feedstock after the 1st injection molding shows a better homogeneity than as-received feedstock due to re-mixing effects between the screw and barrel during the injection molding process. As the number of recycling numbers increases, the homogeneity, viscosities ad shrinkage ratio of recycled feedstocks show slight differences with those of the as-received feedstock until the 6th molding injection. However, some rheological parameters like the moldability index sharply increased up to the 4th injection but shows a tendency to decrease thereafter.

and the transformation temperature is about 400°C. Young’s modulus and hardness are higher in sample with low angle grain boundaries, while creep length is larger in sample with high angle ones. These results indicate that progress of plastic deformation at room temperature is more difficult in sample with low angle ones. During compression test at 200°C, strain softening occurs in all samples. However, yield strength in sample with low angle grain boundaries is higher twice than that with high angle ones due to higher activation energy for grain boundary sliding.

carbon fiber reinforcement was determined to be 1.5 vol.% and 4.0 vol.%, respectively. The addition of the carbon fiber increased the hardness of A356 alloy. However, tensile strength did not increase in the as-cast composites regardless of the SiC coating and volume fraction of the carbon fiber, due to the debonding which reduced load transfer efficiency from matrix to fiber at the interface. After T6-treatment of the composites, a significant increase in strength occurred only in the composite reinforced by the SiC-coated short carbon fiber, which was considered to result from the formation of a precipitate improving the Al/SiC interfacial strength.