011

|

Vol. 19, no. 2 (85)

18-22

EN

Concentrates of copolyamides consisting of copolyamide (?-caprolactam + nylon salt of adipic acid and diethylenetriamine and nylon salt of 1-(2-aminoethyl) piperazine and adipic acid) and the nanoadditive Bentonite were prepared, characterised and used for the preparation of blend polypropylene (PP) fbres. PP fbres modifed with 4, 8 and 12 wt.% of the three types of concentrates prepared were spun without a compatibiliser by the standard melting process and drawn at three drawing ratios. Mechanical properties of the modifed PP fbres, i.e. tenacity and Young´s modulus, are better mainly at lower amounts of each concentrate and at higher drawing ratios. Te electric properties of the modifed PP fbres are positively infuenced by all three concentrates. Te higher their amount in the modifed PP fbres, the better the electrostatic properties. Te sorptive properties of the modifed PP fbres, i.e. the sorption of water vapour and disperse dyestufs, are much better in comparison with non modifed PP fbres.

4

PA 6/Copolyamide/Layered Silicate Fibres

Krištofič M., Dulíková M., Vassová I., Ryba J.

Fibres & Textiles in Eastern Europe

|

2007

|

Vol. 15, no. 5-6 (64)

34--36

EN

The modification of PA 6 fibres with macromolecular modifiers in order to improve their sorptive and electric properties was studied. Modifiers consisting of binary, high molecular, semicrystalline copolyamides (from ε-caprolactam as a major component and 5, 17 and 30 wt.% of nylon salt from adipic acid + diethylenetriamine) and PA 6 homopolyamide were synthesised in the presence of nanoadditive montmorillonite, and the basic characteristics of the modifiers were evaluated. Synthesised modifiers of 10, 20, 30 and 50 wt.% were used for the preparation of blended M/F poly-ε-caprolactam/modifier fibres and the fibres´ properties were evaluated. The electric and sorptive properties of PA 6 fibres modified with modifiers containing montmorillonite were improved; their tensile strength (mainly with lower amount of modifiers) decreased only negligibly.

PL

Analizowano modyfikację włókien PA6 makromolekularnymi modyfikatorami w celu polepszenia właściwości sorpcyjnych i elektroprzewodzących włókien. Po określeniu podstawowej charakterystyki modyfikatorów, modyfikatory składające się z binarnych wysokomolekularnych półkrystalicznych kopoliamidów (z ε-kaprolaktamem jako głównym składnikiem oraz 5, 17 lub 30 %wt solą nylonową kwasu adypinowego dwu-etyleno triaminy) syntetyzowano wraz z homopoliamidem PA6 w obecności nanododatku w postaci montmorylonitu. Syntetyzowane modyfikatory w ilościach 10, 29, 30 i 59 %wt brano dla przygotowania mieszanek włókien poli-ε-kaprolaktam/modyfikator. Następnie określano właściwości sorpcyjne i elektroprzewodzące otrzymanych włókien PA6 modyfikowanych modyfikatorem zawierającym montmorylonit. Wyniki testów wskazują, że właściwości te zostały polepszone a wytrzymałość na zerwanie zmniejszyła się tylko nieznacznie. (zwłaszcza dla włókien z niższymi zawartościami modyfikatora).

5

Modification of PA 6 by Comonomers and Layered Silicate

Krištofič M., Karabcová N., Alexy P., Ryba J., Vassová I.

Fibres & Textiles in Eastern Europe

|

2005

|

Vol. 13, no. 6 (54)

33--35

EN

This paper deals with the synthesis of modifiers consisting of co-polyamide with clay prepared from co-monomers, namely from ε-caprolactam (CL) and nylon salt (NS) from adipic acid + diethylenetriamine (ADETA), and montmorillonite (MMT). We present a procedure for evaluating the modifiers’ properties, such as the amount of low molecular compounds (LMC) and the relative viscosity (ηr = ηs/η0) performed in accordance with principles of the five-level two-factor experimental design. Four selected samples were synthesised and their properties were checked.

PL

Artykuł omawia syntezę modyfikatorów, składających się z kopoliamidów z glikolami preparowanymi z komonomerów, takimi jak ε-kaprolaktam, sól nylonowa otrzymana z kwasu adypinowego z dwuetylenotriaminy oraz montmorylonitu. Przedstawiono procedury oceny właściwości modyfikatora, takich jak ilość nisko-molekularnych składników i lepkość względna (ηr = ηs/η0), przygotowanych zgodnie z zasadami pięciopoziomowego, dwuczynnikowego planu eksperymentu. Cztery wyselekcjonowane próbki poddano syntezie, a następnie określono ich właściwości.