The goal of this paper is to measure the non-wetting to wetting transition temperatures of liquid tin on surfaces of different steel samples in vacuum with residual pressure of 10-8 bar. The experiments were conducted on four steels (C45, S103, CK60 and EN1.4034) of varying compositions using pure tin (99.99%) by the sessile drop method. Non-wetting to wetting transition (contact angle decreasing below 90°) by liquid tin was observed as function of increasing temperature in the range of 820-940 K for low alloyed steels C45, S103 and CK60, while it was considerably higher (around 1130 K) for high chromium EN1.4034 steel. it is concluded that at about the same temperatures, the surfaces of the steel samples are spontaneously deoxidized due to the combined effect of high temperature, low vacuum and C-content of steels. After the oxide layer is removed, the contact angles of liquid tin on steel surfaces were found in the range of 45-80° for low alloyed C45, S103 and CK60 steels and around 20° for high chromium EN1.4034 steel. These relatively high contact angle values compared to other metal/metal couples (such as liquid Cu on steels) are due to the formation of not fully metallic intermetallic compounds (FeSn and FeSn2) at the interface (such do not form in the Cu/Fe system).
In this study, silicon carbide (SiC) reinforced lead-free solder (SAC305) was prepared by the powder metallurgy method. In this method SAC305 powder and SiC powder were milled, compressed and sintered to prepare composite solder. The composite solders were characterized by optical and scanning electron microscopy for the microstructural investigation and mechanical test. Addition of 1.5 wt.% and 2 wt.% ceramic reinforcement to the composite increased compressive strengths and microhardness up to 38% and 68% compared to those of the monolithic sample. In addition, the ceramic particles caused an up to 55% decrease in the wetting angle between the substrate and the composite solder and porosity was always increased with increase of SiC particles.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.