In-Compost Biodegradation of PLA Nonwovens

Gutowska A, Jóźwicka J., Sobczak S., Tomaszewski W., Sulak K., Miros P., Owczarek M., Szalczyńska M., Ciechańska D., Krucińska I.

Fibres & Textiles in Eastern Europe

2014

Vol. 22, no. 5 (107)

99--106

Presented in this work are the results of an investigation into the biodegradation of selected nonwoven materials made of commercial poly[(DL)-lactide] – PLA 6252D supplied by Nature Works® LLC, USA. The biodegradation was examined under laboratory conditions, simulating composting by the mass-loss method at constant process parameters: temperature t = 58 ± 2 °C, pH 7 and inoculum humidity W = 52.6%. The nonwovens examined, with a surface density of about 60 g/m2, revealed a varied crystallinity degree in the range of 10.4 - 35.6% and fibre diameter of 8.2 - 10.9 μm. The nonwovens were formed by the spun-bond method from a melt at 211 - 213 °C on a laboratory stand. The commercial PLA 6252D was also examined. The polymer PLA 6252D and nonwoven materials made thereof are entirely biodegradable in the research environment applied, and after 16 weeks of biodegradation weight loss in the materials reaches 100%.

Rozwój wiedzy w obszarze ochrony środowiska oraz rozporządzenia unijne stały się impulsem do ciągłego poszukiwania nowych materiałów, które będą degradowalne w środowisku naturalnym, a tym samym wzrastającą potrzebę wykorzystywania innowacyjnych metod badań ich biorozkładu. W artykule przedstawiono wyniki badań biorozkładu wybranych materiałów włókninowych wytworzonych z komercyjnie dostępnego poli[(DL)-laktydu)] – PLA o symbolu 6251D (Nature Works® LLC, USA). Badania prowadzono w symulowanych warunkach kompostowania laboratoryjnego, metodą wyznaczania ubytku masy w temperaturze 58 ± 2 °C, wilgotności podłoża badawczego 52.6% i przy odczynie środowiska pH 7. Włókniny poddane ocenie biodegradowalności o masie powierzchniowej ok. 60g/m2 charakteryzowały się różnymi stopniami krystaliczności w zakresie 10.4 - 36.5% i średnicami włókien w przedziale 8.2 - 10.9 μm. Formowano je ze stopu techniką spun-bonded w zakresie temperatur 211 - 213 °C. Badaniom biodegradacyjnym poddano również handlowy polimer PLA 6251D.

Impact of PBSA (Bionolle) Biodegradation Products on the Soil Microbiological Structure

Lichocik M., Owczarek M., Miros P., Guzińska K., Gutowska A., Ciechańska D., Krucińska I., Siwek P.

Fibres & Textiles in Eastern Europe

2012

Vol. 20, no. 6B (96)

179--185

An impact of the decomposition products of Poly(butylene succinate adipate) (PBSA) (Bionolle 3001) in the form of polymer chips and nonwovens made of the polymer upon the qualitative and quantitative microbiological profile of the soil in which samples of the materials were incubated was investigated. The mass loss of the polymer and nonwovens as a result of their biodegradation proceeding in the soil was compared. Two kinds of the soil were applied in the biodegradation tests: garden soil and an agriculture soil taken from the experimental field plots of the Agriculture University (AU) of Cracow. The AU soil despite low moisture content is fertile and holds a great amount of microorganisms. The garden soil does not offer favourable conditions for the biodegradation process, confirmed by a low mass loss in the incubated Bionolle#3001 samples.

W ostatnich dekadach ważnym kierunkiem badań jest opracowanie takich materiałów, które będą ulegały całkowitemu rozkładowi w bardzo krótkim czasie, a produkty ich biodegradacji będą przyjazne środowisku. Gleba jest źródłem wielu mikroorganizmów charakteryzujących się różnymi właściwościami biochemicznymi. Enzymami odgrywającymi główną rolę w degradacji polimerów są esterazy i proteazy zasadowe wytwarzane przez laseczki z rodzaju Bacillus sp., grzyby z rodzaju Tritrachium sp., promieniowce z rodzaju Amycolatopsis sp., oraz Paenibacillus sp. Określono wpływ produktów rozkładu polimeru PBSA (Bionolle#3001) i włókniny otrzymanej z tego polimeru na skład jakościowy i ilościowy profilu mikrobiologicznego gleby, w której inkubowano próby polimeru i włókniny. Dokonano również porównania stopnia ubytku masy polimeru i włókniny w wyniku biorozkładu w glebie ogrodniczej i pochodzącej z pól doświadczalnych Uniwersytetu Rolniczego w Krakowie.

Laboratorium Biodegradacji Instytutu Biopolimerów i Włókien Chemicznych w Łodzi

Gutowska A., Ciechańska D., Borowska J., Miros P., Szalczyńska M.

Analityka : nauka i praktyka

2011

nr 2

44-47

We współczesnym świecie materiały polimerowe odgrywają coraz większą rolę w nowoczesnej gospodarce. W związku z tym co roku przybywa ogromna ilość odpadów przemysłowych i komunalnych, których jedynie niewielki procent poddaje się recyklingowi lub utylizacji.