Preliminary studies on electrodeposition of Zn-Fe-W alloy coatings from citrate-sulphate baths

Shoaib Hafiz Muhammad, Winiarska Katarzyna, Winiarski Juliusz

Ochrona przed Korozją

|

2023

|

nr 2

44--47

EN

Exploratory studies of the electrodeposition process of zinc coatings containing iron and tungsten were carried out using SEM/EDS and XRD techniques. It was shown that from a citrate-sulphate plating bath composed of (mol dm−3): ZnSO4 – 0.2, FeSO4 – 0.2, Na3Cit (tri-sodium citrate salt) – 0.4, (NH4)2SO4 – 0.1 and Na2WO4 – 0.01 Zn-Fe-W alloys can be obtained on a rotating disc electrode. It was noted that the induced co-deposition of tungsten with iron only occurred at pH > 6.0. Below this value, a Zn-Fe alloy coating was obtained. In the pH range from 5.0 to 9.0, the maximum contents of tungsten (15.96 wt. %) and iron (29.36 wt. %) were shown by the coatings deposited at pH 7.0. The increase in the bath pH from 5.0 to 9.0 resulted in clear changes in the phase composition of the deposited coatings. According to the results of XRD analyzes, the following can be indicated as probable: Fe22Zn78 and Fe7W6. However, the recorded diffractograms are difficult to interpret and it was very difficult to clearly define the type of phases present in the coating without additional tests.

PL

Stosując techniki SEM/EDS i XRD, przeprowadzono rozpoznawcze badania procesu elektroosadzania powłok cynkowych zawierających żelazo i wolfram. Wykazano, że z cytrynianowo-siarczanowej kąpieli galwanicznej o składzie (mol dm−3): ZnSO4 – 0,2, FeSO4 – 0,2, Na3Cit (cytrynian tri-sodu) – 0,4, (NH4)2SO4 – 0,1 i Na2WO4 – 0,01 można otrzymać na wirującej elektrodzie dyskowej powłoki stopowe Zn-Fe-W. Zauważono, że indukowane współosadzanie wolframu z żelazem zachodziło dopiero przy pH > 6,0. Poniżej tej wartości otrzymywało się powłokę stopową Zn-Fe. W zakresie pH od 5,0 do 9,0 maksymalną zawartość wolframu (15,96% mas.) i żelaza (29,36% mas.) wykazały powłoki osadzone przy pH 7,0. Wzrost pH kąpieli od 4,5 do 9,0 powodował wyraźne zmiany w składzie fazowym osadzanych powłok. Zgodnie z wynikami analiz XRD można wskazać jako prawdopodobne występowanie: Fe22Zn78 oraz Fe7W6. Zarejestrowane dyfraktogramy są jednak trudne w interpretacji i jednoznaczne określenie rodzaju faz obecnych w powłoce bez wykonania dodatkowych badań było mocno utrudnione.

2

Bioleaching of sulfide containing material from the Wiśniówka Quarry: stability and adhesion of secondary products

Pawlowska Agnieszka, Sadowski Zygmunt, Winiarska Katarzyna

Physicochemical Problems of Mineral Processing

|

2022

|

Vol. 58, iss. 4

art. no. 149884

EN

Secondary products (minerals) formed during bioleaching play an essential role in this process. Their adhesion to the surface of leached grains can inhibit bioleaching. For this reason, it is crucial to know the physicochemical conditions of adhesion. Selected material from the Wiśniówka Quarry (Kielce, Poland) with increased content of sulfides was subjected to microbial leaching. A precipitate collected from a bacterial culture was used as a secondary product (mainly jarosite). Adhesion and bio-extraction tests were carried out in a column reactor with a mineral bed (particle size 0.8 - 1.2 mm). The cationic surfactant (CTAB), anionic surfactant (SDS), and rhamnolipids (RL) were used to modify the surface of minerals and secondary products. Changes in the surface properties were determined with zeta potential measurements. The cationic surfactant above the 0.5 mM caused stability of jarosite suspension. Also, bioleaching efficiency was the highest for mineral surfaces modified by CTAB. The quantitative interpretation of the adhesion of the secondary product to bioleach mineral material was carried out.

3

Possibility of obtaining lanthanum doped nickel coatings from baths based on deep eutectic solvents

Niciejewska Anna, Tylus Włodzimierz, Marczewski Marek, Winiarska Katarzyna, Szczygieł Bogdan, Winiarski Juliusz

Ochrona przed Korozją

|

2022

|

nr 11

344--349

EN

Lanthanum-doped nickel coatings were obtained from the bath based on a deep eutectic solvent: choline chloride and propylene glycol, mixed in a molar ratio of 1 : 2, and 0.2 mol dm−3 NiCl2 ∙ 6H2O and 0.5 mol dm−3 LaCl2 ∙ xH2O. The morphology, topography and chemical composition were examined. The lanthanum content in the coating was determined to be 1.7 wt. % using the ICP-MS method. Lanthanum on the surface was mainly in the form of lanthanum carbonate. The obtained coating was exposed to a 7-day exposure in 0.05 mol dm−3 NaCl solution. The coating showed the highest corrosion resistance (Rp ~ 30 kΩ cm2) after 15 hours of exposure to the NaCl solution.

PL

Powłoki niklowe domieszkowane lantanem zostały otrzymane z kąpieli na bazie rozpuszczalnika eutektycznego chlorku choliny i glikolu propylenowego zmieszanych w proporcjach molowych 1 : 2 oraz 0,2 mol dm−3 NiCl2 ∙ 6H2O i 0,5 mol dm−3 LaCl2 ∙ xH2O. Zbadano morfologię, topografię oraz skład chemiczny. Zawartość lantanu w powłoce została określona na 1,7% mas. techniką ICP-MS. Na powierzchni powłoki lantan występował głównie w postaci węglanu lantanu. Otrzymana powłoka została poddana 7-dniowej ekspozycji w 0,05 mol dm−3 roztworze NaCl. Największą odporność na korozję powłoki stwierdzono po 15-godzinnej ekspozycji w roztworze NaCl.